Integrated In Situ Fabrication of CuO Nanorod-Decorated Polymer Membranes for the Catalytic Flow-Through Reduction of p-Nitrophenol.

We developed a novel method to fabricate copper nanorods in situ in a poly(ether sulfone) (15 wt %) casting solution by a sonochemical reduction of Cu2+ ions with NaBH4. The main twist is the addition of ethanol to remove excess NaBH4 through Cu(0) catalyzed ethanolysis. This enabled the direct use of the resulting copper-containing casting dispersions for membrane preparation by liquid nonsolvent-induced phase separation and led to full utilization of the copper source, generating zero metal waste. We characterized the copper nanorods as presented in the membranes via scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and UV/vis spectroscopy. We could demonstrate that the rapid immobilization from reducing conditions led to the membrane incorporation of copper nanorods in a state of high reactivity, which also promoted the complete oxidation to CuO after fabrication. We further observed a large aspect ratio and crystal straining of the nanorods, likely resulting from growth around the matrix polymer. The entanglement with poly(ether sulfone) further facilitated a selective presentation at the pore surface of the final CuO-decorated membranes. The membranes also exhibit high water permeances of up to 2800 L/m2hbar. Our catalytic membranes achieved exceptionally high activities in the aqueous flow-through reduction of p-nitrophenol (p-NP), with turnover frequencies of up to 115 h-1, even surpassing those of other state-of-the-art catalytic membranes that incorporate Pd or Ag. Additionally, we demonstrated that catalytic hydrolysis of the reducing agent in water can lead to hydrogen gas formation and blocking of active sites during continuous catalytic p-NP hydrogenation. We illustrated that the accompanying conversion loss can be mitigated by facilitated gas transport in the water-filled pores, which is dependent on the orientation of the pore size gradient and the flow direction.

Tunable Syngas Formation at Industrially Relevant Current Densities via CO2 Electroreduction and Hydrogen Evolution over Ni and Fe-derived Catalysts obtained via One-Step Pyrolysis of Polybenzoxazine Based Composites.

Simultaneous electroreduction of CO2 and H2O to syngas can provide a sustainable feed for established processes used to synthesize carbon-based chemicals. The synthesis of MOx/M-N-Cs (M = Ni, Fe) electrocatalysts reported via one-step pyrolysis that shows increased performance during syngas electrosynthesis at high current densities with adaptable H2/CO ratios, e.g., for the Fischer-Tropsch process. When embedded in gas diffusion electrodes (GDEs) with optimized hydrophobicity, the NiOx/Ni-N-C catalyst produces syngas (H2/CO = 0.67) at -200 mA cm-2 while for the FeOx/Fe-N-C syngas production occurs at ≈-150 mA cm-2. By tuning the electrocatalyst's microenvironment, stable operation for >3 h at -200 mA cm-2 is achieved with the NiOx/Ni-N-C GDE. Post-electrolysis characterization revealed that the restructuring of the catalyst via reduction of NiOx to metallic Ni NPs still enables stable operation of the electrode at -200 mA cm-2, when embedded in an optimized microenvironment. The ionomer and additives used in the catalyst layer are important for the observed stable operation. Operando Raman measurements confirm the presence of NiOx during CO formation and indicate weak adsorption of CO on the catalyst surface.

Kinetics of Direct Reaction of Vanadate, Chromate, and Permanganate with Graphene Nanoplatelets for Use in Water Purification.

Oxometalates of vanadium(V), chromium(VI), and manganese(VII) have negative impacts on water resources due to their toxicity. To remove them, the kinetics of 0.04 mM oxometalates in natural and synthetic water were studied using graphene nanoplatelets (GNP). The GNP were dispersible in water and formed aggregates >15 µm that could be easily separated. Within 30 min, the GNP were covered with ~0.4 mg/g vanadium and ~1.0 mg/g chromium as Cr(OH)3. The reaction of 0.04 mM permanganate with 50 mg of GNP resulted in a coverage of 10 mg/g in 5 min, while the maximum value was 300 mg/g manganese as Mn2O3/MnO. TEM showed a random metal distribution on the surfaces; no clusters or nanoparticles were detected. The rate of disappearance in aerated water followed a pseudo second-order adsorption kinetics (PSO) for V(V), a pseudo second-order reaction for Cr(VI), and a pseudo first-order reaction for Mn(VII). For Cr(VI) and Mn(VII), the rate constants were found to depend on the GNP mass. Oxygen sorption occurred with PSO kinetics as a parallel slow process upon contact of GNP with air-saturated water. For thermally regenerated GNP, the rate constant decreased for V(V) but increased for Cr(VI), while no effect was observed for Mn(VII). GNP capacity was enhanced through regeneration for V(V) and Cr(VI); no effect was observed for Mn(VII). The reactions are well-suited for use in water purification processes and the reaction products, GNP, decorated with single metal atoms, are of great interest for the construction of sensors, electronic devices, and for application in single-atom catalysis (SAC).

