Mechanism of One-Step Hydrothermally Synthesized Titanate Catalysts for Ozonation.

A titanate nanotube catalyst for ozonation was synthesized with a simple one-step NaOH hydrothermal treatment without energy-consuming calcination. The synthesized titania catalysts were characterized by X-ray diffraction (XRD), Raman, porosimetry analysis, high-resolution transmission electron microscopy (HR-TEM), Fourier transformed infrared (FTIR), and electron paramagnetic resonance (EPR) analysis. The catalyst treated with a higher concentration of NaOH was found to be more catalytically active for phenol removal due to its higher titanate content that would facilitate more OH groups on its surface. Furthermore, the main active oxidizing species of the catalytic ozonation process were recognized as singlet oxygen and superoxide radical, while the hydroxyl radical may only play a minor role. This work provides further support for the correlation between the properties of titania and catalytic performance, which is significant for understanding the mechanism of catalytic ozonation with titania-based materials.

A Self-Supported CuO/Cu Nanowire Electrode as Highly Efficient Sensor for COD Measurement.

A self-supported CuO/Cu nanowire electrode (CuO/CuNWE), which was prepared by annealing Cu nanowires to form a porous Cu nanowire electrode (CuNWE) and then anodizing the as-prepared CuNWE in alkaline medium to generate Cu(OH)2 nanowires followed by calcination, was employed for chemical oxygen demand (COD) determination using cyclic voltammetry (CV). The structure and electrochemical behavior of the CuO/CuNWE were investigated by scanning electron microscopy, X-ray diffraction, and CV. The results indicated that the as-synthesized CuO/CuNWE, in which CuO nanowires with a length of several micrometers and a diameter of 100 to 300 nm could be found, was stable in alkaline medium and more electrocatalytically active for oxidizing a wide range of organic compounds in comparison with the CuNWE. Under optimized alkaline concentration and scan rate, the CuO/CuNWE exhibited a good performance for COD measurement, with a linear range of 5 to 1153 mg L-1, a sensitivity of 2.46× 10-2 mA /(mg L-1), and a detection limit of about 2.3 mg L-1. In addition, an excellent correlation was observed in COD values obtained by our method and the classic dichromate method (r = 0.9995, p < 0.01, n = 11). Finally, our method was successfully used to measure the COD values in real water samples, showing great potential for practical application in water pollution control.