Antimicrobial and Flame-Retardant Coatings Prepared from Nano- and Microparticles of Unmodified and Nitrogen-Modified Polyphenols.

The purpose of this study was to elucidate the structures and functional properties of tannin- and lignin-derived nano- and microparticles and the coatings prepared from them. Nanoparticles prepared from technical lignins and water-insoluble tannin obtained from softwood bark showed large differences in the suspension testing of antibacterial efficacy against methicillin-resistant Staphylococcus aureus (MRSA) bacteria. A common factor among the most effective lignin nanoparticles was a relatively low molar mass of the lignin, but that alone did not guarantee high efficacy. Tannin nanoparticles showed good antibacterial activity both in suspension testing and as coatings applied onto cellulose. The nanoparticles of nitrogen-modified tannin and the small microparticles of nitrogen-modified kraft lignin exhibited promising flame-retardant parameters when applied as coatings on cellulose. These results illustrate the potential of nano- and microsized particles of unmodified and chemically modified polyphenols to provide functional coatings to cellulosic substrates for environments and applications with high hygiene and fire safety requirements.

Improved Fire Retardancy of Cellulose Fibres via Deposition of Nitrogen-Modified Biopolyphenols.

Driven by concerns over the health and environmental impacts of currently used fire retardants (FRs), recent years have seen strong demand for alternative safer and sustainable bio-based FRs. In this paper, we evaluated the potential of nitrogen-modified biopolyphenols as FRs for cellulosic natural fibres that could be used in low-density cellulose insulations. We describe the preparation and characterisation of nitrogen-modified lignin and tannin containing over 10% nitrogen as well as the treatment of cellulose pulp fibres with combinations of lignin or tannin and adsorption-enhancing retention aids. Combining lignin or tannin with a mixture of commercial bio-based flocculant (cationised tannin) and anionic retention chemical allowed for a nearly fourfold increase in lignin adsorption onto cellulosic pulp. The nitrogen-modified biopolyphenols showed significant improvement in heat release parameters in micro-scale combustion calorimetry (MCC) testing compared with their unmodified counterparts. Moreover, the adsorption of nitrogen-modified lignin or tannin onto cellulose fibres decreased the maximum heat release rate and total heat release compared with cellulose reference by 15-23%. A further positive finding was that the temperature at the peak heat release rate did not change. These results show the potential of nitrogen-modified biopolyphenols to improve fire-retarding properties of cellulosic products.