Additive Manufacturing of CrFeNiTi Multi-Principal Element Alloys.

High entropy alloys (HEAs) and their closely related variants, called multi-principal element alloys (MPEAs), are the topic of a rather new area of research, and so far, the gathered knowledge is incomplete. This is especially true when it comes to material libraries, as the fabrication of HEA and MPEA samples with a wide variation in chemical compositions is challenging in itself. Additive manufacturing technologies are, to date, seen as possibly the best option to quickly fabricate HEA and MPEA samples, offering both the melting metallurgical and solid-state sintering approach. Within this study, CrFeNiTi MPEA samples were fabricated via laser powder-bed fusion (PBF-LB) and solid-state sintering of mechanically alloyed powder feedstock. The main emphasis is on the PBF-LB process, while solid-state sintering serves as benchmark. Within a volumetric energy density (VED) window of 50 J/mm3 to 83 J/mm3, dense samples with large defect-free sections and an average micro-hardness of 965 HV0.1 were fabricated. Clear correlations between the local chemical alloy composition and the related micro-hardness were recorded, with the main factor being the evaporation of titanium at higher VED settings through a reduction in the C14_Laves phase fraction.

Heat Treatments and Critical Quenching Rates in Additively Manufactured Al-Si-Mg Alloys.

Laser powder-bed fusion (LPBF) has significantly gained in importance and has become one of the major fabrication techniques within metal additive manufacturing. The fast cooling rates achieved in LPBF due to a relatively small melt pool on a much larger component or substrate, acting as heat sink, result in fine-grained microstructures and high oversaturation of alloying elements in the α-aluminum. Al-Si-Mg alloys thus can be effectively precipitation hardened. Moreover, the solidified material undergoes an intrinsic heat treatment, whilst the layers above are irradiated and the elevated temperature in the built chamber starts the clustering process of alloying elements directly after a scan track is fabricated. These silicon-magnesium clusters were observed with atom probe tomography in as-built samples. Similar beneficial clustering behavior at higher temperatures is known from the direct-aging approach in cast samples, whereby the artificial aging is performed immediately after solution annealing and quenching. Transferring this approach to LPBF samples as a possible post-heat treatment revealed that even after direct aging, the outstanding hardness of the as-built condition could, at best, be met, but for most instances it was significantly lower. Our investigations showed that LPBF Al-Si-Mg exhibited a high dependency on the quenching rate, which is significantly more pronounced than in cast reference samples, requiring two to three times higher quenching rate after solution annealing to yield similar hardness results. This suggests that due to the finer microstructure and the shorter diffusion path in Al-Si-Mg fabricated by LPBF, it is more challenging to achieve a metastable oversaturation necessary for precipitation hardening. This may be especially problematic in larger components.

On the Anisotropic Mechanical Properties of Selective Laser-Melted Stainless Steel.

The thorough description of the peculiarities of additively manufactured (AM) structures represents a current challenge for aspiring freeform fabrication methods, such as selective laser melting (SLM). These methods have an immense advantage in the fast fabrication (no special tooling or moulds required) of components, geometrical flexibility in their design, and efficiency when only small quantities are required. However, designs demand precise knowledge of the material properties, which in the case of additively manufactured structures are anisotropic and, under certain circumstances, inhomogeneous in nature. Furthermore, these characteristics are highly dependent on the fabrication settings. In this study, the anisotropic tensile properties of selective laser-melted stainless steel (1.4404, 316L) are investigated: the Young's modulus ranged from 148 to 227 GPa, the ultimate tensile strength from 512 to 699 MPa, and the breaking elongation ranged, respectively, from 12% to 43%. The results were compared to related studies in order to classify the influence of the fabrication settings. Furthermore, the influence of the chosen raw material was addressed by comparing deviations on the directional dependencies reasoned from differing microstructural developments during manufacture. Stainless steel was found to possess its maximum strength at a 45° layer versus loading offset, which is precisely where AlSi10Mg was previously reported to be at its weakest.