Wire Laser Metal Deposition Additive Manufacturing of Duplex Stainless Steel Components-Development of a Systematic Methodology.

A systematic four-stage methodology was developed and applied to the Laser Metal Deposition with Wire (LMDw) of a duplex stainless steel (DSS) cylinder > 20 kg. In the four stages, single-bead passes, a single-bead wall, a block, and finally a cylinder were produced. This stepwise approach allowed the development of LMDw process parameters and control systems while the volume of deposited material and the geometrical complexity of components increased. The as-deposited microstructure was inhomogeneous and repetitive, consisting of highly ferritic regions with nitrides and regions with high fractions of austenite. However, there were no cracks or lack of fusion defects; there were only some small pores, and strength and toughness were comparable to those of the corresponding steel grade. A heat treatment for 1 h at 1100 °C was performed to homogenize the microstructure, remove nitrides, and balance the ferrite and austenite fractions compensating for nitrogen loss occurring during LMDw. The heat treatment increased toughness and ductility and decreased strength, but these still matched steel properties. It was concluded that implementing a systematic methodology with a stepwise increase in the deposited volume and geometrical complexity is a cost-effective way of developing additive manufacturing procedures for the production of significantly sized metallic components.

Effect of Sigma Phase Morphology on the Degradation of Properties in a Super Duplex Stainless Steel.

Sigma phase is commonly considered to be the most deleterious secondary phase precipitating in duplex stainless steels, as it results in an extreme reduction of corrosion resistance and toughness. Previous studies have mainly focused on the kinetics of sigma phase precipitation and influences on properties and only a few works have studied the morphology of sigma phase and its influences on material properties. Therefore, the influence of sigma phase morphology on the degradation of corrosion resistance and mechanical properties of 2507 super duplex stainless steel (SDSS) was studied after 10 h of arc heat treatment using optical and scanning electron microscopy, electron backscattered diffraction analysis, corrosion testing, and thermodynamic calculations. A stationary arc was applied on the 2507 SDSS disc mounted on a water-cooled chamber, producing a steady-state temperature gradient covering the entire temperature range from room temperature to the melting point. Sigma phase was the major intermetallic precipitating between 630 °C and 1010 °C and its morphology changed from blocky to fine coral-shaped with decreasing aging temperature. At the same time, the average thickness of the precipitates decreased from 2.9 µm to 0.5 µm. The chemical composition of sigma was similar to that predicted by thermodynamic calculations when formed at 800⁻900 °C, but deviated at higher and lower temperatures. The formation of blocky sigma phase introduced local strain in the bulk of the primary austenite grains. However, the local strain was most pronounced in the secondary austenite grains next to the coral-shaped sigma phase precipitating at lower temperatures. Microstructures with blocky and coral-shaped sigma phase particles were prone to develop microscale cracks and local corrosion, respectively. Local corrosion occurred primarily in ferrite and in secondary austenite, which was predicted by thermodynamic calculations to have a low pitting resistance equivalent. To conclude, the influence of sigma phase morphology on the degradation of properties was summarized in two diagrams as functions of the level of static load and the severity of the corrosive environment.