Influence of sample surface topography on laser ablation process.

In this work we discuss how sample surface topography can significantly influence the laser ablation (LA) process and, in turn, the analytical response of the LA Inductively Coupled Plasma Mass Spectrometry (LA-ICP-MS) method. Six different surface topographies were prepared on a certified aluminium alloy sample BAM 311 and SRM NIST 610 to investigate the phenomenon. All the samples were repetitively measured by LA-ICP-MS using a spot by spot analysis. The effect of laser fluence in the range of 1-13 J/cm2 was studied. For majority of measured isotopes, the ICP-MS signal was amplified with roughening of the sample surface. A stronger effect was observed on the Al alloy sample, where the more than sixty-time enhancement was achieved in comparison to the polished surface of the sample. Since the effect of surface topography is different for each analyte, it can be stated that surface properties affect not only the ICP-MS response, but also elemental fractionation in LA. The presented results show that different surface topographies may lead to misleading data interpretation because even when applying ablation preshots, the signal of individual elements changes. The utmost care must be taken when preparing the surface for single shot analysis or chemical mapping. On the other hand, by roughening the sample surface, it is possible to significantly increase the sensitivity of the method for individual analytes and supress a matrix effect.

Feasibility of Nanoparticle-Enhanced Laser Ablation Inductively Coupled Plasma Mass Spectrometry.

Nanoparticles (NPs) applied to the surface of some solids can increase signals in inductively coupled plasma mass spectrometry (ICPMS). Drops containing 20 and/or 40 nm nanoparticles of Ag and/or Au were deposited on metallic and ceramic/glass samples, and after being dried, both the samples treated with NPs and plain targets were ablated by one pulse per spot. The laser ablation ICPMS (LA-ICPMS) signals were enhanced for metallic samples modified with NPs in comparison to signals produced at the plain, untreated surface. Maps of LA-ICPMS signals recorded for several laser fluences show that the NP-induced signal enhancement exceeds even 2 orders of magnitude for metallic samples. No enhancement was achieved for nonconductive samples. This enhancement is limited to the peripheral annular region of the dried droplet area where NPs are concentrated due to the "coffee stain" effect. Ablation crater profilometric inspection revealed a more uniform material rearrangement over the NP-treated surface compared with the ablated plain target. However, besides a smoother crater bottom, no other evidence of an NP-enhancing effect was noticed, although an increased ablation rate was anticipated. Limits of detection dropped by 1 order of magnitude for the minor elements in the presence of NPs. Observed phenomena depend only on the NP surface concentration but not on the material or size of the NPs. An electron microprobe study of the collected ablation aerosol has shown that aerosol particles consisting of target material are aggregated around the NPs. The hypothesis is that such aggregates exhibit better transport/vaporization efficiency, thus enhancing signals for metallic samples. A detailed study of the suggested mechanism will be continued in ongoing work.

Investigation of the microstructure and mineralogical composition of urinary calculi fragments by synchrotron radiation X-ray microtomography: a feasibility study.

The outcomes from the feasibility study on utilization of synchrotron radiation X-ray microtomography (SR-µCT) to investigate the texture and the quantitative mineralogical composition of selected calcium oxalate-based urinary calculi fragments are presented. The comparison of the results obtained by SR-µCT analysis with those derived from current standard analytical approaches is provided. SR-µCT is proved as a potential effective technique for determination of texture, 3D microstructure, and composition of kidney stones.

Tungsten carbide precursors as an example for influence of a binder on the particle formation in the nanosecond laser ablation of powdered materials.

A study of LA-ICP-MS analysis of pressed powdered tungsten carbide precursors was performed to show the advantages and problems of nanosecond laser ablation of matrix-unified samples. Five samples with different compositions were pressed into pellets both with silver powder as a binder serving to keep the matrix unified, and without any binder. The laser ablation was performed by nanosecond Nd:YAG laser working at 213 nm. The particle formation during ablation of both sets of pellets was studied using an optical aerosol spectrometer allowing the measurement of particle concentration in two size ranges (10-250 nm and 0.25-17 microm) and particle size distribution in the range of 0.25-17 microm. Additionally, the structure of the laser-generated particles was studied after their collection on a filter using a scanning electron microscope (SEM) and the particle chemical composition was determined by an energy dispersive X-ray spectroscope (EDS). The matrix effect was proved to be reduced using the same silver powdered binder for pellet preparation in the case of the laser ablation of powdered materials. The LA-ICP-MS signal dependence on the element content present in the material showed an improved correlation for Co, Ti, Ta and Nb of the matrix-unified samples compared to the non-matrix-unified pellets. In the case of W, the ICP-MS signal of matrix-unified pellets was influenced by the changes in the particle formation.

Direct solid analysis of powdered tungsten carbide hardmetal precursors by laser-induced argon spark ablation with inductively coupled plasma atomic emission spectrometry.

The potential of the laser-induced argon spark atomizer (LINA-Spark atomizer) coupled with ICP-AES as a convenient device for direct analysis of WC/Co powdered precursors of sintered hardmetals was studied. The samples were presented for the ablation as pressed pellets prepared by mixing with powdered silver binder containing GeO2 as internal standard. The pellets were ablated with the aid of a Q-switched Nd:YAG laser (1064 nm) focused 16 mm behind the target surface with a resulting estimated power density of 5 GW cm(-2). Laser ablation ICP-AES signals were studied as a function of ablation time, and the duration of time prior to measurement (pre-ablation time) which was necessary to obtain reliable results was about 40 s. Linear calibration plots were obtained up to 10% (m/m) Ti, 9% Ta and 3.5% Nb both without internal standardization and by using germanium as an added internal standard or tungsten as a contained internal standard. The relative uncertainty at the centroid of the calibration line was in the range from +/- 6% to +/- 11% for Nb, Ta and Ti both with and without internal standardisation by Ge. A higher spread of points about the regression was observed for cobalt for which the relative uncertainty at the centroid was in the range from +/- 9% to +/- 14%. Repeatability of results was improved by the use of both Ge and W internal standards. The lowest determinable quantities calculated for calibration plots were 0.060% Co, 0.010% Nb, 0.16% Ta and 0.030% Ti with internal standardization by Ge. The LA-ICP-AES analyses of real samples led to good agreement with the results obtained by solution-based ICP determination with a relative bias not exceeding 10%. The elimination of the dissolution procedure of powdered tungsten (Nb, Ta, Ti) carbide is the principal advantage of the developed LA-ICP-AES method.