RESUMO
The development of highly gas-permeable membranes is required for gas separation applications. In this study, 1-(p-trimethylsilyl)phenyl-1-propyne (SPP) was copolymerized with diphenylacetylenes bearing tert-butyl (BDPA) and SiMe3 (SDPA) groups at various feed ratios to obtain poly(SPP-co-BDPA) and poly(SPP-co-SDPA) copolymers, respectively. Free-standing membranes were fabricated from toluene solutions of the copolymers, the gas permeability of which increased as the SPP ratio decreased (P O2 : 550-2100 barrers). Interestingly, poly(SPP-co-BDPA) and poly(SPP-co-SDPA) at a 1 : 4 ratio of SPP:BDPA and SPP:SDPA, respectively, showed higher permeabilities than the respective homopolymers. Desilylation of the poly(SPP-co-BDPA) membrane increased the gas permeability, whereas desilylation of the poly(SPP-co-SDPA) membrane had the opposite result.
RESUMO
Efficient gas-separation systems comprising gas-permeable membranes are important for energy conservation in various industrial applications. Herein, high-molecular-weight copolymers (2ab and 2ac) were synthesized in good yields by the copolymerization of 1-(p-trimethylsilyl)phenyl-2-(p-trimethylsilyl)phenylacetylene (1a) with 1-phenyl-2-(p-tert-butyl)phenylacetylene (1b) and 1-phenyl-2-(p-trimethylsilyl)phenylacetylene (1c) in various monomer feed ratios using TaCl5-n-Bu4Sn. Tough membranes were obtained by solution casting. The copolymers exhibited very high gas permeabilities (P O2 : 1700-3400 barrers). Desilylation of 2ac membranes decreased the gas permeability, but desilylation of 2ab membranes resulted in a significant increase in the gas permeability. The highest oxygen permeability coefficient obtained was 9300 barrers, which was comparable to that of poly(1-trimethylsilyl-1-propyne), a polymer known to have the highest gas permeability.