Potential for Recycling Metakaolin/Slag-Based Geopolymer Concrete of Various Strength Levels in Freeze-Thaw Conditions.

Geopolymer concrete (GPC) represents an innovative green and low-carbon construction material, offering a viable alternative to ordinary Portland cement concrete (OPC) in building applications. However, existing studies tend to overlook the recyclability aspect of GPC for future use. Various structural applications necessitate the use of concrete with distinct strength characteristics. The recyclability of the parent concrete is influenced by these varying strengths. This study examined the recycling potential of GPC across a spectrum of strength grades (40, 60, 80, and 100 MPa, marked as C40, C60, C80, and C100) when subjected to freeze-thaw conditions. Recycling 5-16 mm recycled geopolymer coarse aggregate (RGAs) from GPC prepared from 5 to 16 mm natural coarse aggregates (NAs). The cementitious material comprised 60% metakaolin and 40% slag, with natural gravel serving as the NAs, and the alkali activator consisting of sodium hydroxide solution and sodium silicate solution. The strength of the GPC was modulated by altering the Na/Al ratio. After 350 freeze-thaw cycles, the GPC specimens underwent crushing, washing, and sieving to produce RGAs. Subsequently, their physical properties (apparent density, water absorption, crushing index, and attached mortar content and microstructure (microhardness, SEM, and XRD) were thoroughly examined. The findings indicated that GPC with strength grades of C100, C80, and C60 were capable of enduring 350 freeze-thaw cycles, in contrast to C40, which did not withstand these conditions. RGAs derived from GPC of strength grades C100 and C80 complied with the criteria for Class II recycled aggregates, whereas RGAs produced from GPC of strength grade C60 aligned with the Class III level. A higher-strength grade in the parent concrete correlated with enhanced performance characteristics in the resulting recycled aggregates.

Influence of Alkali-Activators on Acid Rain Resistance of Geopolymer-Recycled Pervious Concrete with Optimal Pore Size.

Geopolymer-recycled pervious concrete (GRPC) is a novel concrete that can effectively inhibit the corrosion of acid rain and alleviate urban waterlog. The goal of this study is to ascertain the optimal pore size of GRPC and study its acid rain resistance activated by different alkali-activators. Three different sizes (0.8, 1.0, and 1.2 mm) were separately chosen as the pore diameters of GRPC. The alkali-activator solution adopted sodium hydroxide (NaOH), sodium silicate (Na2SiO3), and a mixture of the two. The mechanical properties and permeability coefficient were tested to determine the optimal pore size of GRPC. After that, specimens with the optimal pore size were immersed in a simulative acid rain solution (sulfuric acid solution with pH = 4.0) for 6 d and were dried 1 d until 56 d. The effects of different alkali activators on acid rain resistance of GRPC were analyzed by compressive strength, neutralization depth, and mass loss. The results manifested that the mechanical properties of GRPC were excellent, the compressive strength of GRPCH+N reached more than 60.1 MPa, and their splitting tensile strength attained more than 5.9 MPa, meeting the strength requirement of the road for heavy traffic load. Considering the mechanical properties and the acid rain purification effect of alkaline GRPC required a relatively small permeability coefficient; the optimal pore size was 1 mm. When specimens with optimal pore size were exposed to acid solution, the corrosion products (gypsums) would block the pores of GRPC to inhibit further corrosion, keeping the stability of the compressive strength. GRPC activated by the mixture of NaOH and Na2SiO3 generated a more stable amorphous three-dimensional network structure, endowing GRPCH+N with better mechanical properties and acid corrosion resistance.

Effect of Ordinary Portland Cement on Mechanical Properties and Microstructures of Metakaolin-Based Geopolymers.

