Stable, predictable and training-free operation of superconducting Bi-2212 Rutherford cable racetrack coils at the wire current density of 1000 A/mm2.

High-temperature superconductors (HTS) could enable high-field magnets stronger than is possible with Nb-Ti and Nb3Sn, but two challenges have so far been the low engineering critical current density JE, especially in high-current cables, and the danger of quenches. Most HTS magnets made so far have been made out of REBCO coated conductor. Here we demonstrate stable, reliable and training-quench-free performance of Bi-2212 racetrack coils wound with a Rutherford cable fabricated from wires made with a new precursor powder. These round multifilamentary wires exhibited a record JE up to 950 A/mm2 at 30 T at 4.2 K. These coils carried up to 8.6 kA while generating 3.5 T at 4.2 K at a JE of 1020 A/mm2. Different from the unpredictable training performance of Nb-Ti and Nb3Sn magnets, these Bi-2212 magnets showed no training quenches and entered the flux flow state in a stable manner before thermal runaway and quench occurred. Also different from Nb-Ti, Nb3Sn, and REBCO magnets for which localized thermal runaways occur at unpredictable locations, the quenches of Bi-2212 magnets consistently occurred in the high field regions over a long conductor length. These characteristics make quench detection simple, enabling safe protection, and suggest a new paradigm of constructing quench-predictable superconducting magnets from Bi-2212.

Adenovirus-mediated herpes simplex virus thymidine kinase gene therapy combined with ganciclovir induces hepatoma cell apoptosis.

The present study aimed to examine the apoptotic effects of adenovirus (ADV)-mediated herpes simplex virus thymidine kinase (ADV-TK) combined with ganciclovir (GCV) in tissues obtained from patients with hepatocellular carcinoma in order to provide a theoretical basis for the development of this gene therapy program. Apoptosis detection was conducted using the terminal deoxynucleotidyl-transferase-mediated dUTP nick end labelling assay and the apoptosis index was compared between the experimental; and control groups. Furthermore, the protein expression levels of caspase-3, B-cell lymphoma-2 (Bcl-2), Bcl-2-assoicated protein X (Bax) and nuclear factor (NF)-κB were examined in pathological specimens using immunohistochemical staining. The Bax/Bcl-2 ratio and the release of cytochrome c were examined using western blot analysis. Results indicated that combined ADV-TK and GCV treatment significantly increased the number of apoptotic cells compared with the control group (P<0.05). Immunohistological analysis revealed that ADV-TK and GCV treatment significantly increased the number of caspase-3-positive cells, reduced the Bax/Bcl-2 ratio and NF-κB expression levels and promoted the release of cytochrome c compared with the control group (P<0.01). In conclusion, the present results suggest that combined ADV-TK and GCV treatment exerts its effect through the apoptotic signaling pathway.

Control of Epitaxial BaFe2As2 Atomic Configurations with Substrate Surface Terminations.

Atomic layer controlled growth of epitaxial thin films of unconventional superconductors opens the opportunity to discover novel high temperature superconductors. For instance, the interfacial atomic configurations may play an important role in superconducting behavior of monolayer FeSe on SrTiO3 and other Fe-based superconducting thin films. Here, we demonstrate a selective control of the atomic configurations in Co-doped BaFe2As2 epitaxial thin films and its strong influence on superconducting transition temperatures by manipulating surface termination of (001) SrTiO3 substrates. In a combination of first-principles calculations and high-resolution scanning transmission electron microscopy imaging, we show that Co-doped BaFe2As2 on TiO2-terminated SrTiO3 is a tetragonal structure with an atomically sharp interface and with an initial Ba layer. In contrast, Co-doped BaFe2As2 on SrO-terminated SrTiO3 has a monoclinic distortion and a BaFeO3- x initial layer. Furthermore, the superconducting transition temperature of Co-doped BaFe2As2 ultrathin films on TiO2-terminated SrTiO3 is significantly higher than that on SrO-terminated SrTiO3, which we attribute to shaper interfaces with no lattice distortions. This study allows the design of the interfacial atomic configurations and the effects of the interface on superconductivity in Fe-based superconductors.

Origin of the emergence of higher T c than bulk in iron chalcogenide thin films.

