Mixed oxides with corundum-type structure obtained from recycling can seals as paint pigments: color stability.

Green chromium and red iron oxides are technically important pigments due to their high color intensity, good dispersibility in paints, and superior hiding power. We report on the synthesis of colored pigments of mixed oxides with a corundum-type structure. The pigments are obtained via the addition of coloring ions to boehmite from recycled metallic aluminium. X-ray diffractometry (XRD) and Raman spectroscopy confirmed the crystallographic phase. Additionally, the oxidation state 3+ responsible for the greenish (chromium) and reddish (iron) coloration of the mixed oxides was confirmed by XPS and visible-light absorption measurements. The colorimetric stability of the oxides in acid and alkaline environments was evaluated. After 240 h of exposure to harsh environments, both pigments demonstrated stability and showed no strong color difference.

Synthesis of Blue Gahnite (ZnAl2O4:Co, Nd): A Cost-Effective Method for Producing Solar-Reflective Pigments for Cool Coatings.

Developing strategies for the green synthesis of novel materials, such as pigments for protection from solar radiation, is a fundamental research subject in material science to mitigate the heat island effect. Within this perspective, the current study reports on the synthesis of blue pigments of ZnAl2O4:M (M = Co2+ and Co2+/Nd3+) using recycled metallic aluminum (discarded can seal) with reflective properties of Near-infrared radiation. The pigments were characterized by XRD, SEM, XPS, UV-Vis, NIR diffuse reflectance spectroscopy, and CIE-1976 L*a*b* color measurements. The wettability of the coatings containing the synthesized pigments was also evaluated. The structural characterization showed that the pigments present the Gahnite crystalline phase. Colorimetric measurements obtained by the CIEL*a*b* method show values correlated to blue pigments attributed to Co2+ ions in tetrahedral sites. The pigments exhibit high near-infrared solar reflectance (with R% ≥ 60%), with an enhancement of nearly 20% for the pigment-containing neodymium when applied in white paint, indicating that the prepared compounds have the potential to be energy-saving color pigments for coatings.

Eco-Friendly Polysaccharide-Based Synthesis of Nanostructured MgO: Application in the Removal of Cu2+ in Wastewater.

The present study described three synthesis routes using different natural polysaccharides as low-cost non-toxic fuels and complexing agents for obtaining MgO. Cassava starch, Aloe vera leaves (mainly acemannan) gel, and citric pectin powder were mixed with magnesium nitrate salt and calcined at 750 °C for 2 h. The samples were named according to the polysaccharide: cassava starch (MgO-St), citrus pectin (MgO-CP), and Aloe vera (MgO-Av). X-ray diffraction identified the formation of a monophasic periclase structure (FCC type) for the three samples. The N2 adsorption/desorption isotherms (B.E.T. method) showed an important difference in textural properties, with a higher pore volume (Vmax = 89.76 cc/g) and higher surface area (SA = 43.93 m2/g) obtained for MgO-St, followed by MgO-CP (Vmax = 11.01 cc/g; SA = 7.01 m2/g) and MgO-Av (Vmax = 6.44 cc/g; SA = 6.63 m2/g). These data were consistent with the porous appearance observed in SEM images. Porous solids are interesting as adsorbents for removing metallic and molecular ions from wastewater. The removal of copper ions from water was evaluated, and the experimental data at equilibrium were adjusted according to the Freundlich, Langmuir, and Temkin isotherms. According to the Langmuir model, the maximum adsorption capacity (qmax) was 6331.117, 5831.244, and 6726.623 mg·g-1 for the adsorbents MgO-St, MgO-Av, and MgO-CP, respectively. The results of the adsorption isotherms indicated that the synthesized magnesium oxides could be used to decrease the amount of Cu2+ ions in wastewater.

Antiviral Properties against SARS-CoV-2 of Nanostructured ZnO Obtained by Green Combustion Synthesis and Coated in Waterborne Acrylic Coatings.

