RESUMO
The aim of this work is to study the physical-chemical, mechanical, and biocompatible properties of hydroxyapatite obtained by hydrothermal synthesis, at relatively low temperatures and high pressures, starting from natural sources (Rapana whelk shells), knowing that these properties influence the behavior of nanostructured materials in cells or tissues. Thus, hydroxyapatite nanopowders were characterized by chemical analysis, Fourier-transform infrared spectroscopy (FT-IR), dynamic light scattering (DLS), scanning electron microscopy (SEM), and X-ray diffraction (XRD). In vitro studies on osteoblast cell lines (cytotoxicity and cell proliferation), as well as preliminary mechanical tests, have been performed. The results showed that the obtained powders have a crystallite size below 50 nm and particle size less than 100 nm, demonstrating that hydrothermal synthesis led to hydroxyapatite nanocrystalline powders, with a Ca:P ratio close to the stoichiometric ratio and a controlled morphology (spherical particle aggregates). The tensile strength of HAp samples sintered at 1100 °C/90 min varies between 37.6-39.1 N/mm2. HAp samples sintered at 1300 °C/120 min provide better results for the investigated mechanical properties. The coefficient of friction has an appropriate value for biomechanical applications. The results of cell viability showed that the cytotoxic effect is low for all tested samples. Better cell proliferation is observed for osteoblasts grown on square samples.
RESUMO
In this work, the photodegradation process of atorvastatin calcium (ATC) is reported as depending on: (1) the presence and the absence of excipients in the solid state; (2) the chemical interaction of ATC with phosphate buffer (PB) having pH equal to 7 and 8; and (3) hydrolysis reaction of ATC in the presence of aqueous solution of NaOH. The novelty of this work consists in the monitoring of the ATC photodegradation by photoluminescence (PL). The exposure of ATC in solid state to UV light induces the photo-oxygenation reactions in the presence of water vapors and oxygen from air. According to the X-ray photoelectron spectroscopic studies, we demonstrate that the photo-oxygenation reaction leads to photodegradation compounds having a high share of C=O bonds compared to ATC before exposure to UV light. Both in the presence of PB and NaOH, the photodegradation process of ATC is highlighted by a significant decrease in the intensity of the PL and photoluminescence excitation (PLE) spectra. According to PLE spectra, the exposure of ATC in the presence of NaOH to UV light leads to the appearance of a new band in the spectral range 340-370 nm, this belonging to the photodegradation products. Arguments concerning the chemical compounds, that resulted in this last case, are shown by Raman scattering and FTIR spectroscopy.
RESUMO
Photodegradation of the aqueous solutions of acetylsalicylic acid, in the absence (ASA) and the presence of excipients (ASE), is demonstrated by the photoluminescence (PL). A shift of the PL bands from 342 and 338 nm to 358 and 361-397 nm for ASA and ASE in solid state and as aqueous solutions was reported. By exposure of the solution of ASA 0.3 M to UV light, a decrease in the PL band intensity was highlighted. This behavior was revealed for ASA in the presence of phosphate buffer (PB) having the pH equal to 6.4, 7, and 8 or by the interaction with NaOH 0.3 M. A different behavior was reported in the case of ASE. In the presence of PB, an increase in the intensity of the PL band of ASE simultaneously with a change of the ratio between the intensities of the bands at 361-364 and 394-397 nm was highlighted. The differences between PL spectra of ASA and ASE have their origin in the presence of salicylic acid (SAL). The interaction of ASE with NaOH induces a shift of the PL band at 405-407 nm. Arguments for the reaction of ASA with NaOH are shown by Raman scattering and FTIR spectroscopy.