Geopolymers have been considered a sustainable alternative to ordinary Portland cement (CEM I) for its lower embodied carbon and ability to make use of industrial by-products. Additionally, its excellent engineering properties of high strength, low permeability, good chemical resistance, and excellent fire resistance also strike a chord in the minds of researchers. The goal of this study is to clarify the effect of calcium sources on the mechanical properties and microstructures of the geopolymers. CEM I was chosen as the sole calcium source, while metakaolin was used as the source material. Five distinct geopolymers were prepared, having various ratio of CEM I: 0%, 5%, 10%, 20%, and 30%. The alkali-activator was a mixture of 12 M sodium hydroxide (NaOH) and sodium silicate (Na2SiO3), utilizing compressive strength and flexural strength to evaluate the changes of the geopolymers' mechanical properties. SEM, XRD, and FTIR were used to examine microscopic features, evaluate internal morphology, and analyze changes in components of the geopolymers containing different amounts of CEM I. The experimental results indicated that the optimal incorporation of CEM I was 5%. Under this dosage, the compressive strength and flexural strength of the geopolymers can reach 71.1 MPa and 6.75 MPa, respectively. With the incorporation of CEM I, the heat released by cement hydration can accelerate the geopolymerization reaction between silica-alumina materials and alkaline solutions. Additionally, the coexistence of N-A-S-H gel from components of an aluminosilicate mix and C-S-H gel from the CEM I promoted a more densified microstructure of the geopolymers and improved the geopolymer's strength. However, as the amount of CEM I in the mixture increased, the geopolymer matrix was unable to provide enough water for the CEM I to hydrate, which prevented excessive CEM I from forming hydration products, weakening the workability of the matrix and eventually hindering the development of geopolymer strength.

Resistance to Sulfuric Acid Corrosion of Geopolymer Concrete Based on Different Binding Materials and Alkali Concentrations.

Geopolymer binder is expected to be an optimum alternative to Portland cement due to its excellent engineering properties of high strength, acid corrosion resistance, low permeability, good chemical resistance, and excellent fire resistance. To study the sulfuric acid corrosion resistance of geopolymer concrete (GPC) with different binding materials and concentrations of sodium hydroxide solution (NaOH), metakaolin, high-calcium fly ash, and low-calcium fly ash were chosen as binding materials of GPC for the geopolymerization process. A mixture of sodium silicate solution (Na2SiO3) and NaOH solution with different concentrations (8 M and 12 M) was selected as the alkaline activator with a ratio (Na2SiO3/NaOH) of 1.5. GPC specimens were immersed in the sulfuric acid solution with the pH value of 1 for 6 days and then naturally dried for 1 day until 98 days. The macroscopic properties of GPC were characterized by visual appearance, compressive strength, mass loss, and neutralization depth. The materials were characterized by SEM, XRD, and FTIR. The results indicated that at the immersion time of 28 d, the compressive strength of two types of fly ash-based GPC increased to some extent due to the presence of gypsum, but this phenomenon was not observed in metakaolin-based GPC. After 98 d of immersion, the residual strength of fly ash based GPC was still higher, which reached more than 25 MPa, while the metakaolin-based GPC failed. Furthermore, due to the rigid 3D networks of aluminosilicate in fly ash-based GPC, the mass of all GPC decreased slightly during the immersion period, and then tended to be stable in the later period. On the contrary, in metakaolin-based GPC, the incomplete geopolymerization led to the compressive strength being too low to meet the application of practical engineering. In addition, the compressive strength of GPC activated by 12 M NaOH was higher than the GPC activated by 8 M NaOH, which is owing to the formation of gel depended on the concentration of alkali OH ion, low NaOH concentration weakened chemical reaction, and reduced compressive strength. Additionally, according to the testing results of neutralization depth, the neutralization depth of high-calcium fly ash-based GPC activated by 12 M NaOH suffered acid attack for 98 d was only 6.9 mm, which is the minimum value. Therefore, the best performance was observed in GPC prepared with high-calcium fly ash and 12 M NaOH solution, which is attributed to gypsum crystals that block the pores of the specimen and improve the microstructure of GPC, inhibiting further corrosion of sulfuric acid.