Combined experimental and theoretical investigation of the premartensitic transition in Ni2MnGa.

Ultraviolet-photoemission (UPS) measurements and supporting specific-heat, thermal-expansion, resistivity, and magnetic-moment measurements are reported for the magnetic shape-memory alloy Ni2MnGa over the temperature range 100T(PM) is due to the Ni d minority-spin electrons. Below T(M) this peak disappears, resulting in an enhanced density of states at energies around 0.8 eV. This enhancement reflects Ni d and Mn d electronic contributions to the majority-spin density of states.

Formation of a new dynamical mode in -uranium observed by inelastic x-ray and neutron scattering.

Phonon dispersion curves were obtained from inelastic x-ray and neutron scattering measurements on alpha-uranium single crystals at temperatures from 298 to 573 K. Both measurements showed a softening and an abrupt loss of intensity in the longitudinal optic branch along [00zeta] above 450 K. Above the same temperature a new dynamical mode of comparable intensity emerges along the [01zeta] zone boundary with energy near the top of the phonon spectrum. The new mode forms without a structural transition but coincides with an anomaly in the mechanical deformation behavior. We argue that the mode is an intrinsically localized vibration and formed as a result of a strong electron-phonon interaction.

Tricritical phenomena at the gamma-->alpha transition in Ce0.9-xLaxTh0.1 alloys.

The gamma-->alpha isostructural transition in the Ce0.9-xLaxTh0.1 system is measured as a function of La alloying using specific heat, magnetic susceptibility, resistivity, thermal expansivity or striction measurements. A line of discontinuous transitions, as indicated by the change in volume, decreases exponentially from 118 K to close to 0 K with increasing La doping, and the transition changes from being first-order to continuous at a critical concentration, x(c) approximately 0.14. At the tricritical point, the coefficient of the linear T term in the specific heat gamma and the magnetic susceptibility increase rapidly near x(c) and approach large values at x=0.35 signifying that a heavy Fermi-liquid state evolves at large doping. The Wilson ratio reaches a value above 2 for a narrow range of concentrations near x(c), where the specific heat and susceptibility vary most rapidly with the doping concentration.

Large harmonic softening of the phonon density of states of uranium.

Phonon density-of-states curves were obtained from inelastic neutron scattering spectra from the three crystalline phases of uranium at temperatures from 50 to 1213 K. The alpha-phase showed an unusually large thermal softening of phonon frequencies. Analysis of the vibrational power spectrum showed that this phonon softening originates with the softening of a harmonic solid, as opposed to vibrations in anharmonic potentials. It follows that thermal excitations of electronic states are more significant thermodynamically than are the classical volume effects. For the alpha-beta and beta-gamma phase transitions, vibrational and electronic entropies were comparable.