Linking Composition, Structure and Thickness of CoOOH layers to Oxygen Evolution Reaction Activity by Correlative Microscopy.

The role of ß-CoOOH crystallographic orientations in catalytic activity for the oxygen evolution reaction (OER) remains elusive. We combine correlative electron backscatter diffraction/scanning electrochemical cell microscopy with X-ray photoelectron spectroscopy, transmission electron microscopy, and atom probe tomography to establish the structure-activity relationships of various faceted ß-CoOOH formed on a Co microelectrode under OER conditions. We reveal that ≈6 nm ß-CoOOH(01 1 ‾ ${\bar{1}}$ 0), grown on [ 1 ‾ 2 1 ‾ ${\bar{1}2\bar{1}}$ 0]-oriented Co, exhibits higher OER activity than ≈3 nm ß-CoOOH(10 1 ‾ ${\bar{1}}$ 3) or ≈6 nm ß-CoOOH(0006) formed on [02 2 ‾ 1 ] ${\bar{2}1]}$ - and [0001]-oriented Co, respectively. This arises from higher amounts of incorporated hydroxyl ions and more easily reducible CoIII -O sites present in ß-CoOOH(01 1 ‾ ${\bar{1}}$ 0) than those in the latter two oxyhydroxide facets. Our correlative multimodal approach shows great promise in linking local activity with atomic-scale details of structure, thickness and composition of active species, which opens opportunities to design pre-catalysts with preferred defects that promote the formation of the most active OER species.

Differentiating between Acidic and Basic Surface Hydroxyls on Metal Oxides by Fluoride Substitution: A Case Study on Blue TiO2 from Laser Defect Engineering.

Both oxygen vacancies and surface hydroxyls play a crucial role in catalysis. Yet, their relationship is not often explored. Herein, we prepare two series of TiO2 (rutile and P25) with increasing oxygen deficiency and Ti3+ concentration by pulsed laser defect engineering in liquid (PUDEL), and selectively quantify the acidic and basic surface OH by fluoride substitution. As indicated by EPR spectroscopy, the laser-generated Ti3+ exist near the surface of rutile, but appear to be deeper in the bulk for P25. Fluoride substitution shows that extra acidic bridging OH are selectively created on rutile, while the surface OH density remains constant for P25. These observations suggest near-surface Ti3+ are highly related to surface bridging OH, presumably the former increasing the electron density of the bridging oxygen to form more of the latter. We anticipate that fluoride substitution will enable better characterization of surface OH and its correlation with defects in metal oxides.

3D atomic-scale imaging of mixed Co-Fe spinel oxide nanoparticles during oxygen evolution reaction.

The three-dimensional (3D) distribution of individual atoms on the surface of catalyst nanoparticles plays a vital role in their activity and stability. Optimising the performance of electrocatalysts requires atomic-scale information, but it is difficult to obtain. Here, we use atom probe tomography to elucidate the 3D structure of 10 nm sized Co2FeO4 and CoFe2O4 nanoparticles during oxygen evolution reaction (OER). We reveal nanoscale spinodal decomposition in pristine Co2FeO4. The interfaces of Co-rich and Fe-rich nanodomains of Co2FeO4 become trapping sites for hydroxyl groups, contributing to a higher OER activity compared to that of CoFe2O4. However, the activity of Co2FeO4 drops considerably due to concurrent irreversible transformation towards CoIVO2 and pronounced Fe dissolution. In contrast, there is negligible elemental redistribution for CoFe2O4 after OER, except for surface structural transformation towards (FeIII, CoIII)2O3. Overall, our study provides a unique 3D compositional distribution of mixed Co-Fe spinel oxides, which gives atomic-scale insights into active sites and the deactivation of electrocatalysts during OER.

The Effect of Water on the 2-Propanol Oxidation Activity of Co-Substituted LaFe1- Cox O3 Perovskites.

