Efficient photo-catalytic degradation of malachite green using nickel tungstate material as photo-catalyst.

The present study focused on the evaluation of photo-catalytic and photo-electrochemical properties of the photo-catalyst based on nickel tungstate material prepared by a nitrate method through the degradation of malachite green (MG) dye's. The effect of catalyst loading and dye concentration was examined. Physico-chemical, optical, electrical, electrochemical, and photo-electrochemical properties of the prepared material were analyzed by X-ray diffraction (XRD), fourier transform-infrared spectroscopy (FTIR), BET analysis, optical reflectance diffuse (DR), scanning electron microscopy (SEM/EDX), electrical conductivity, cyclic voltammetry (CV), current intensity, mott-shottky, and nyquist. XRD revealed the formation of monoclinic structure with a small particle size. BET surface area of the sample was around 10 m2/g. The results show that the degradation of MG was more than 80%, achieved after 3 h of irradiation at pH 4.6 and with a catalyst loading of 75 mg. Also, it was found that the dye photo-degradation obeyed the pseudo-first order kinetic via Langmuir Hinshelwood model.

Visible light degradation of Orange II using xCuyOz/TiO2 heterojunctions.

Cu(2)O/TiO(2), Cu/Cu(2)O/TiO(2) and Cu/Cu(2)O/CuO/TiO(2) heterojunctions were prepared and studied for their potential application as photocatalysts able to induce high performance under visible light. Orange II was used as a representative dye molecule. The effect of the amount and composition of the photosensitizers toward the activation of TiO(2) was studied. In each case, the global mechanism of Inter Particle Electrons Injection (IPEI) was discussed. The highest photocatalytic activity was observed for the system Cu/Cu(2)O/CuO (MB2 catalyst) under visible light (t(1/2)=24 min, k=159.7 x 10(-3)min(-1)) and for the heterojunction cascade Cu/Cu(2)O/CuO/TiO(2) (MB2 (50%)/TiO(2)) under UV-vis light (t(1/2)=4 min, k=1342 x 10(-3)min(-1)). In the last case, the high performance was attributed firstly to the electromotive forces developed under this configuration in which CuO energy bands mediate the electrons transfer from Cu(2)O to TiO(2). The formation of monobloc sensitizers also accounts for the decrease of the probability of the charges lost. It was demonstrated that "Cu(2)O/CuO" governs the capability of the heterojunction cascade and Cu does not play a significant role regardless of the heterojunction cascade efficiency. The electrical energy consumption per order of magnitude for photocatalytic degradation of Orange II was investigated for some representative catalytic systems. Visible/MB2 and UV/vis MB2 (50%)/TiO(2) exhibited respectively 0.340 and 0.05 kW hm(-3) demonstrating the high efficiency of the systems.