RESUMO
We observed a remarkable improvement of domain wall (DW) mobility, DW velocity, giant magnetoimpedance (GMI) effect and magnetic softening at appropriate stress-annealing conditions. Beneficial effect of stress-annealing on GMI effect and DW dynamics is associated with the induced transverse magnetic anisotropy. An improvement of the circumferential permeability in the nearly surface area of metallic nucleus is evidenced from observed magnetic softening and remarkable GMI effect rising. We assumed that the outer domain shell with transverse magnetic anisotropy associated to stress-annealing induced transverse magnetic anisotropy affects the travelling DW in a similar way as application of transversal bias magnetic field allowing enhancement the DW velocity. Observed decreasing of the half-width of the EMF peak in stress-annealed microwires can be associated to the decreasing of the characteristic DW width. Consequently, stress annealing enabled us to design the magnetic anisotropy distribution beneficial for optimization of either GMI effect or DW dynamics.
RESUMO
There is a pressing need for improving of the high-frequency magneto-impedance effect of cost-effective soft magnetic materials for use in high-performance sensing devices. The impact of the stress-annealing on magnetic properties and high frequency impedance of Fe-rich glass-coated microwires was studied. Hysteresis loops of Fe-rich microwires have been considerably affected by stress- annealing. In stress-annealed Fe- rich microwire we obtained drastic decreasing of coercivity and change of character of hysteresis loop from rectangular to linear. By controlling stress-annealing conditions (temperature and time) we achieved drastic increasing (by order of magnitude) of giant magnetoimpedance ratio. Coercivity, remanent magnetization, diagonal and of-diagonal magnetoimpedance effect of Fe-rich microwires can be tuned by stress-annealing conditions: annealing temperature and time. Observed experimental results are discussed considering relaxation of internal stresses, compressive "back-stresses" arising after stress annealing and topological short range ordering.
RESUMO
We have studied magnetic and structural properties of the Heusler-type Ni-Mn-Ga glass-coated microwires prepared by Tailor-Ulitovsky technique. As-prepared sample presents magnetoresistance effect and considerable dependence of magnetization curves (particularly magnetization values) on magnetic field attributed to the magnetic and atomic disorder. Annealing strongly affects the temperature dependence of magnetization and Curie temperature of microwires. After annealing of the microwires at 973 K, the Curie temperature was enhanced to about 280 K which is beneficial for the magnetic solid state refrigeration. The observed hysteretic anomalies on the temperature dependences of resistance and magnetization in the as-prepared and annealed samples are produced by the martensitic transformation. The magnetoresistance and magnetocaloric effects have been investigated to illustrate a potential technological capability of studied microwires.
RESUMO
We report on studies of domain wall propagation of magnetically-bistable Fe-Co-rich microwires paying attention on the effect of applied and internal stresses. We measured magnetic domain propagation in various magnetic Fe-Co-rich amorphous microwires with metallic nucleus diameters (from 2.8 microm to 18 microm) using Sixtus Tonks-like experiments. We found that application of applied stresses and increasing of internal stresses result in decreasing of domain wall (DW) velocity. We assume that in order to achieve higher DW propagation velocity at the same magnetic field and enhanced DW mobility, special attention should be paid to the decrease of magnetoelastic energy.