RESUMO
A π-conjugated polymer semiconductor, PBDTTTffPI, was synthesized for use as an organic semiconductor suitable for electrohydrodynamic (EHD) jet printing technology. Bulky alkylation of the polymer gave PBDTTTffPI good solubility in several organic solvents. EHD jet printing using PBDTTTffPI ink produced direct patterns of polymer semiconductors while maintaining smooth surface morphologies and crystal structures similar to those of spin-coated PBDTTTffPI films. EHD-jet-printed PBDTTTffPI was appropriate for use as a semiconductor layer in organic field-effect transistors (OFETs) and logic gates. OFETs that used EHD-jet-printed PBDTTTffPI had better electrical characteristics than devices that used spin-coated semiconductor films. When a dielectric material (Al2O3) with a high dielectric constant was introduced, the jet-printed PBDTTTffPI operated well at low voltages. Integrated devices such as inverters, NAND gates, and NOR gates were fabricated by printing PBDTTTffPI patterns and showed good switching behaviors. Therefore, the use of printable PBDTTTffPI provides an advance toward fabrication of practical integrated arrays in next-generation devices.
RESUMO
A low-bandgap acceptor (ITIC) was added to a binary system composed of a wide-bandgap polymer (PBT-OTT) and an acceptor (PC71BM) to increase the light harvesting efficiency of the associated organic solar cells (OSCs). A ternary blend OSC with an acceptor ratio of PC71BM:ITIC = 8:2 was found to exhibit a power conversion efficiency of 8.18%, which is 18% higher than that of the binary OSC without ITIC. This improvement is mainly due to the enhanced light absorption and optimized film morphology that result from ITIC addition. Furthermore, an energy level cascade forms in the blend that ensures efficient charge transfer, and bimolecular and trap-assisted recombination is suppressed. Thus the use of ternary blend systems provides an effective strategy for the development of efficient single-junction OSCs.
RESUMO
The position at which conjugated side chains were fluorinated, the meta- or ortho-position in phenyl side chains, was varied to investigate the positional effects of fluorination on the energy levels, crystalline ordering, and photovoltaic properties of the polymers. The fluorine in the ortho-position achieved a lower HOMO energy level than that in the meta-position, but reduced the chain rigidity.