Perovskites are interesting oxidation catalysts due to their chemical flexibility enabling the tuning of several properties. In this work, we synthesized LaFe1-x Cox O3 catalysts by co-precipitation and thermal decomposition, characterized them thoroughly and studied their 2-propanol oxidation activity under dry and wet conditions to bridge the knowledge gap between gas and liquid phase reactions. Transient tests showed a highly active, unstable low-temperature (LT) reaction channel in conversion profiles and a stable, less-active high-temperature (HT) channel. Cobalt incorporation had a positive effect on the activity. The effect of water was negative on the LT channel, whereas the HT channel activity was boosted for x>0.15. The boost may originate from a slower deactivation rate of the Co3+ sites under wet conditions and a higher amount of hydroxide species on the surface comparing wet to dry feeds. Water addition resulted in a slower deactivation for Co-rich catalysts and higher activity in the HT channel state.

Room temperature synthesized solid solution AuFe nanoparticles and their transformation into Au/Fe Janus nanocrystals.

Solid solution AuFe nanoparticles were synthesized for the first time under ambient conditions by an adapted method previously established for the Fe3O4-Au core-shell morphology. These AuFe particles preserved the fcc structure of Au incorporated with paramagnetic Fe atoms. The metastable AuFe can be segregated by transformation into Janus Au/Fe particles with bcc Fe and fcc Au upon annealing. The ferromagnetic Fe was epitaxially grown on low index fcc Au planes. This preparation route delivers new perspective materials for magnetoplasmonics and biomedical applications and suggests the reconsideration of existing protocols for magnetite-gold core-shell synthesis.

Influence of Nanoparticle Processing on the Thermoelectric Properties of (Bix Sb1-X )2 Te3 Ternary Alloys.

The synthesis of phase-pure ternary solutions of tetradymite-type materials (Bix Sb1-x )2 Te3 (x=0.25; 0.50; 0.75) in an ionic liquid approach has been carried out. The nanoparticles are characterized by means of energy-dispersive X-ray spectroscopy (EDX), powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), and transmission electron microscopy. In addition, the role of different processing approaches on the thermoelectric properties - Seebeck coefficient as well as electrical and thermal conductivity - is demonstrated.

Formic Acid-Assisted Selective Hydrogenolysis of 5-Hydroxymethylfurfural to 2,5-Dimethylfuran over Bifunctional Pd Nanoparticles Supported on N-Doped Mesoporous Carbon.

Biomass-derived 5-hydroxymethylfurfural (HMF) is regarded as one of the most promising platform chemicals to produce 2,5-dimethylfuran (DMF) as a potential liquid transportation fuel. Pd nanoparticles supported on N-containing and N-free mesoporous carbon materials were prepared, characterized, and applied in the hydrogenolysis of HMF to DMF under mild reaction conditions. Quantitative conversion of HMF to DMF was achieved in the presence of formic acid (FA) and H2 over Pd/NMC within 2 h. The reaction mechanism, especially the multiple roles of FA, was explored through a detailed comparative study by varying hydrogen source, additive, and substrate as well as by applying in situ ATR-IR spectroscopy. The major role of FA is to shift the dominant reaction pathway from the hydrogenation of the aldehyde group to the hydrogenolysis of the hydroxymethyl group via the protonation by FA at the C-OH group, lowering the activation barrier of the C-O bond cleavage and thus significantly enhancing the reaction rate. XPS results and DFT calculations revealed that Pd2+ species interacting with pyridine-like N atoms significantly enhance the selective hydrogenolysis of the C-OH bond in the presence of FA due to their high ability for the activation of FA and the stabilization of H- .

One-step synthesis of carbon-supported electrocatalysts.

Cost-efficiency, durability, and reliability of catalysts, as well as their operational lifetime, are the main challenges in chemical energy conversion. Here, we present a novel, one-step approach for the synthesis of Pt/C hybrid material by plasma-enhanced chemical vapor deposition (PE-CVD). The platinum loading, degree of oxidation, and the very narrow particle size distribution are precisely adjusted in the Pt/C hybrid material due to the simultaneous deposition of platinum and carbon during the process. The as-synthesized Pt/C hybrid materials are promising electrocatalysts for use in fuel cell applications as they show significantly improved electrochemical long-term stability compared to the industrial standard HiSPEC 4000. The PE-CVD process is furthermore expected to be extendable to the general deposition of metal-containing carbon materials from other commercially available metal acetylacetonate precursors.

Particle Size Distributions for Cellulose Nanocrystals Measured by Transmission Electron Microscopy: An Interlaboratory Comparison.

