Investigation of the mechanical and chemical characteristics of nanotubular and nano-pitted anodic films on grade 2 titanium dental implant materials.

OBJECTIVE: The objective of this study was to investigate the reproducibility, mechanical integrity, surface characteristics and corrosion behavior of nanotubular (NT) titanium oxide arrays in comparison with a novel nano-pitted (NP) anodic film. METHODS: Surface treatment processes were developed to grow homogenous NT and NP anodic films on the surface of grade 2 titanium discs and dental implants. The effect of process parameters on the surface characteristics and reproducibility of the anodic films was investigated and optimized. The mechanical integrity of the NT and NP anodic films were investigated by scanning electron microscopy, surface roughness measurement, scratch resistance and screwing tests, while the chemical and physicochemical properties were investigated in corrosion tests, contact angle measurement and X-ray photoelectron spectroscopy (XPS). RESULTS AND DISCUSSION: The growth of NT anodic films was highly affected by process parameters, especially by temperature, and they were apt to corrosion and exfoliation. In contrast, the anodic growth of NP film showed high reproducibility even on the surface of 3-dimensional screw dental implants and they did not show signs of corrosion and exfoliation. The underlying reason of the difference in the tendency for exfoliation of the NT and NP anodic films is unclear; however the XPS analysis revealed fluorine dopants in a magnitude larger concentration on NT anodic film than on NP surface, which was identified as a possible causative. Concerning other surface characteristics that are supposed to affect the biological behavior of titanium implants, surface roughness values were found to be similar, whereas considerable differences were revealed in the wettability of the NT and NP anodic films. CONCLUSION: Our findings suggest that the applicability of NT anodic films on the surface of titanium bone implants may be limited because of mechanical considerations. In contrast, it is worth to consider the applicability of nano-pitted anodic films over nanotubular arrays for the enhancement of the biological properties of titanium implants.

[Carbon/carbon implants in oral and maxillofacial surgery--Part 2]. / Karbon/karbon implantátumok az arc- és állcsontsebészetben--2. rész.

In their previous report, the authors presented observations regarding the long-term application of carbon/carbon implants. After evaluating the good functional and aesthetic results, the effect of the human body on the structure and morphology of the implants was investigated with state of the art methods. An implant retrieved from the body after eight years was compared to implants which were sterilized but not implanted (reference). Carbon and oxygen were the main components of both implants, however, as a result of the interaction with the human body the amount of oxygen increased 3-4 times and phosphorus, sulphur, calcium and iron were detectable as trace elements on the surface. The width of the carbon fibres (5-7 µm) building up the implants was not changed during the interaction with the human body. The surface of the implant retrieved from the human body was covered with a 15-17 µm thick layer, not present on the reference implant, having a similar composition to that of the carbon fibres (high amount of calcium that is typical to bone tissue was not detected). According to these results, the structure and the morphology of the implants were not altered notably by the human body.

[Changes in the indications for oral surgical implants based on statistical analysis]. / Az implantációs sebészeti beavatkozások indikációs területének változása a statisztikai vizsgálatok tükrében.

Journals, books and lectures on oral implantology are concerned less and less with the various fields of indication and their changes. The reason for this is in part that from a surgical point of view we consider the lack of contraindication as the indication of dental implant placement, while from a prosthetic point of view implant supported prosthetic work can be done in any prosthetic situation. Despite of this it is an interesting question, how the ratios of the various fields of indication have changed in view of the age groups and genders in Hungary in the past twenty years. In the present study a part of the patients reporting to the outpatient clinic of the Department of Oral and Maxillofacial Surgery and Dentistry of Semmelweis University for dental implant placement in the past 22 years were analyzed using statistical methods. Various age groups, genders and types of implants were compared in view of the indication of placement. The results were compared to data published in international literature.