Cobalt-Doped Carbon Nitride Frameworks Obtained from Calcined Aromatic Polyimines as Cathode Catalyst of Anion Exchange Membrane Fuel Cells.

Cobalt-doped carbon nitride frameworks (CoNC) were prepared from the calcination of Co-chelated aromatic polyimines (APIM) synthesized from stepwise polymerization of p-phenylene diamine (PDA) and o-phthalaldehyde (OPAl) via Schiff base reactions in the presence of cobalt (II) chloride. The Co-chelated APIM (Co-APIM) precursor converted to CoNC after calcination in two-step heating with the second step performed at 100 °C lower than the first one. The CoNCs demonstrated that its Co, N-co-doped carbonaceous framework contained both graphene and carbon nanotube, as characterized by X-ray diffraction pattern, Raman spectra, and TEM micropictures. CoNCs also revealed a significant ORR peak in the current-voltage polarization cycle and a higher O2 reduction current than that of commercial Pt/C in a linear scanning voltage test in O2-saturated KOH(aq). The calculated e-transferred number even reaches 3.94 in KOH(aq) for the CoNC1000A900 cathode catalyst, which has the highest BET surface area of 393.94 m2 g-1. Single cells of anion exchange membrane fuel cells (AEMFCs) are fabricated using different CoNCs as the cathode catalysts, and CoNC1000A900 demonstrates a peak power density of 374.3 compared to the 334.7 mW cm-2 obtained from the single cell using Pt/C as the cathode catalyst.

New Inverse Emulsion-Polymerized Iron/Polyaniline Composites for Permanent, Highly Magnetic Iron Compounds via Calcination.

The hydrophilic initiator potassium persulfate (KPS) was converted into a hydrophobic molecule by complexing with cetyltrimethylammonium bromide (CTAB) at both ends of the molecule (CTAPSu). Inverse emulsion polymerization thus proceeded inside micelles dispersed in the affluent toluene with CTAPSu as the initiator. Polyaniline (PANI) formed inside the micelles and entangled with Fe3O4 nanoparticles already esterified with oleic acid (OA). Iron composites consisted of OA-esterified Fe3O4 nanoparticles covered with PANI after de-emulsification. After calcination at 950 °C in an argon atmosphere, the resultant iron compound was a mixture of α-Fe (ferrite) and Fe3C (cementite), as determined by X-ray diffraction. Eventually, the calcined iron compounds (mixtures) demonstrated superparamagnetic properties with a high saturation magnetization (Ms) of 197 emu/g, which decayed to 160 emu/g after exposure to the atmosphere for four months.

Superparamagnetic, High Magnetic α-Fe & α″-Fe16N2 Mixture Prepared from Inverse Suspension-Polymerized Fe3O4@polyaniline Composite.

Oleic acid (OA)-modified Fe3O4 nanoparticles were successfully covered with polyanilines (PANIs) via inverse suspension polymerization in accordance with SEM and TEM micrographs. The obtained nanoparticles were able to develop into a ferrite (α-Fe) and α″-Fe16N2 mixture with a superparamagnetic property and high saturated magnetization (SM) of 245 emu g-1 at 950 °C calcination under the protection of carbonization materials (calcined PANI) and other iron-compounds (α″-Fe16N2). The SM of the calcined iron-composites slightly decreases to 232 emu g-1 after staying in the open air for 3 months. The calcined mixture composite can be ground into homogeneous powders without the segregation of the iron and carbon phases in the mortar without significantly losing magnetic activities.