How light sources and distance of the light tip influence water sorption, solubility, and biaxial flexural strength of a composite resin.

This study evaluated the water sorption (WS), solubility (SL), and biaxial flexural strength (BFS) of a resin composite based on different polymerization units, storage permeants (distilled water and 75% ethanol), and distances between the light's tip and the composite resin. Using a stainless steel mold, 80 specimens were made and separated in two independent groups, according to the duration of storage (7 days or 60 days). The specimens were photocured using either a QTH or LED light (both used at 600 mW/cm2 for 40 seconds), with the light's tip guide either 0 mm or 2 mm from the surface of the resin. In general, the 75% ethanol produced higher WS and SL values but lower BFS values compared to water. Both distances influenced the WS and SL values, especially when 75% ethanol was used (p < 0.05), although neither distance affected BFS values (p > 0.05). For nearly all groups, the WS, SL, and BFS in different solvents and at different distances for photocuring of the tested resin were not affected by the curing light used.

Influence of pulse-delay curing on sorption and solubility of a composite resin

The purpose of this study was to evaluate the sorption and solubility of a composite resin (TPH³; Dentsply) cured with halogen light due to different storage media and curing modes. The methodology was based on the ISO 4049 standard. Two independent groups were established according to the storage time (7 days-G1; 60 days-G2). A stainless steel mould (2 mm x 8 mm Ø) was used. The selected curing modes were: I (Conventional - C): 40s - 600 mW/cm²; II (Pulse I - PD): 3 s - 200 mW/cm² + 2 min (delay) + 39 s - 600 mW/cm²; III (Pulse II): 10 s - 200 mW/cm² + 2 min (delay) + 37 s - 600 mW/cm²; IV (Pulse III): 3 s- 600 mW/cm² + 2 min (delay) + 37 s -600 mW/cm². The media used were: distilled water, 75 percent ethanol and 100 percent chlorophorm. Five repetitions were made for each group. The specimens were placed in a desiccator at 37ºC for 24 h and, after that, at 23ºC for 1 h to be weighed until a constant mass (m1) was obtained. The discs were immersed separately into the 3 media for 7 days (G1) and 60 days (G2), and thereafter reweighed (m2). The reconditioning in the desiccator was done until a constant mass (m3) was obtained. Sorption and solubility were calculated and the data of G1 and the sorption data of G2 were subjected to two-way ANOVA and Tukey's tests (p=0.05). The solubility data of G2 were analyzed by Kruskal-Wallis test (p=0.05). For G1 and G2, no statistically significant differences were found in sorption among curing techniques (p>0.05). The solubility values were negative, which means that there was mass gain. Regarding the storage media, in G2 chlorophorm had the highest sorption values. It may be concluded that the curing modes (C and PD I, II and III) did not affect the sorption of the tested composite resin. However, different storage media influenced sorption behavior. The solubility test demonstrated negative data, masking the real solubility.

Influence of pulse-delay curing on sorption and solubility of a composite resin.

The purpose of this study was to evaluate the sorption and solubility of a composite resin (TPH(3); Dentsply) cured with halogen light due to different storage media and curing modes. The methodology was based on the ISO 4049 standard. Two independent groups were established according to the storage time (7 days-G1; 60 days-G2). A stainless steel mould (2 mm x 8 mm Ø) was used. The selected curing modes were: I (Conventional - C): 40s - 600 mW/cm(2); II (Pulse I - PD): 3 s - 200 mW/cm(2) + 2 min (delay) + 39 s - 600 mW/cm(2); III (Pulse II): 10 s - 200 mW/cm(2) + 2 min (delay) + 37 s - 600 mW/cm(2); IV (Pulse III): 3 s- 600 mW/cm(2) + 2 min (delay) + 37 s -600 mW/cm(2). The media used were: distilled water, 75% ethanol and 100% chlorophorm. Five repetitions were made for each group. The specimens were placed in a desiccator at 37 masculineC for 24 h and, after that, at 23 masculineC for 1 h to be weighed until a constant mass (m1) was obtained. The discs were immersed separately into the 3 media for 7 days (G1) and 60 days (G2), and thereafter reweighed (m2). The reconditioning in the desiccator was done until a constant mass (m3) was obtained. Sorption and solubility were calculated and the data of G1 and the sorption data of G2 were subjected to two-way ANOVA and Tukey's tests (p=0.05). The solubility data of G2 were analyzed by Kruskal-Wallis test (p=0.05). For G1 and G2, no statistically significant differences were found in sorption among curing techniques (p>0.05). The solubility values were negative, which means that there was mass gain. Regarding the storage media, in G2 chlorophorm had the highest sorption values. It may be concluded that the curing modes (C and PD I, II and III) did not affect the sorption of the tested composite resin. However, different storage media influenced sorption behavior. The solubility test demonstrated negative data, masking the real solubility.