Fabrication of epitaxial FeSexTe1-x thin films using pulsed laser deposition (PLD) enables improving their superconducting transition temperature (T c) by more than ~40% than their bulk T c. Intriguingly, T c enhancement in FeSexTe1-x thin films has been observed on various substrates and with different Se content, x. To date, various mechanisms for T c enhancement have been reported, but they remain controversial in universally explaining the T c improvement in the FeSexTe1-x films. In this report, we demonstrate that the controversies over the mechanism of T c enhancement are due to the abnormal changes in the chalcogen ratio (Se:Te) during the film growth and that the previously reported T c enhancement in FeSe0.5Te0.5 thin films is caused by a remarkable increase of Se content. Although our FeSexTe1-x thin films were fabricated via PLD using a Fe0.94Se0.45Te0.55 target, the precisely measured composition indicates a Se-rich FeSexTe1-x (0.6 < x < 0.8) as ascertained through accurate compositional analysis by both wavelength dispersive spectroscopy (WDS) and Rutherford backscattering spectrometry (RBS). We suggest that the origin of the abnormal composition change is the difference in the thermodynamic properties of ternary FeSexTe1-x, based on first principle calculations.

Effects of filament size on critical current density in overpressure processed Bi-2212 round wire.

Bi2Sr2CaCu2Ox (Bi-2212) conductor is the only high temperature superconductor manufactured as a round wire and is a very promising conductor for very high field applications. One of the key design parameters of Bi-2212 wire is its filament size, which has been previously reported to affect the critical current density (Jc ) and ac losses. Work with 1 bar heat treatment showed that the optimal filament diameter was about 15 µm but it was not well understood at that time that gas bubbles were the main current limiting mechanism. Here we investigated a recent Bi-2212 wire with a 121×18 filament architecture with varying wire diameter (1.0 to 1.5 mm) using 50 bar overpressure processing. This wire is part of a 1.2 km piece length of 1.0 mm diameter made by Oxford Superconducting Technology. We found that Jc is independent of the filament size in the range from 9 to 14 µm, although the n value increased with increasing filament size. A new record Jc (4.2 K, 15 T) of 4200 A/mm2 and JE (4.2 K, 15 T) of 830 A/mm2 were achieved.

Development of a Persistent Superconducting Joint between Bi-2212/Ag-alloy Multifilamentary Round Wires.

Superconducting joints are one of the key components needed to make Ag-alloy clad Bi2Sr2CaCu2O8+x (Bi-2212) superconducting round wire (RW) successful for high-field, high-homogeneity magnet applications, especially for nuclear magnetic resonance (NMR) magnets in which persistent current mode (PCM) operation is highly desired. In this study, a procedure for fabricating superconducting joints between Bi-2212 round wires during coil reaction was developed. Melting temperatures of Bi-2212 powder with different amounts of Ag addition were investigated by differential thermal analysis (DTA) so as to provide information for selecting the proper joint matrix. Test joints of 1.3 mm dia. wires heat treated in 1 bar flowing oxygen using the typical partial melt Bi-2212 heat treatment (HT) had transport critical currents I c of ~900 A at 4.2 K and self-field, decreasing to ~480 A at 14 T evaluated at 0.1 µV/cm at 4.2 K. Compared to the I c of the open-ended short conductor samples with identical 1 bar HT, the I c values of the superconducting joint are ~20% smaller than that of conductor samples measured in parallel field but ~20% larger than conductor samples measured in perpendicular field. Microstructures examined by scanning electron microscopy (SEM) clearly showed the formation of a superconducting Bi-2212 interface between the two Bi-2212 round wires. Furthermore, a Bi-2212 RW closed-loop solenoid with a superconducting joint heat treated in 1 bar flowing oxygen showed an estimated joint resistance below 5×10-12 Ω based on its field decay rate. This value is sufficiently low to demonstrate the potential for persistent operation of large inductance Bi-2212 coils.

Origin of the dynamics of the spin state in undoped BaFe2As2: Mössbauer studies.

Fe-As based superconductors provide a good system for understanding the relationship between magnetism and superconductivity. Considerable efforts have been expended in understanding the magnetic behavior of the parent compound, BaFe2As2. However, it had not been realized that traces of adsorbed O2 by the material bring about drastic changes in its magnetic behavior. O2 is known to trap electrons, forming O2(-). Guided by this discovery, we observe in the absence of O2 a dynamic transition between intermediate and low spin states of Fe and hysteresis effects, and in the presence of O2 trapping of the magnetic state. These observations are likely to have a bearing on the role of magnetism in superconductivity.

Mössbauer studies of the superconducting cobalt/nickel-doped BaFe2As2. Whither go the injected electron(s)?

Mössbauer studies of cobalt- and nickel-doped BaFe(2)As(2) show that the s-electron density at the (57)Fe nuclei, as measured by the isomer shift, is the same as that for the parent BaFe(2)As(2). Apparently, the electron population of the d shell, which shields the s-electron density at the nuclei, remains unchanged. We invoke the involvement of p-orbital hybridization with the d orbital in Fe-As bonding. Furthermore, the shrinkage of the lattice on substitution enhances the As-As sp hybridization, providing a path for the migration of additional electrons. The proposed mechanism is consistent with Hall coefficient and thermoelectric effect measurements.