RESUMO
This study explores the enhancement of electrical conductivity in polymer composites by incorporating carbon nanotubes (CNTs) into a co-continuous poly(lactic acid)/low-density polyethylene (PLA/LDPE) blend, creating a double percolation structure. Theoretical thermodynamic predictions indicate that CNTs preferentially localize in the LDPE phase. The percolation threshold of CNTs in the PLA/LDPE/CNT composites was 0.208 vol% (5.56 wt%), an 80% reduction compared to the LDPE/CNT composite, due to the double percolation structure. This thermodynamic migration of CNTs from PLA to LDPE significantly enhanced conductivity, achieving a 13.8-fold increase at a 7.5 wt% CNT loading compared to the LDPE/CNT composite. The localization of CNTs was driven by thermodynamic, kinetic, and rheological factors, with viscosity differences between PLA and LDPE causing dense CNT aggregation in LDPE. Initial contact of CNTs with PLA reduced aggregation, allowing PLA to infiltrate CNT aggregates during melt-mixing, which influenced the final morphology and electrical conductivity. These findings provide new insights into the fabrication of conductive polymer composites for force sensor applications.
RESUMO
The crosslinked poly(acrylic acid-co-acrylamide)-grafted deproteinized natural rubber/silica ((PAA-co-PAM)-DPNR/silica) composites were prepared and applied as coating materials for fertilizer in this work. The crosslinked (PAA-co-PAM)-DPNR was prepared via emulsion graft copolymerization in the presence of MBA as a crosslinking agent. The modified DPNR was mixed with various contents of silica (10 to 30 phr) to form the composites. The existence of crosslinked (PAA-co-PAM) after modification provided a water adsorption ability to DPNR. The swelling degree values of composites were found in the range of 2217.3 ± 182.0 to 8132.3 ± 483.8%. The addition of silica in the composites resulted in an improvement in mechanical properties. The crosslinked (PAA-co-PAM)-DPNR with 20 phr of silica increased its compressive strength and compressive modulus by 1.61 and 1.55 times compared to the unloaded silica sample, respectively. There was no breakage of samples after 80% compression strain. Potassium nitrate, a model fertilizer, was loaded into chitosan beads with a loading percentage of 40.55 ± 1.03% and then coated with the modified natural rubber/silica composites. The crosslinked (PAA-co-PAM)-DPNR/silica composites as the outer layers had the ability of holding water in their structure and retarded the release of fertilizer. These composites could be promising materials for controlled release and water retention that would have potential for agricultural application.
RESUMO
Bamboo leaf fiber (BLF) was incorporated into an eco-friendly foam cushion made from natural rubber latex (NRL) to enhance the biodegradation rate. The objective of this work was to investigate the effects of BLF content on the foam structure, mechanical properties, cushion performance, and biodegradability. The NRL foam cushion nets with and without BLF were prepared using the Dunlop method along with microwave-assisted vulcanization. BLF (90-106 µm in length) at various loadings (0.00, 2.50, 5.00, 7.50, and 10.00 phr) were introduced to the latex compounds before gelling and vulcanizing steps. Scanning electron microscopy (SEM) showed that the BLF in a NRL foam caused an increase in cell size and a decrease in the number of cells. The changes in the cell structure and number of cells resulted in increases in the bulk density, hardness, compression set, compressive strength, and cushion coefficient. A soil burial test of 24 weeks revealed faster weight loss of 1.8 times when the BLF content was 10.00 phr as compared to the NRL foam without BLF. The findings of this work suggest the possibility of developing an eco-friendly cushion with a faster degradation rate while maintaining cushion performance, which could be a better alternative for sustainable packaging in the future.
RESUMO
This work aims to enhance the polarity of natural rubber by grafting copolymers onto deproteinized natural rubber (DPNR) to improve its compatibility with silica. Poly(acrylic acid-co-acrylamide)-grafted DPNR ((PAA-co-PAM)-DPNR) was successfully prepared by graft copolymerization with acrylic acid and acrylamide in the latex stage, as confirmed by FTIR. The optimum conditions to obtain the highest conversion, grafting efficiency, and grafting percentage were a reaction time of 360 min, a reaction temperature of 50 °C, and an initiator concentration of 1.0 phr. The monomer conversion, grafting efficiency, and grafting percentage were 91.9-94.1, 20.8-38.9, and 2.1-9.9%, respectively, depending on the monomer content. It was shown that the polarity of the natural rubber increased after grafting. The (PAA-co-PAM)-DPNR was then mixed with silica to prepare DPNR/silica composites. The presence of the (PAA-co-PAM)-DPNR and silica in the composites was found to improve the mechanical properties of the DPNR. The incorporation of 10 phr of silica into the (PAA-co-PAM)-DPNR with 10 phr monomer increased its tensile strength by 1.55 times when compared to 10 phr of silica loaded into the DPNR. The silica-filled (PAA-co-PAM)-DPNR provided s higher storage modulus, higher Tg, and a lower tan δ peak, indicating stronger modified DPNR/silica interactions and greater thermal stability when compared to silica-filled DPNR.