Photocatalytic and Photothermal Antimicrobial Mussel-Inspired Nanocomposites for Biomedical Applications.

Bacterial infection has traditionally been treated with antibiotics, but their overuse is leading to the development of antibiotic resistance. This may be mitigated by alternative approaches to prevent or treat bacterial infections without utilization of antibiotics. Among the alternatives is the use of photo-responsive antimicrobial nanoparticles and/or nanocomposites, which present unique properties activated by light. In this study, we explored the combined use of titanium oxide and polydopamine to create nanoparticles with photocatalytic and photothermal antibacterial properties triggered by visible or near-infrared light. Furthermore, as a proof-of-concept, these photo-responsive nanoparticles were combined with mussel-inspired catechol-modified hyaluronic acid hydrogels to form novel light-driven antibacterial nanocomposites. The materials were challenged with models of Gram-negative and Gram-positive bacteria. For visible light, the average percentage killed (PK) was 94.6 for E. coli and 92.3 for S. aureus. For near-infrared light, PK for E. coli reported 52.8 and 99.2 for S. aureus. These results confirm the exciting potential of these nanocomposites to prevent the development of antibiotic resistance and also to open the door for further studies to optimize their composition in order to increase their bactericidal efficacy for biomedical applications.

Mechanical Properties of Ternary Composite from Waste Leather Fibers and Waste Polyamide Fibers with Acrylonitrile-Butadiene Rubber.

This study aimed to improve the mechanical properties of a composite material consisting of waste leather fibers (LF) and nitrile rubber (NBR) by partially replacing LF with waste polyamide fibers (PA). A ternary recycled composite NBR/LF/PA was produced by a simple mixing method and vulcanized by compression molding. The mechanical properties and dynamic mechanical properties of the composite were investigated in detail. The results showed that the mechanical properties of NBR/LF/PA increased with an increase in the PA ratio. The highest tensile strength value of NBR/LF/PA was found to have increased about 1.26 times, that is from 12.9 MPa of LF50 to 16.3 MPa of LF25PA25. Additionally, the ternary composite demonstrated high hysteresis loss, which was confirmed by dynamic mechanical analysis (DMA). The presence of PA formed a non-woven network that significantly enhanced the abrasion resistance of the composite compared to NBR/LF. The failure mechanism was also analyzed through the observation of the failure surface using scanning electron microscopy (SEM). These findings suggest that the utilization of both waste fiber products together is a sustainable approach to reducing fibrous waste while improving the qualities of recycled rubber composites.