Sodium alginate blended membrane with polyurethane: Desalination performance and antimicrobial activity evaluation.

A series of polymeric membranes were synthesized by blending polyurethane with sodium alginate (0.2, 0.4, 0.6, 0.8 and 1.0%). The structural, morphological and thermal properties of the membranes were examined by FTIR, SEM, AFM and TGA, respectively. Performance evaluation (salt rejection and flux) was assessed through reverse osmosis technique (RO). The FTIR spectra of membranes confirmed extensive hydrogen bonding (3350 cm-1). The SEM and AFM analyses supported a progressively rising surface roughness of blended membranes. The hydrophilicity, crosslinking density and thermal stability of the membranes were improved with an increase in alginate content. The capability of salt (NaCl and MgCl2) rejection was improved with alginate up to 0.8%. In addition, the rejection of divalent ions was better than monovalent ions (94 ± 0.96% for NaCl and 98 ± 0.98% for MgCl2). The blended membranes ascertained an effective chlorine resistivity. The antibacterial activity was also promising, which enhanced with the alginate content in the membrane. The sodium alginate blended membrane with polyurethane proved to be an efficient approach to develop the blended membranes with tunable properties for water desalination.

Innovation in Chinese internet companies: A meta-frontier analysis.

The innovation of a particular company benefits the whole industry when innovation technology transfers to others. Similarly, the development and innovation in internet companies influence the development and innovation of the industry. This investigation has applied a unique approach of meta-frontier analysis to estimate and analyze the innovation in internet companies in China. A unique dataset of Chinese internet companies from 2000 to 2017 has been utilized to estimate and compare the innovation over the period of study. The change in technology gap ratio (TGR) and a shift in production function have translated into innovation which was overlooked by previous studies. It is found that the production function of internet companies is moving upward in the presence of external factors such as smartphones invention, mobile internet, mobile payments, and artificial intelligence, etc. Consequently, a sudden increase in TGR is captured due to the innovation of some companies. Hence, the average TE of the industry falls caused by the increased distance of other companies form industry production function. However, the innovation advantage defused when other companies start imitating and the average TE elevates. A steady increase in the TGR index revealed that the continuous innovation-based growth of some companies lifting the production frontier upward. This provides the opportunity for other companies to imitate and provides continuous growth in the industry. This study provides a novel methodological approach to measure innovation and also provide practical implication by empirical estimation of innovation in Chinese internet companies.

In vitro study of chitosan-based multi-responsive hydrogels as drug release vehicles: a preclinical study.

Systematic administration of painkillers and anti-inflammatory drugs is routinely employed to minimize pain and bodily disorders. Controlled drug delivery has the potential to improve the outcomes of disorders by providing sustained exposure to efficacious drug concentrations. Herein, we report the fabrication of multi-responsive hydrogels using reactive and functional polymers such as chitosan and polyvinyl pyrrolidone by varying the concentration of a cleavable crosslinker, tetraethyl orthosilicate. The swelling indices of the hydrogels were evaluated in distilled water, solutions with different pH values and different electrolytes. FTIR, WAXRD and TGA were conducted to investigate the structures, crystallinities and thermal stabilities of the prepared multi-responsive hydrogels, respectively. The ultimate tensile strength and elongations at break of the fabricated hydrogels were investigated to assess their mechanical stability. Optical microscopy, biodegradation, antimicrobial and cytotoxicity analyses were further carried out to verify the magnified crosslinked and porous structures, biodegradabilities, biocompatibilities and toxic behaviour of the as-prepared hydrogels, respectively. Drug release analysis was conducted to evaluate their release behaviour in PBS, SGF, SIF and electrolyte solutions. The overall results indicate the successful development of novel, non-toxic and sustained drug deliverable hydrogels, which can be considered as a paramount success towards the fabrication of controlled drug delivery systems.

γ-Irradiated chitosan based injectable hydrogels for controlled release of drug (Montelukast sodium).

Novel pH-sensitive γ-irradiated low molecular weight (MW) chitosan (CS) (pre-irradiated) and poly (vinyl alcohol) (PVA) blended injectable hydrogels, crosslinked with varying concentrations of glycerol, were fabricated for drug delivery application. The effect of low MW irradiated CS on controlled drug release was evaluated to address the problem of higher viscosity and lower solubility of high MW CS. The FTIR spectra of hydrogels depicted the presence of all the incorporated functional groups and the developed interactions (physical and chemical). The surface morphology of hydrogels assessed by scanning electron microscope exhibited porous microstructure. All hydrogels were subjected to the swelling analysis in different media (water, buffer and electrolytes). The pH sensitive hydrogel samples exhibited less swelling at acidic and neutral pH while higher swelling at basic pH. CPG-0.5 showed the highest swelling at all pH media as compared to other hydrogel samples. CPG-1.0 was selected for the release analysis of drug because of its highest swelling (114.47%) in distilled water having neutral pH. It was loaded with model drug (Montelukast Sodium) during the preparation phase and studied for drug release capability. The in-vitro controlled release evaluation of hydrogel (CPG-1.0) was performed in SGF and SIF using UV-visible spectroscopy. The results confirmed their applications in injectable drug release systems as all the loaded drug was released in 30 min in SGF (pH -1.2) while the release of drug in SIF (pH -6.8) was in controlled manner (99.62% in 3 h). The improved antibacterial activity of these hydrogel films was owing to the fact that the γ-irradiated low MW CS has ruptured the bacterial cell and its metabolism more efficiently by inflowing in the cell.