RESUMO
Long-fiber thermoplastic (LFT) materials compounded via the direct LFT (LFT-D) process are very versatile composites in which polymers and continuous reinforcement fiber can be combined in almost any way. Polycarbonate (PC) as an amorphous thermoplastic matrix system reinforced with glass fibers (GFs) is a promising addition regarding the current development needs, for example battery enclosures for electromobility. Two approaches to the processing and compression molding of PC GF LFT-D materials with various parameter combinations of screw speed and fiber rovings are presented. The resulting fiber lengths averaged around 0.5 mm for all settings. The tensile, bending, Charpy, and impact properties were characterized and discussed in detail. Special attention to the characteristic charge and flow area formed by compression molding of LFT-D materials, as well as sample orientation was given. The tensile modulus was 10 GPa, while the strength surpassed 125 MPa. The flexural modulus can reach up to 11 GPa, and the flexural strength reached up to 216 MPa. PC GF LFT-D is a viable addition to the LFT-D process, exhibiting good mechanical properties and stable processability.
RESUMO
The effect of hybrid carbon fillers of multi-walled carbon nanotubes (CNT) and carbon black (CB) on the electrical and morphological properties of polystyrene (PS) nanocomposites were systematically investigated in microinjection molding (µIM). The polymer nanocomposites with three different filler concentrations (i.e., 3, 5 and 10 wt %) at various weight ratios of CNT/CB (100/0, 30/70, 50/50, 70/30, 0/100) were prepared by melt blending, then followed by µIM under a defined set of processing conditions. A rectangular mold insert which has three consecutive zones with decreasing thickness along the flow direction was adopted to study abrupt changes in mold geometry on the properties of resultant microparts. The distribution of carbon fillers within microparts was observed by scanning electron microscopy, which was correlated with electrical conductivity measurements. Results indicated that there is a flow-induced orientation of incorporated carbon fillers and this orientation increased with increasing shearing effect along the flow direction. High structure CB is found to be more effective than CNT in terms of enhancing the electrical conductivity, which was attributed to the good dispersion of CB in PS and their ability to form conductive networks via self-assembly. Morphology observations indicated that there is a shear-induced depletion of CB particles in the shear layer, which is due to the marked difference of shear rates between the shear and core layers of the molded microparts. Moreover, an annealing treatment is beneficial to enhance the electrical conductivity of CNT-containing microparts.
RESUMO
Cellulosic nanomaterials provide a novel and sustainable platform for the production of high performance materials enabled by nanotechnology. Bacterial cellulose (BC) is a highly crystalline material and contains pure cellulose without lignin and hemicellulose. BC offers an opportunity to provide control of the products' properties in-situ, via specific BC production methods and culture conditions. The BC potential in advanced material applications are hindered by a limited knowledge of optimal BC production conditions, efficient process scale-up, separation methods, and purification methods. There is a growing body of work on the production of bacterial cellulose nanocrystals (BCNs) from BC fibers. However, there is limited information regarding the effect of BC fibers' characteristics on the production of nanocrystals. This review describes developments in BC and BCNs production methods and factors affecting their yield and physical characteristics.