Effect of Forming and Heat Treatment Parameters on the Mechanical Properties of Medium Manganese Steel with 5% Mn.

Medium manganese steels fall into the category of modern third-generation high-strength steels. Thanks to their alloying, they use a number of strengthening mechanisms, such as the TRIP and TWIP effects, to achieve their mechanical properties. The excellent combination of strength and ductility also makes them suitable for safety components in car shells, such as side reinforcements. Medium manganese steel with 0.2% C, 5% Mn, and 3% Al was used for the experimental program. Sheets with a thickness of 1.8 mm without surface treatment were formed in a press hardening tool. Side reinforcements require various mechanical properties in different parts. The change in mechanical properties was tested on the produced profiles. The changes in the tested regions were produced by local heating to an intercritical region. These results were compared with classically annealed specimens in a furnace. In the case of tool hardening, strength limits were over 1450 MPa with a ductility of about 15%.

Study of Transition Areas in Press-Hardened Steels in a Combined Tool for Hot and Cold Forming.

Press-hardening, also known as hot stamping, is a manufacturing process for producing car body parts that must meet the high demands of their mechanical properties and safety parameters. Moreover, these components often require different mechanical properties in different parts of the component. This work presents the press-hardening process in a special combined tool where one half of the tool is heated and the other half is cooled. The cooled part has been 3D printed due to the complexity of the internal cooling channels. The aim of this work is to investigate the variation of the microstructures in the sheet metal and the mechanical properties in relation to the cooling process in the tool and to determine the transition area where these properties cross over. Two steels were chosen for the experiment. The most commonly used steel 22MnB5, and an experimental high-strength steel with 0.2% C alloyed with manganese and aluminium. A temperature of 425 °C was set in the heated part of the tool, and different holding times in the tool were tested. In the heated part of the tool, a bainitic structure with a fraction of ferrite and retained austenite was formed, while in the quenched part of the tool, a martensitic transformation was promoted due to rapid cooling. In addition to microscopic analyses, mechanical tests and hardness measurements were also performed.

Production of Hybrid Joints by Selective Laser Melting of Maraging Tool Steel 1.2709 on Conventionally Produced Parts of the Same Steel.

Joining additively manufactured (AM) complex shaped parts to larger conventionally produced parts can lead to innovative product designs. Another alternative is direct deposition on a conventional semi-product. Therefore, similar joints of maraging tool steel 1.2709 were produced by AM deposition of powder of this steel on a bulk conventionally manufactured steel part. The resulting hybrid parts were solution annealed and precipitation hardened. Solution annealing at 820 °C for 20 min was followed by furnace cooling. Precipitation hardening was performed at 490 °C for 6 h. The mechanical properties of the samples were characterised using tensile testing and hardness measurement across the joint. Metallographic analysis was also carried out. The tensile properties of the AM and conventionally produced steel after equivalent heat treatments were also determined as the reference values. The mechanical properties of the hybrid parts are close to the properties of both steels. The hybrid parts in the as-built condition had a tensile strength of 1029 MPa and a total elongation of 14%. Solution annealing did not change these properties significantly, except for yield strength, which decreased by approximately 150 MPa. After precipitation annealing, the strength was higher, 2011 MPa, and total elongation dropped to 5%.