RESUMO
BACKGROUND: The aim of the study was to assess the protective effect of applying potassium iodide (KI) over silver diamine fluoride (SDF) on demineralized root dentin in the case of a sustained acidogenic attack. METHODS: Forty caries-free third molars were used in the study. A diamond disc was used to separate the roots and the tooth crowns from the roots. Each root fragment was randomly distributed in one of the four study groups: C-samples were not demineralized; DD-demineralized samples; RS1-demineralized samples covered with SDF+KI (RS-Riva Star product, SDI limited, Bayswater, Australia); RS2-demineralized samples covered with SDF+KI and submersed to another acidic challenge for 3 days. SEM and EDX were used for the morphological and elemental analysis. Vickers hardness assessment was performed using a tribometer CETR UMT-2 (Bruker Corporation, Berlin, Germany). One-way ANOVA and post hoc Bonferroni tests were used for the statistical analysis with a significance level of p < 0.05. RESULTS: Morphological and elemental changes were observed on the surface of the study samples. Significant differences were observed between the recorded hardness values of groups C and DD (p = 0.005), C and RS2 (p = 0.002), DD and RS1 (p = 0.011); RS1 and RS2 (p = 0.004). CONCLUSIONS: The application of SDF and KI (Riva Star product) on root dentin caries resulted in the formation of a heterogeneous outer layer that sealed the dentin and increased the microhardness of the treated surface. In the conditions of the present study, this layer did not provide enough protection for root dentin exposed to continuous attacks.
RESUMO
The aim of the present study was to assess by atomic force microscopy (AFM) the surface roughness of a traditional glass ionomer cement- GIC (Fuji IX GP, GC Corporation, Tokyo, Japan) and a resin modified glass ionomer cement- RMGIC (Vitremer, 3M ESPE, St. Paul, MN, USA) after different immersion regimes on some acidic drinks. Sixteen cylindrical samples having the height of 5 mm and the thickness of 2 mm were obtained from each material and they were divided into two groups: Group I (Fuji IX samples) and Group II (Vitremer samples). Specimens of each group were then randomly divided into 4 subgroups: subgroup A (control)-15 samples were kept in artificial saliva and in the other three subgroups, each having 15 samples the samples were immersed in Coca-Cola (subgroup B), Cappy lemonade and mint (subgroup C) and Fuzetea (subgroup D) for 7 days (subgroups A1-D1), 14 days (subgroups A2-D2), and 21 days (subgroups A3-D3). AFM qualitative and quantitative surface evaluation (mean value of surface roughness parameter, Sa) of each sample was performed. The highest surface roughness was determined when both materials were submerged 14 days in acidic drinks. Traditional GIC was more affected by acidic environment when comparing to RMGIC.
RESUMO
The aim of this in vitro study was to evaluate the effect of hydrochloric acid associated with the abrasive effect of toothbrushing on the surface condition of three flowable composite resins used for direct restoration. Seventy samples of each composite resin: Grandio Flow (VOCO, Germany)-group A, Filtek Ultimate Flow (3M-ESPE, MN, USA)-group B, G-aenial Flo X (GC Europe)-group C were prepared, submersed in hydrochloric acid 30% for 60 min and then submitted to simulated toothbrushing procedure using 5000 cycles with toothbrushes with medium and hard bristles, immediately after the chemical attack, after 30 min or without any chemical attack. The sample's surface roughness was analyzed using a noncontact profilometer (Dektak XT, Bruker, USA). ANOVA and post hoc Bonferroni tests, with a p < 0.05, were used to analyze the values. Hydrochloric acid action for 60 min and six months of toothbrushing using toothbrushes having medium hardness or firm bristles affects the surface roughness of tested flowable composite resins. Toothbrushing with firm bristles immediately after acidic challenge determines increased surface roughness for two of the three flowable composite resins (Grandio Flow and Filtek Ultimate Flow). Toothbrushing with medium or firm bristles thirty minutes after the acidic aggression determine no effect on surface condition of flowable composite resins.