RESUMO
The utilization of polyols derived from renewable sources presents an opportunity to enhance the sustainability of rigid polyurethane (PUR) foams, thereby contributing to the advancement of a circular bioeconomy. This study explores the development of PUR rigid foams exclusively using polyols sourced from second-generation renewable biomass feedstocks, specifically depolymerized birch bark suberin (suberinic acids) and tall oil fatty acids. The polyols achieved a total renewable material content as high as 74%, with a suberinic acid content of 37%. Response surface modeling was employed to determine the optimal bio-polyol, blowing agents, and catalyst content, hence, optimizing the bio-based foam formulations. In addition, response surface modeling was applied to rigid PUR foam formulations based on commercially available petroleum-based polyols for comparison. The results, including apparent density (~40-44 kg/m3), closed cell content (~95%), compression strength (>0.2 MPa, parallel to the foaming direction), and thermal conductivity (~0.019 W/(m·K)), demonstrated that the suberinic acids-based rigid PUR foam exhibited competitive qualities in comparison to petroleum-based polyols. Remarkably, the bio-based rigid PUR foams comprised up to 29% renewable materials. These findings highlight the potential of suberinic acid-tall oil polyols as effective candidates for developing rigid PUR foams, offering promising solutions for sustainable insulation applications.
RESUMO
Developing polyols from biomass sources contributes to a more circular economy by replacing petroleum-based polyols in the vast production of polyurethanes (PUR). One such potential biomass source could be leftover birch bark from which suberinic acids (SA) can be obtained. The purpose of this study was to identify the best synthesis routes for novel SA-based polyols, obtain rigid PUR foams, and evaluate their competitiveness and potential suitability as thermal insulation material. Novel polyols were synthesized from depolymerized SA by esterification with various functionality and molecular weight alcohols in several molar ratios. The moisture content, hydroxyl and acid values, and apparent viscosity were tested. Free-rise rigid PUR foams from the most suitable SA-based polyol and tall oil-based polyol were successfully prepared, reaching ~20 wt.% total renewable material content in the foam. The obtained rigid PUR foams' morphological, mechanical, and thermal properties were investigated and compared to present foam materials, including commercial foams. The apparent density (~33 kg/m3), as well as the closed cell content (~94%), compression strength (0.25 MPa, parallel to the foaming direction), and thermal conductivity (~0.019 W/(m·K)), approved the competitiveness and potential ability of SA-based rigid PUR foam production as thermal insulation material.
RESUMO
Developing polyols derived from natural sources and recycling materials attracts great interest for use in replacing petroleum-based polyols in polyurethane production. In this study, rigid polyurethane (PUR) foams with various isocyanate indices were obtained from polyols based on rapeseed oil and polyethylene terephthalate (RO/PET). The various properties of the prepared PUR foams were investigated, and the effect of the isocyanate index was evaluated. The closed-cell content and water absorption were not impacted by the change of the isocyanate index. The most significant effect of increasing the isocyanate index was on the dimensional stability of the resulting foams. This is due to the increased crosslink density, as evidenced by the increased formation of isocyanurate and increase of the glass transition temperature. Additionally, the influence on compression strength, modulus, and long-term thermal conductivity were evaluated and compared with reference PUR foams from commercially available polyols. Rigid PUR foams from RO/PET polyol were found to be competitive with reference materials and could be used as thermal insulation material.