Development of a visible-light-active-NiTiO3 coating for the efficient removal of the persistent herbicide 2,6-dichlorobenzamide (BAM) from drinking water.

In the present research work, the photocatalytic evaluation of NiTiO3 nanoparticles immobilized on glass plates by the spin-coating procedure was carried out in the degradation of the recalcitrant herbicide 2,6-dichlorobenzamide (BAM). The concentrations of Ni employed to synthesize NiTiO3 nanoparticles were 1 wt% (1TESNi) and 2 wt% (2TESNi). The stability of coatings was evaluated by several washings and thermal treatments, which were verified by UV-vis analyses. The morphology of the coatings was studied by scanning electron microscopy (SEM-EDS). The coatings displayed thickness values of 1.35 and 2.56 µm for TiO2 and 1TESNi, respectively. The crystalline phases of the coatings were analyzed by X-ray diffraction (XRD), confirming the presence of NiTiO3 and other phases related to TiO2. The bandgap of 1TESNi, compared with the bare TiO2, was reduced from 2.96 to 2.40 eV as a consequence of Ni addition. The TiO2, 1TESNi and 2TESNi coatings were evaluated in the photodegradation of BAM using visible-light for 240 min. The highest effectiveness was displayed by the 1TESNi coating, obtaining degradation of 92.56% after 240 min. Also, the photocatalytic efficiency of the 1TESNi coating was only reduced 1.99% after 3 reuse cycles in the BAM degradation. The scavenger tests revealed that the main oxidizing species involved in the reaction were the •OH- and •O2- radicals. The 1TESNi coating showed the highest photocatalytic efficiency because of its absorption in the visible-light region, valuable surface area and electronic charge separation. Thus, these advantageous features guarantee that NiTiO3 coatings are an efficient method for degrading recalcitrant herbicides from drinking water using a practical way to recover and reuse photocatalysts.

Novel polypropylene-TiO2:Bi spherical floater for the efficient photocatalytic degradation of the recalcitrant 2,4,6-TCP herbicide.

In this work, spherical photocatalytic floaters were fabricated by depositing TiO2:Bi (TBi) particles on polypropylene (PP) spheres (recycled from beer cans). These particles were deposited on the sphere (TBi-sphere) by the spray coating technique and evaluated their performance for the photocatalytic degradation of 2,4,6-trichlorophenol (2,4,6-TCP) herbicide. SEM images demonstrated that the BTi powders consisted in conglomerated grains with sizes of 20-80 nm and the analysis by X-ray diffraction confirmed the presence of rutile and anatase phases in the BTi. The photocatalytic experiments showed that the TBi and TBi-sphere produced maximum degradation of 90 and 97% for 2,4,6-TCP, respectively, after 4 h under UV-Vis light. The photocatalytic powders/composites were reused 3 times and the loss of degradation efficiency was 3 and 16% for the TBi powder and TBi-sphere, respectively. This means that the TBi-sphere is more stable for the continuous degradation of the 2,4,6-TCP contaminant. The TiO2:Bi powder was compared with the commercial TiO2 (P25) and found that the TiO2:Bi powder had higher light absorption (≈42%) and higher surface area (≈105%) than the P25. Therefore, the degradation percentage for the 2,4,6-TCP was 52% higher in the sample doped with Bi. Also, scavenger experiments were carried out and found that the main oxidizing agents produced for the degradation of 2,4,6-TCP were •OH- radicals and •O2- anions. Other species such as h+ were also produced at lower amount. Hence, our results demonstrated that spherical/floatable photocatalytic composites are a viable option to remove herbicide residuals from the water, which is of interest in water-treatment-plants.

An eco-friendly and sustainable support of agave-fibers functionalized with graphene/TiO2:SnO2 for the photocatalytic degradation of the 2,4-D herbicide from the drinking water.

In this research, we evaluated the photocatalytic performance of biodegradable composites for the removal of the 2,4-Dichlorophenoxyacetic acid (2,4-D) herbicide. The composite was composed by agave fibers (AgF), graphene-microplates (GM) and titanium dioxide TiO2/SnO2 (TSn) nanoparticles (NPs) and was named TSn + AgF/GM. Both, the TSn NPs and the GM were deposited on the AgF using the Dip-coating method. According to the analysis by X-Ray Diffraction (XRD), the crystalline phase for the TiO2 and SnO2 was anatase and tetragonal-rutile, respectively. The Scanning Electron Microscopy (SEM) images demonstrated that the AgF were completely saturated by the GM (which had average dimensions of 15 µm × 22 µm) and by conglomerations of TSn NPs with average size of 642 nm. The TSn NPs and the TSn + AgF/GM composite were evaluated for the photocatalytic degradation of the 2,4-D herbicide under ultraviolet-visible (UV-Vis) light and found a maximum degradation of 98.4 and 93.7% (after 4 h) for the TSn NPs and the TSn + AgF/GM composite, respectively. Reuse cycles were also performed and the degradation percentage decreased by 13.1% and by 7.8% (after 3 cycles of reuse) when the TSn NPs and the TSn + AgF/GM composite are employed, respectively. Scavenger experiments were also carried out and found that the oxidizing agents are mainly produced in the order of: •OH>•O2- > h+; then, the main oxidizing agents generated during the photocatalytic reaction were the hydroxyl radicals. Thus, the photocatalytic system studied in this work for the degradation of 2,4-D could pave the way for the development of new eco-friendly/floatable photocatalysts, which can be applied in wastewater-treatment plants.