RESUMO
Thin polycrystalline films of the solar absorber copper-zinc-tin-sulfide (CZTS) were formed by annealing coatings deposited on molybdenum-coated soda lime glass via ultrasonic spraying of aerosol droplets from colloidal CZTS nanocrystal dispersions. Production of uniform continuous nanocrystal coatings with ultrasonic spraying requires that the evaporation time is longer than the aerosol flight time from the spray nozzle to the substrate such that the aerosol droplets still have low enough viscosity to smooth the impact craters that form on the coating surface. In this work, evaporation was slowed by adding a high boiling point cosolvent, cyclohexanone, to toluene as the dispersing liquid. We analyzed, quantitatively, the effects of the solvent composition on the aerosol and coating drying dynamics using an aerosol evaporation model. Annealing coatings in sulfur vapor converts them into polycrystalline films with micrometer size grains, but the grains form continuous films only when Na is present during annealing to enhance grain growth. Continuous films are easier to form when the average nanocrystal size is 15 nm: using larger nanocrystals (e.g., 20 nm) sacrifices film continuity.
RESUMO
A three-step method to create dense polycrystalline semiconductor thin films from nanocrystal liquid dispersions is described. First, suitable substrates are coated with nanocrystals using aerosol-jet printing. Second, the porous nanocrystal coatings are compacted using a weighted roller or a hydraulic press to increase the coating density. Finally, the resulting coating is annealed for grain growth. The approach is demonstrated for making polycrystalline films of copper zinc tin sulfide (CZTS), a new solar absorber composed of earth-abundant elements. The range of coating morphologies accessible through aerosol-jet printing is examined and their formation mechanisms are revealed. Crack-free albeit porous films are obtained if most of the solvent in the aerosolized dispersion droplets containing the nanocrystals evaporates before they impinge on the substrate. In this case, nanocrystals agglomerate in flight and arrive at the substrate as solid spherical agglomerates. These porous coatings are mechanically compacted, and the density of the coating increases with compaction pressure. Dense coatings annealed in sulfur produce large-grain (>1 µm) polycrystalline CZTS films with microstructure suitable for thin-film solar cells.