Electrochemical CO2 reduction over nanoparticles derived from an oxidized Cu-Ni intermetallic alloy.

Oxide-derived Cu-Ni (3-32 at%-Ni) alloy nanoparticles with a size of 10 nm enhance selectivity for ethylene and ethanol formation over oxide-derived Cu nanoparticles by electrochemical CO2 reduction. X-ray absorption spectroscopy measurements suggest that Ni (generally recognized as an element to avoid) is in a mixed phase of oxidized and metallic states.

Synthesis of Cu Nanoparticles Using Copper Carbonate as Cu Source Toward Versatile Applications.

Cu nanoparticles (NPs) coated with polyvinylpyrrolidone (PVP) were fabricated by polyol method using copper carbonate as a raw material. To increase the reaction temperature, glycol multimers such as diethylene glycol, triethylene glycol, or tetraethylene glycol were examined as a solvent. With increasing degree of multimerization, average diameter of Cu NPs decreased. The synthesis of Cu NPs was further investigated by changing reaction temperature, the amount and molecular weight of PVP in triethylene glycol as a solvent. Average diameter and standard deviation of Cu NPs were found to be highly dependent on those factors. As a result, fine Cu NPs ranging from 28 to 67 nm in average size with narrow size distribution (standard deviation: 16-28%) were obtained. The obtained Cu NPs were applied to a nanofluid, which showed higher thermal conductivity than the theoretical value. The antibacterial activity of Cu NPs was also demonstrated, and found to have strong antibacterial activity.

Effect of Particle Size on the Magnetic Properties of Ni Nanoparticles Synthesized with Trioctylphosphine as the Capping Agent.

Magnetic cores of passive components are required to have low hysteresis loss, which is dependent on the coercive force. Since it is well known that the coercive force becomes zero at the superparamagnetic regime below a certain critical size, we attempted to synthesize Ni nanoparticles in a size-controlled fashion and investigated the effect of particle size on the magnetic properties. Ni nanoparticles were synthesized by the reduction of Ni acetylacetonate in oleylamine at 220 °C with trioctylphosphine (TOP) as the capping agent. An increase in the TOP/Ni ratio resulted in the size decrease. We succeeded in synthesizing superparamagnetic Ni nanoparticles with almost zero coercive force at particle size below 20 nm by the TOP/Ni ratio of 0.8. However, the saturation magnetization values became smaller with decrease in the size. The saturation magnetizations of the Ni nanoparticles without capping layers were calculated based on the assumption that the interior atoms of the nanoparticles were magnetic, whereas the surface-oxidized atoms were non-magnetic. The measured and calculated saturation magnetization values decreased in approximately the same fashion as the TOP/Ni ratio increased, indicating that the decrease could be mainly attributed to increases in the amounts of capping layer and oxidized surface atoms.

Improving Powder Magnetic Core Properties via Application of Thin, Insulating Silica-Nanosheet Layers on Iron Powder Particles.

A thin, insulating layer with high electrical resistivity is vital to achieving high performance of powder magnetic cores. Using layer-by-layer deposition of silica nanosheets or colloidal silica over insulating layers composed of strontium phosphate and boron oxide, we succeeded in fabricating insulating layers with high electrical resistivity on iron powder particles, which were subsequently used to prepare toroidal cores. The compact density of these cores decreased after coating with colloidal silica due to the substantial increase in the volume, causing the magnetic flux density to deteriorate. Coating with silica nanosheets, on the other hand, resulted in a higher electrical resistivity and a good balance between high magnetic flux density and low iron loss due to the thinner silica layers. Transmission electron microscopy images showed that the thickness of the colloidal silica coating was about 700 nm, while that of the silica nanosheet coating was 30 nm. There was one drawback to using silica nanosheets, namely a deterioration in the core mechanical strength. Nevertheless, the silica nanosheet coating resulted in nanoscale-thick silica layers that are favorable for enhancing the electrical resistivity.