RESUMO
Surfaces of iron oxide of ferrimagnetic magnetite (Fe3O4) nanoparticles (MNPs) prepared by Massart's method and their functionalized form (f-MNPs) with succinic acid, L-arginine, oxalic acid, citric acid, and glutamic acid were studied by dynamic light scattering (DLS), Fourier transform infrared spectroscopy (FTIR-S), UV-vis, thermogravimetric analysis (TGA)/differential scanning calorimetry (DSC), X-ray photoelectron spectroscopy (XPS), and reflection electron energy loss spectroscopy (REELS). The XPS analysis of elements and their chemical states at the surface of MNPs and f-MNPs revealed differences in chemical bonding of atoms, content of carbon-oxygen groups, iron oxide forms, iron oxide magnetic properties, adsorbed molecules, surface coverage, and overlayer thickness, whereas the Auger parameters (derived from XPS and Auger spectra) and elastic and inelastic scattering probabilities of electrons on atoms and valence band electrons (derived from REELS spectra) indicated modification of surface charge redistribution, electronic, and optical properties. These modified properties of f-MNPs influenced their biological properties. The surfaces biocompatible for L929 cells showed various cytotoxicity for HeLa cells (10.8-5.3% of cell death), the highest for MNPs functionalized with oxalic acid. The samples exhibiting the largest efficiency possessed smaller surface coverage and thickness of adsorbed molecules layers, the highest content of oxygen and carbon-oxygen functionalizing groups, the highest ratio of lattice O2- and OH- to C sp2 hybridizations on MNP surface, the highest ratio of adsorbed O- and OH- to C sp2 hybridizations on adsorbed molecule layers, the closest electronic and optical properties to Fe3O4, and the lowest degree of admolecule polymerization. This high cytotoxicity was attributed to interaction of cells with a surface, where increased content of oxygen groups, adsorbed O-, and OH- may play the role of additional adsorption and catalytic sites and a large content of adsorbed molecule layers of carboxylic groups facilitating Fenton reaction kinetics leading to cell damage.
RESUMO
Graphene on diamond has been attracting considerable attention due to the unique and highly beneficial features of this heterostructure for a range of electronic applications. Here, ultrahigh-vacuum X-ray photoelectron spectroscopy is used for in situ analysis of the temperature dependence of the Ni-assisted thermally induced graphitization process of intrinsic nanocrystalline diamond thin films (65 nm thickness, 50-80 nm grain size) on silicon wafer substrates. Three major stages of diamond film transformation are determined from XPS during the thermal annealing in the temperature range from 300 °C to 800 °C. Heating from 300 °C causes removal of oxygen; formation of the disordered carbon phase is observed at 400 °C; the disordered carbon progressively transforms to graphitic phase whereas the diamond phase disappears from the surface from 500 °C. In the well-controllable temperature regime between 600 °C and 700 °C, the nanocrystalline diamond thin film is mainly preserved, while graphitic layers form on the surface as the predominant carbon phase. Moreover, the graphitization is facilitated by a disordered carbon interlayer that inherently forms between diamond and graphitic layers by Ni catalyst. Thus, the process results in formation of a multilayer heterostructure on silicon substrate.