Hopping and band mobilities of pentacene, rubrene, and 2,7-dioctyl[1]benzothieno[3,2-b][1]benzothiophene (C8-BTBT) from first principle calculations.

Hopping and band mobilities of holes in organic semiconductors at room temperature were estimated from first principle calculations. Relaxation times of charge carriers were evaluated using the acoustic deformation potential model. It is found that van der Waals interactions play an important role in determining accurate relaxation times. The hopping mobilities of pentacene, rubrene, and 2,7-dioctyl[1]benzothieno[3,2-b][1]benzothiophene (C8-BTBT) in bulk single crystalline structures were found to be smaller than 4 cm(2)∕Vs, whereas the band mobilities were estimated between 36 and 58 cm(2)∕Vs, which are close to the maximum reported experimental values. This strongly suggests that band conductivity is dominant in these materials even at room temperature.

Microstructural study of the polymorphic transformation in pentacene thin films.

We have observed, by high-resolution cross-sectional transmission electron microscopy, the first direct evidence of polymorphic transformation in pentacene thin films deposited on silicon oxide substrates. Polymorphic transformation from the thin-film phase to the bulk phase occurred preferentially near polycrystalline grain boundaries, which exhibit concave surfaces. This process is thought to be driven by compressive stress caused by the grain boundaries. In addition to this stress, lattice mismatch between the two phases also results in structural defect formation.