RESUMO
BACKGROUND: Dental materials with dentine regenerative properties are preferred over conventional materials. Calcium silicate cements, such as Biodentine, are bioactive and offer excellent sealing ability, making them ideal for various dental treatments. OBJECTIVES: This study aimed to fabricate bioactive calcium silicates infused with titanium (Ti) and strontium (Sr) to optimize their neo-angiogenic, antimicrobial, and regenerative properties while maintaining mechanical stability. METHODOLOGY: Ti- and Sr-infused calcium silicate cements were synthesized, and their mineral phases were characterized using X-ray diffraction. Morphological and elemental analyses were performed using field emission scanning electron microscopy (FESEM) and energy dispersive X-ray spectroscopy (EDS). Raman spectroscopy was used to confirm the formation of bioactive material. A hemocompatibility assessment was conducted to evaluate blood compatibility. RESULTS: The presence of Ca2, SiO4, and SrTiO3 mineral phases indicated the successful infusion of Ti and Sr into the calcium silicate cement. FESEM and EDS revealed interconnected small spheres and rods in the silicate network with the relevant elemental compositions. Raman spectra verified that Si-O-Si and Ti-O-Ti vibrations exist, validating the formation of a bioactive material. The hemocompatibility assessment demonstrated optimal blood compatibility. CONCLUSIONS: This study successfully fabricated an improved calcium silicate-based material with enhanced regenerative properties and excellent biocompatibility. This newly formed substrate holds promise for providing superior restorative solutions and aiding in conservative treatment modalities during dental procedures.