Particle size is a key parameter that must be measured to ensure reproducible production of cellulose nanocrystals (CNCs) and to achieve reliable performance metrics for specific CNC applications. Nevertheless, size measurements for CNCs are challenging due to their broad size distribution, irregular rod-shaped particles, and propensity to aggregate and agglomerate. We report an interlaboratory comparison (ILC) that tests transmission electron microscopy (TEM) protocols for image acquisition and analysis. Samples of CNCs were prepared on TEM grids in a single laboratory, and detailed data acquisition and analysis protocols were provided to participants. CNCs were imaged and the size of individual particles was analyzed in 10 participating laboratories that represent a cross section of academic, industrial, and government laboratories with varying levels of experience with imaging CNCs. The data for each laboratory were fit to a skew normal distribution that accommodates the variability in central location and distribution width and asymmetries for the various datasets. Consensus values were obtained by modeling the variation between laboratories using a skew normal distribution. This approach gave consensus distributions with values for mean, standard deviation, and shape factor of 95.8, 38.2, and 6.3 nm for length and 7.7, 2.2, and 2.9 nm for width, respectively. Comparison of the degree of overlap between distributions for individual laboratories indicates that differences in imaging resolution contribute to the variation in measured widths. We conclude that the selection of individual CNCs for analysis and the variability in CNC agglomeration and staining are the main factors that lead to variations in measured length and width between laboratories.

Terpolymer Multicompartment Nanofibers as Templates for Hybrid Pt Double Helices.

Hybrid inorganic/block copolymer (BCP) materials have become increasingly relevant for application in heterogeneous catalysis, microelectronics, and nanomedicine. While block copolymer templates are widely used for the formation of inorganic nanostructures, multicompartment templates could give access to more complex shapes and inner structures that are challenging to obtain with traditional processes. Here, we report the formation and characterization of hybrid platinum/polymer helices using multicompartment nanofibers (MCNFs) of polystyrene-block-polybutadiene-block-poly(tert-butyl methacrylate) (PS-b-PB-b-PT) triblock terpolymers as templates. Cross-linking of a PS-b-PB-b-PT helix-on-cylinder morphology resulted in uniform nanofibers with a diameter of 90 nm and a length of several micrometers, as well as an inner PB double helix (diameter 35 nm, pitch 25 nm, core 12 nm). The PB double helix served as template for the sol-gel reaction of H2PtCl6 into hybrid Pt double helices (Pt@MCNFs) as verified by STEM, electron tomography, AFM, and SEM. Carbonization of the Pt hybrids into Pt decorated carbon nanofibers (Pt@C) was followed in situ on a TEM heating state. Gradual heating from 25 to 1000 °C induced fusion of amorphous Pt NPs into larger crystalline Pt NP, which sheds light on the aging of Pt NPs in BCP scaffolds under high temperature conditions. The Pt@MCNFs were further sulfonated and incorporated into a filter to catalyze a model compound in a continuous flow process.

Vesicular Polymer Hexosomes Exhibit Topological Defects.

Polymer hexosomes are block copolymer solution morphologies that adopt an internal structure composed of an inverse hexagonal (HII) phase. To date, most polymer hexosomes are reportedly rotationally symmetric solid structures that possess a common feature where hexagonally ordered inverted cylinders rotate along a central axis of symmetry to form circular hoops. Here, we report on the formation of polymer hexosomes whose inverted cylinders orient in an unusual manner, forming hoops that are noncircular. For topological reasons, this led to the generation of four defects in the resulting hexosome structure. We find that these defect-bearing hexosomes are hollow, thereby resembling polymer vesicles or polymersomes with an inverse hexagonal cylindrical morphology in the shell. The topological defects of these so-called "vesicular hexosomes" are enticing as they could serve as a platform to spatially anchor targeting ligands or biomolecules on the surface, while the hollow cylindrical shell and the vesicular lumen could spatially accommodate cargoes within the different domains. We propose that these vesicular hexosomes do not form via a conventional nucleation-growth self-assembly pathway, but rather via a two-step process involving first liquid-liquid phase separation followed by polymer microphase separation.

Magnetite-Gold nanohybrids as ideal all-in-one platforms for theranostics.

