RESUMO
A cold cathode X-ray tube was fabricated using a carbon nanotube (CNT) field electron emitter made by a free-standing CNT film which is composed of a highly packed CNT network. A lot of CNT bundles with a sharp tip are vertically aligned at the edge of the thin CNT film with a length of 10 mm and a thickness of 7 µm. The cold cathode X-ray tube using the CNT field emitter presents an extremely high tube current density of 152 A/cm2 (corresponding to tube current of 106.4 mA), the electron beam transmittance of 95.2% and a small focal spot size (FSS) of 0.5 mm. In addition, the cold cathode X-ray tube also shows stable lifetime during 100â¯000 shots. High emission current density of the cold cathode X-ray tube is mainly attributed to a lot of electron emission sites at an edge of the CNT film. The small FSS is caused by an ensemble of the CNT field electron emitter made by a free-standing thin CNT film and the optimized curve-shape elliptical focusing lens. Based on obtained results, the cold cathode X-ray tube can be widely used for various X-ray applications such as medical diagnosis systems and security check systems in the future.
RESUMO
The field emission properties of boron nitride nanotube (BNNT) field emitters according to vacuum pressure were demonstrated. During the short-term emission operation, the field emission behaviors were almost similar, regardless of the vacuum pressure, even though the turn-on electric field of the BNNT field emitter was slightly increased as the vacuum pressure increased. On the other hand, during the long-term emission operation, both the degradation and fluctuations of the emission current of the BNNT field emitters were dramatically increased as the vacuum pressure increased. The degradation of field emission properties of the BNNT emitters according to vacuum pressure is mainly attributed to the ion bombardment effect, rather than the oxidation effect. The field emission behavior under Ar ambient also strongly demonstrates that the degradation and the fluctuation of the emission current are largely dependent on the ion bombardment effect.
RESUMO
Boron nitride nanotubes (BNNTs) have attracted considerable attention as a field emission material because of their high mechanical strength, high negative electron affinity, and high oxidation resistance. Nevertheless, the obtained field-emission properties of BNNTs have indicated poor emission performance, which is a very high turn-on electric field with a low emission current. We fabricated BNNT field emitters and investigated their field-emission properties. The field-emission properties of the BNNT field emitters were considerably enhanced compared to those of other BN nanomaterial-based field emitters. The turn-on and the threshold electric fields of the BNNT field emitter were 3.1 and 5.4 V/µm at the gap distance of 750 µm, respectively. Both the turn-on and the threshold electric fields of the BNNT field emitters were decreased by increasing the gap distance between the emitter tip and the anode electrode. Degradation of the emission current during field emission operation for 20 h showed no significant difference according to the gap distance. Emission current fluctuation of the BNNT field emitters showed that the smaller gap was more unstable than the larger gap. The enhanced emission properties are mainly attributed to the small diameter, high-quality, and straight structure of BNNTs as well as the stable network formation of the BNNT film with good mechanical and electrical contact between the BNNTs and the cathode electrode. The remarkable emission performance of the BNNT field emitters might have promising applications for various field-emission devices.