Zinc oxide (ZnO) nanorod thin films were prepared by CBD onto glass and FTO/glass substrates. Silver (Ag) nanoparticles were synthesized on the surface of the prepared ZnO nanorod thin films using electrochemical methods. The scanning electron microscopy images of the Ag/ZnO/glass core/shell nanostructure confirmed that the average particles size is 20 nm while it was 41 nm for Ag NPs that synthesized onto ZnO/FTO NRs. The photocatalytic activity of the prepared Ag/ZnO core/shell nanostructure was studied by analyzing the degradation of methylene blue (MB) dye under visible light. Various pH values (6 and 10) and exposure time (30-240) min were controlled to investigate the photocatalytic activity of as-prepared Ag/ZnO core/shell nanostructure and that annealed at 200 °C and 300 °C for 1 h. It was observed that when the pH was 6, the degradation rate increased with the annealing temperature and irradiation time reaching 51% at the annealing temperature of 300 °C and exposure time of 240 min. In other hands, when the pH was 10, and the sample was annealed at 200 °C, it showed a good degradation rate of 100% at the irradiation time of 90 min. By contrast, the sample annealed at 300 °C required 180 min to degrade the MB dye completely. The photoelectrochemical cell measurement based on photocurrent density revealed a slight response to light. Cycle voltammetry (CV) measurement was conducted, and the CV curves of the Ag/ZnO core/shell electrodes indicated nonfaradaic and pseudocapacitance behavior. The electrodes showed nearly rectangular CV curves, which indicated the dominance of the nonfaradaic capacitance behavior. The specific capacitance of the electrodes remained at approximately 99%. Mott-Schottky analysis revealed that the semiconductor was an n-type with dependence on flat band potential V FB deviation in the negative direction.
RESUMO
Seasonal variations in phytoplankton abundance and their composition were studied at five stations in the middle region (between Al-Hindiya barrage to Kifil City) of the Euphrates River in Iraq between March, 2004, and February, 2005. A total 151 taxa of phytoplankton were identified, belonging to Bacillariophyceae (98), Chlorophyceae (33), Cyanophyceae (14), Euglenophyceae (2), Xanthophyceae (2), and Dinophyceae (2). The total abundance of phytoplankton cells varied from 136 to 5312 cells l(-1) with maxima in spring and fall. Bacillariophyceae were the most abundant group at all stations. Some species of phytoplankton occurred continuously during the study period (Cyclotella ocellata, C. meneghiana, Cocconeis placentula, Nitzchia spp, Meringosphaera spinosa). The study recorded four species as new records for Iraqi. The phytoplankton was indicative of oligotrophic conditions although it showed some signs of organic pollution near cities.