Autonomous healing of fatigue cracks via cold welding.

Fatigue in metals involves gradual failure through incremental propagation of cracks under repetitive mechanical load. In structural applications, fatigue accounts for up to 90% of in-service failure1,2. Prevention of fatigue relies on implementation of large safety factors and inefficient overdesign3. In traditional metallurgical design for fatigue resistance, microstructures are developed to either arrest or slow the progression of cracks. Crack growth is assumed to be irreversible. By contrast, in other material classes, there is a compelling alternative based on latent healing mechanisms and damage reversal4-9. Here, we report that fatigue cracks in pure metals can undergo intrinsic self-healing. We directly observe the early progression of nanoscale fatigue cracks, and as expected, the cracks advance, deflect and arrest at local microstructural barriers. However, unexpectedly, cracks were also observed to heal by a process that can be described as crack flank cold welding induced by a combination of local stress state and grain boundary migration. The premise that fatigue cracks can autonomously heal in metals through local interaction with microstructural features challenges the most fundamental theories on how engineers design and evaluate fatigue life in structural materials. We discuss the implications for fatigue in a variety of service environments.

Gradient nanostructured steel with superior tensile plasticity.

Nanostructured metallic materials with abundant high-angle grain boundaries exhibit high strength and good radiation resistance. While the nanoscale grains induce high strength, they also degrade tensile ductility. We show that a gradient nanostructured ferritic steel exhibits simultaneous improvement in yield strength by 36% and uniform elongation by 50% compared to the homogenously structured counterpart. In situ tension studies coupled with electron backscattered diffraction analyses reveal intricate coordinated deformation mechanisms in the gradient structures. The outermost nanolaminate grains sustain a substantial plastic strain via a profound deformation mechanism involving prominent grain reorientation. This synergistic plastic co-deformation process alters the rupture mode in the post-necking regime, thus delaying the onset of fracture. The present discovery highlights the intrinsic plasticity of nanolaminate grains and their significance in simultaneous improvement of strength and tensile ductility of structural metallic materials.

New nanoscale toughening mechanisms mitigate embrittlement in binary nanocrystalline alloys.

Nanocrystalline metals offer significant improvements in structural performance over conventional alloys. However, their performance is limited by grain boundary instability and limited ductility. Solute segregation has been proposed as a stabilization mechanism, however the solute atoms can embrittle grain boundaries and further degrade the toughness. In the present study, we confirm the embrittling effect of solute segregation in Pt-Au alloys. However, more importantly, we show that inhomogeneous chemical segregation to the grain boundary can lead to a new toughening mechanism termed compositional crack arrest. Energy dissipation is facilitated by the formation of nanocrack networks formed when cracks arrested at regions of the grain boundaries that were starved in the embrittling element. This mechanism, in concert with triple junction crack arrest, provides pathways to optimize both thermal stability and energy dissipation. A combination of in situ tensile deformation experiments and molecular dynamics simulations elucidate both the embrittling and toughening processes that can occur as a function of solute content.

Improve sensitization and corrosion resistance of an Al-Mg alloy by optimization of grain boundaries.

The sensitization and subsequent intergranular corrosion of Al-5.3 wt.% Mg alloy has been shown to be an important factor in stress corrosion cracking of Al-Mg alloys. Understanding sensitization requires the review of grain boundary character on the precipitation process which can assist in developing and designing alloys with improved corrosion resistance. This study shows that the degree of precipitation in Al-Mg alloy is dependent on grain boundary misorientation angle, adjacent grain boundary planes and grain boundary types. The results show that the misorientation angle is the most important factor influencing precipitation in grain boundaries of the Al-Mg alloy. Low angle grain boundaries (≤15°) have better immunity to precipitation and grain boundary acid attack. High angle grain boundaries (>15°) are vulnerable to grain boundary acid attack. Grain boundaries with adjacent plane orientations near to {100} have potential for immunity to precipitation and grain boundary acid attack. This work shows that low Σ (Σ ≤ 29) coincident site lattice (CSL) grain boundaries have thinner ß precipitates. Modified nitric acid mass loss test and polarization test demonstrated that the global corrosion resistance of sputtered Al-Mg alloy is enhanced. This may be attributed to the increased fractions of low Σ (Σ ≤ 29) CSL grain boundaries after sputtering.