Nanostructured Ti-Zr-Pd-Si-(Nb) bulk metallic composites: Novel biocompatible materials with superior mechanical strength and elastic recovery.

The microstructure, mechanical behaviour, and biocompatibility (cell culture, morphology, and cell adhesion) of nanostructured Ti45 Zr15 Pd35- x Si5 Nbx with x = 0, 5 (at. %) alloys, synthesized by arc melting and subsequent Cu mould suction casting, in the form of rods with 3 mm in diameter, are investigated. Both Ti-Zr-Pd-Si-(Nb) materials show a multi-phase (composite-like) microstructure. The main phase is cubic ß-Ti phase (Im3m) but hexagonal α-Ti (P63/mmc), cubic TiPd (Pm3m), cubic PdZr (Fm3m), and hexagonal (Ti, Zr)5 Si3 (P63/mmc) phases are also present. Nanoindentation experiments show that the Ti45 Zr15 Pd30 Si5 Nb5 sample exhibits lower Young's modulus than Ti45 Zr15 Pd35 Si5 . Conversely, Ti45 Zr15 Pd35 Si5 is mechanically harder. Actually, both alloys exhibit larger values of hardness when compared with commercial Ti-40Nb, (HTi-Zr-Pd-Si ≈ 14 GPa, HTi-Zr-Pd-Si-Nb ≈ 10 GPa and HTi-40Nb ≈ 2.7 GPa). Concerning the biological behaviour, preliminary results of cell viability performed on several Ti-Zr-Pd-Si-(Nb) discs indicate that the number of live cells is superior to 94% in both cases. The studied Ti-Zr-Pd-Si-(Nb) bulk metallic system is thus interesting for biomedical applications because of the outstanding mechanical properties (relatively low Young's modulus combined with large hardness), together with the excellent biocompatibility.

In vitro biocompatibility assessment of Ti40Cu38Zr10Pd12 bulk metallic glass.

The use of biocompatible materials has attained an increasing importance for tissue regeneration and transplantation. The excellent mechanical and corrosion properties of Ti40Cu38Zr10Pd12 bulk metallic glass (BMG) turn it into a potential candidate for its use in orthopaedic implants. Before being considered as a biomaterial, some biological parameters must be taken into account. In this study,mouse preosteoblasts were cultured in the presence or absence of the alloy at different times (24 h, 7 and 21 days) and no differences in cell viability were detected.Moreover, cells were able to adhere to the alloy surface by establishing focal contacts, and displayed a flattened polygonal morphology. After 14 days in culture, differentiation into osteoblasts was observed. Besides, the amount of Cu ions released and their potential toxic effects were analyzed, showing that the amount of Cu released did not increase cell death. Finally, the low levels of inflammatory cytokines secreted by THP-1 differentiated macrophages exposed to the alloy suggest the absence of an immunogenic response to the alloy. In conclusion, in vitro studies indicate that the Ti40Cu38Zr10Pd12 BMG could be considered as a biomaterial to be used in orthopaedic implants.