The COVID-19 pandemic has increased the need for developing disinfectant surfaces as well as reducing the spread of infections on contaminated surfaces and the contamination risk from the fomite route. The present work reports on the antiviral activity of coatings containing ZnO particles obtained by two simple synthesis routes using Aloe vera (ZnO-aloe) or cassava starch (ZnO-starch) as reaction fuel. After detailed characterization using XRD and NEXAFS, the obtained ZnO particles were dispersed in a proportion of 10% with two different waterborne acrylic coatings (binder and commercial white paint) and brushed on the surface of polycarbonates (PC). The cured ZnO/coatings were characterized by scanning electron microscopes (SEM) and energy-dispersive X-ray spectroscopy (EDS). Wettability tests were performed. The virucidal activity of the ZnO particles dispersed in the waterborne acrylic coating was compared to a reference control sample (PC plates). According to RT-PCR results, the ZnO-aloe/coating displays the highest outcome for antiviral activity against SARS-CoV-2 using the acrylic binder, inactivating >99% of the virus after 24 h of contact relative to reference control.

Synthesis and Characterization of Boehmite Particles Obtained from Recycling: Water Disinfection Application.

We report on the synthesis of boehmite aluminum oxide hydroxide particles with lamellar structure (γ-AlO(OH)) obtained from the recycling of metallic can seals, with the addition of silver nanoparticles (Ag-NPs) reduced by Aloe Vera extract. X-ray diffractometry (XRD) confirmed the γ-phase, and scanning electron microscopy (SEM) showed the presence of Ag-NPs on the boehmite particle surface, confirming the efficiency of the synthesis to obtain the composite material. The samples were used to treat lake water, according to the Standard Methods for the Examination of Water and Wastewater. The results indicated that the elimination of total coliforms and Escherichia coli occurred, with excellent efficiency for the Ag-boehmite sample. The tests show the possibility of reuse (5×) of the sample, as it maintained the efficiency of disinfection for E. coli. The preparation, use, and reuse of boehmite obtained from metallic waste is a case of a circular economy, focused on sustainability and green chemistry.

Experimental data for green synthesis of Zn-abietate complex from natural resin.

This data article is associated with the work "Ecofriendly synthesis of Zn-abietate complex derived from Pinus elliottii resin and its application as an antibacterial pigment against S. aureus and E. coli". The characterization data of the Zn-abietate complex obtained from Pinus elliottii resin and their reactional intermediary (Na-abietate) are reported. The Na-abietate was prepared with purified Pinus resin and sodium hydroxide (≥ 99%) in a stoichiometric ratio of 1:1. For the Zn-abietate synthesis was used ZnSO4 and Na-abietate solutions were at mild temperature and stirring without using organic solvents to ensuring the green character of the synthesis. Spectroscopic and structural characterization was consistent with an octahedral complex involving three carboxylate ligands per metal ion. X-ray photoelectron spectroscopy (XPS) analysis of the Na-abietate salt confirms the presence of carbonyl groups, carbon-oxygen atoms simple bonds (O-C/O=C), and carboxylate groups oxygen atoms (O-C=O). Analysis of the Zn LMM Auger, for the Zn-abietate complex, indicates the presence of zinc atoms with oxidation state Zn2+, this is supported by the distance between Zn 2p3/2 and 1p1/2 in the XPS spectrum. Together, these data will be useful for the structural representation of the samples.

Polysaccharides as Green Fuels for the Synthesis of MgO: Characterization and Evaluation of Antimicrobial Activities.

The synthesis of structured MgO is reported using feedstock starch (route I), citrus pectin (route II), and Aloe vera (route III) leaf, which are suitable for use as green fuels due to their abundance, low cost, and non-toxicity. The oxides formed showed high porosity and were evaluated as antimicrobial agents. The samples were characterized by energy-dispersive X-ray fluorescence (EDXRF), X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The crystalline periclase monophase of the MgO was identified for all samples. The SEM analyses show that the sample morphology depends on the organic fuel used during the synthesis. The antibacterial activity of the MgO-St (starch), MgO-CP (citrus pectin), and MgO-Av (Aloe vera) oxides was evaluated against pathogens Staphylococcus aureus (ATCC 6538P) and Escherichia coli (ATCC 8739). Antifungal activity was also studied against Candida albicans (ATCC 64548). The studies were carried out using the qualitative agar disk diffusion method and quantitative minimum inhibitory concentration (MIC) tests. The MIC of each sample showed the same inhibitory concentration of 400 µg. mL-1 for the studied microorganisms. The formation of inhibition zones and the MIC values in the antimicrobial analysis indicate the effective antimicrobial activity of the samples against the test microorganisms.