High-quality, 25 nm octahedral-shaped Fe3O4 magnetite nanocrystals are epitaxially grown on 9 nm Au seed nanoparticles using a modified wet-chemical synthesis. These Fe3O4-Au Janus nanoparticles exhibit bulk-like magnetic properties. Due to their high magnetization and octahedral shape, the hybrids show superior in vitro and in vivo T2 relaxivity for magnetic resonance imaging as compared to other types of Fe3O4-Au hybrids and commercial contrast agents. The nanoparticles provide two functional surfaces for theranostic applications. For the first time, Fe3O4-Au hybrids are conjugated with two fluorescent dyes or the combination of drug and dye allowing the simultaneous tracking of the nanoparticle vehicle and the drug cargo in vitro and in vivo. The delivery to tumors and payload release are demonstrated in real time by intravital microscopy. Replacing the dyes by cell-specific molecules and drugs makes the Fe3O4-Au hybrids a unique all-in-one platform for theranostics.

Adjusting the catalytic properties of cobalt ferrite nanoparticles by pulsed laser fragmentation in water with defined energy dose.

Highly active, structurally disordered CoFe2O4/CoO electrocatalysts are synthesized by pulsed laser fragmentation in liquid (PLFL) of a commercial CoFe2O4 powder dispersed in water. A partial transformation of the CoFe2O4 educt to CoO is observed and proposed to be a thermal decomposition process induced by the picosecond pulsed laser irradiation. The overpotential in the OER in aqueous alkaline media at 10 mA cm-2 is reduced by 23% compared to the educt down to 0.32 V with a Tafel slope of 71 mV dec-1. Importantly, the catalytic activity is systematically adjustable by the number of PLFL treatment cycles. The occurrence of thermal melting and decomposition during one PLFL cycle is verified by modelling the laser beam energy distribution within the irradiated colloid volume and comparing the by single particles absorbed part to threshold energies. Thermal decomposition leads to a massive reduction in particle size and crystal transformations towards crystalline CoO and amorphous CoFe2O4. Subsequently, thermal melting forms multi-phase spherical and network-like particles. Additionally, Fe-based layered double hydroxides at higher process cycle repetitions emerge as a byproduct. The results show that PLFL is a promising method that allows modification of the structural order in oxides and thus access to catalytically interesting materials.

Studies of local structural distortions in strained ultrathin BaTiO3 films using scanning transmission electron microscopy.

Ultrathin ferroelectric heterostructures (SrTiO3/BaTiO3/BaRuO3/SrRuO3) were studied by scanning transmission electron microscopy (STEM) in terms of structural distortions and atomic displacements. The TiO2-termination at the top interface of the BaTiO3 layer was changed into a BaO-termination by adding an additional BaRuO3 layer. High-angle annular dark-field (HAADF) imaging by aberration-corrected STEM revealed that an artificially introduced BaO-termination can be achieved by this interface engineering. By using fast sequential imaging and frame-by-frame drift correction, the effect of the specimen drift was significantly reduced and the signal-to-noise ratio of the HAADF images was improved. Thus, a quantitative analysis of the HAADF images was feasible, and an in-plane and out-of-plane lattice spacing of the BaTiO3 layer of 3.90 and 4.22 Å were determined. A 25 pm shift of the Ti columns from the center of the unit cell of BaTiO3 along the c-axis was observed. By spatially resolved electron energy-loss spectroscopy studies, a reduction of the crystal field splitting (CFS, ΔL3=1.93 eV) and an asymmetric broadening of the eg peak were observed in the BaTiO3 film. These results verify the presence of a ferroelectric polarization in the ultrathin BaTiO3 film.

Periodic cation segregation in Cs0.44[Nb2.54W2.46O14] quantified by high-resolution scanning transmission electron microscopy.

The atomic structure of Cs0.44[Nb2.54W2.46O14] closely resembles the structure of the most active catalyst for the synthesis of acrylic acid, the M1 phase of Mo10V2(4+)Nb2TeO42-x. Consistently with observations made for the latter compound, the high-angle electron scattering signal recorded by scanning transmission electron microscopy shows a significant intensity variation, which repeats periodically with the projected crystallographic unit cell. The occupation factors for the individual mixed Nb/W atomic columns are extracted from the observed intensity variations. For this purpose, experimental images and simulated images are compared on an identical intensity scale, which enables a quantification of the cation distribution. According to our analysis specific sites possess low tungsten concentrations of 25%, whereas other sites have tungsten concentrations above 70%. These findings allow us to refine the existing structure model of the target compound, which has until now described a uniform distribution of the niobium and tungsten atoms in the unit cell, showing that the similarity between Cs0.44[Nb2.54W2.46O14] and the related catalytic compounds also extends to the level of the cation segregation.