RESUMO
The ion-specific hydration states of zwitterionic poly(3-( N-2-methacryloyloxyethyl- N, N-dimethyl)ammonatopropanesulfonate) (PMAPS) brushes in various aqueous solutions were investigated by neutron reflectivity (NR) and atomic force microscopy (AFM). The asymmetric hydration state of the PMAPS brushes was verified from the NR scattering-length density profiles, while the variation in their swollen thickness was complementary as determined from AFM topographic images. PMAPS brushes got thicker in any salt solutions, while the extent of swelling and the dimensions of swollen chain structure were dependent on the ion species and salt concentration in the solutions. Anion specificity was clearly observed, whereas cations exhibited weaker modulation in ion-specific hydration states. The anion specificity could be ascribed to ion-specific interactions between the quaternary ammonium cation in sulfobetaine and the anions. The weak cation specificity was attributed to the intrinsically weak cohesive interactions between the weakly hydrated sulfonate anion in sulfobetaine and the strongly hydrated cations. The ion-specific hydration of PMAPS brushes was largely consistent with the ion-specific aggregation state of the PMAPS chains in aqueous solutions.
RESUMO
Effect of alkyl chain spacer length between the charged groups (CSL) in zwitterionic poly(sulfobetaine) (PSB) brushes on the hydration state was investigated. PSB brushes with ethyl (PMAES), propyl (PMAPS), or butyl (PMABS) CSL were prepared by surface-initiated atom transfer radical polymerization on silicon wafers. Hydration states of the PSB brushes in aqueous solutions and/or humid vapor were investigated by contact angle measurement, infrared spectroscopy, AFM observation, and neutron reflectivity. The PSB brushes are swollen in humid air and deionized water due to the hydration of the charged groups leading to the reduction of hydrated PSB brushes/water interfacial free energy. The hydrated PSB brushes exhibit clear interface with low interfacial roughness due to networking of the PSB brush chains through association of the SBs. The hydrated PSB brushes produce diffusive swollen layer in the presence of NaCl because of the charge screening followed by SB dissociation by the bound ions. The ionic strength sensitivity in the hydration got more significant with increasing the CSL in SBs because of the augmentation in partial charge by charged group separation.