RESUMO
In this work, the performance of anion exchange membrane (AEM) electrolysis is evaluated. A parametric study is conducted, focusing on the effects of various operating parameters on the AEM efficiency. The following parameters-potassium hydroxide (KOH electrolyte concentration (0.5-2.0 M), electrolyte flow rate (1-9 mL/min), and operating temperature (30-60 °C)-were varied to understand their relationship to AEM performance. The performance of the electrolysis unit is measured by its hydrogen production and energy efficiency using the AEM electrolysis unit. Based on the findings, the operating parameters greatly influence the performance of AEM electrolysis. The highest hydrogen production was achieved with the operational parameters of 2.0 M electrolyte concentration, 60 °C operating temperature, and 9 mL/min electrolyte flow at 2.38 V applied voltage. Hydrogen production of 61.13 mL/min was achieved with an energy consumption of 48.25 kW·h/kg and an energy efficiency of 69.64%.
RESUMO
An investigation was conducted to determine the effects of operating parameters for various electrode types on hydrogen gas production through electrolysis, as well as to evaluate the efficiency of the polymer electrolyte membrane (PEM) electrolyzer. Deionized (DI) water was fed to a single-cell PEM electrolyzer with an active area of 36 cm2. Parameters such as power supply (50-500 mA/cm2), feed water flow rate (0.5-5 mL/min), water temperature (25-80 °C), and type of anode electrocatalyst (0.5 mg/cm2 PtC [60%], 1.5 mg/cm2 IrRuOx with 1.5 mg/cm2 PtB, 3.0 mg/cm2 IrRuOx, and 3.0 mg/cm2 PtB) were varied. The effects of these parameter changes were then analyzed in terms of the polarization curve, hydrogen flowrate, power consumption, voltaic efficiency, and energy efficiency. The best electrolysis performance was observed at a DI water feed flowrate of 2 mL/min and a cell temperature of 70 °C, using a membrane electrode assembly that has a 3.0 mg/cm2 IrRuOx catalyst at the anode side. This improved performance of the PEM electrolyzer is due to the reduction in activation as well as ohmic losses. Furthermore, the energy consumption was optimal when the current density was about 200 mA/cm2, with voltaic and energy efficiencies of 85% and 67.5%, respectively. This result indicates low electrical energy consumption, which can lower the operating cost and increase the performance of PEM electrolyzers. Therefore, the optimal operating parameters are crucial to ensure the ideal performance and durability of the PEM electrolyzer as well as lower its operating costs.
RESUMO
Die configurations, filler orientations, electrical conductivity, and mechanical properties of polypropylene reinforced milled carbon fibers were studied as functions of their manufacturing processes. Series of manufacturing processes often deteriorate the material properties, hence, finding a suitable process aid is key to improving the electrical and mechanical properties of composite materials. Compared with the conventional manufacturing process, extrusion is a key process in the production of a highly conductive composite. A twin-screw extruder was used at a temperature of 230 °C and a rotational speed of 50 rpm before the compression molding process was carried out at 200 °C and 13 kPa. This research examined different die configurations, namely rod and sheet dies. The results indicated that the rod dies showed better mechanical properties and electrical conductivity with 25 MPa and 5 S/cm compared to the sheet dies. Moreover, rod dies are able to orientate to 86° and obtain longest filler length with 55 µm compared to the sheet dies. The alteration of the filler orientation in the produced material at a high shear rate further enhanced the electrical conductivity of the material.