Interconnected Nanoporous Polysulfone by the Self-Assembly of Randomly Linked Copolymer Networks and Linear Multiblocks.

Porous materials have attracted considerable attention due to their versatile applications, especially in water purification. Interconnected nanoporous structures are distinguished by their high degree of porosity and resistance to clogging, as well as their insensitivity to nanostructural orientation. Previous works on randomly linked copolymer systems have shown that they can effectively produce disordered cocontinuous nanostructures, which upon removal of one component yield interconnected nanoporous materials. However, the cocontinuous nanomaterials previously developed using polystyrene (PS) and poly(d,l-lactic acid) (PLA) strands, and the resulting interconnected nanoporous PS monoliths, were far too brittle to enable practical use as membranes. Here, we study the self-assembly of randomly linked copolymer networks prepared using blocks of the engineering polymer polysulfone (PSU). A wide cocontinuous regime (spanning 40 wt %) was found for randomly end-linked copolymer networks (RECNs) constructed from PSU and PLA strands, via a combination of mechanical testing, gravimetry, small-angle X-ray scattering, and scanning electron microscopy. The PSU/PLA cocontinuous nanomaterial with symmetric composition showed 2.4 times higher Young's modulus and ∼100 times greater toughness than the corresponding PS/PLA sample. The interconnected nanoporous PSU fabricated after etching of PLA even exhibited 1.6 times greater toughness than PS/PLA prior to PLA removal. To facilitate the production of thin films of cocontinuous nanomaterials, we applied solution-processable randomly linked linear PSU/PLA multiblock polymers onto ultrafiltration membranes. The interconnected nanoporous PSU thin film generated by etching PLA was found to effectively reject 50 nm diameter particles without significantly compromising permeability. This discovery presents a valuable addition to the existing techniques used to fabricate PSU membranes. In contrast to traditional methods, which are sensitive to processing conditions, produce a wide range of pore sizes, and offer limited adjustability of pore size, the current technique is anticipated to enable interconnected PSU membranes with more uniform and tailorable porosity.

Janus bottlebrush compatibilizers.

Bottlebrush random copolymers (BRCPs), consisting of a random distribution of two homopolymer chains along a backbone, can segregate to the interface between two immiscible homopolymers. BRCPs undergo a reconfiguration, where each block segregates to one of the homopolymer phases, adopting a Janus-type structure, reducing the interfacial tension and promoting adhesion between the two homopolymers, thereby serving as a Janus bottlebrush copolymer (JBCP) compatibilizer. We synthesized a series of JBCPs by copolymerizing deuterated or hydrogenated polystyrene (DPS/PS) and poly(tert-butyl acrylate) (PtBA) macromonomers using ruthenium benzylidene-initiated ring-opening metathesis polymerization (ROMP). Subsequent acid-catalyzed hydrolysis converted the PtBA brushes to poly(acrylic acid) (PAA). The JBCPs were then placed at the interface between DPS/PS homopolymers and poly(2-vinyl pyridine) (P2VP) homopolymers, where the degree of polymerization of the backbone (NBB) and the grafting density (GD) of the JBCPs were varied. Neutron reflectivity (NR) was used to determine the interfacial width and segmental density distributions (including PS homopolymer, PS block, PAA block and P2VP homopolymer) across the polymer-polymer interface. Our findings indicate that the star-like JBCP with NBB = 6 produces the largest interfacial broadening. Increasing NBB to 100 (rod-like shape) and 250 (worm-like shape) reduced the interfacial broadening due to a decrease in the interactions between blocks and homopolymers by stretching of blocks. Decreasing the GD from 100% to 80% at NBB = 100 caused an increase the interfacial width, yet further decreasing the GD to 50% and 20% reduced the interfacial width, as 80% of GD may efficiently increase the flexibility of blocks and promote interactions between homopolymers, while maintaining relatively high number of blocks attached to one molecule. The interfacial conformation of JBCPs was further translated into compatibilization efficiency. Thin film morphology studies showed that only the lower NBB values (NBB = 6 and NBB = 24) and the 80% GD of NBB = 100 had bicontinuous morphologies, due to a sufficient binding energy that arrested phase separation, supported by mechanical testing using asymmetric double cantilever beam (ADCB) tests. These provide fundamental insights into the assembly behavior of JBCPs compatibilizers at homopolymer interfaces, opening strategies for the design of new BCP compatibilizers.

Cocontinuous Nanostructures by Microphase Separation of Statistically Cross-Linked Polystyrene/Poly(2-vinylpyridine) Networks.

Cocontinuous polymeric nanostructures have drawn considerable attention due to their ability to combine distinct, percolation-dependent properties of two different polymer domains. Randomly end-linked copolymer networks (RECNs) have previously been shown to support the formation of disordered cocontinuous nanostructures across wide composition windows in a robust way. However, achieving highly efficient linking of telechelic polymers with excellent end-group fidelity often requires complex synthetic routes. As an alternative, we study here statistically cross-linked copolymer networks (SCCNs) composed of polystyrene and poly(2-vinylpyridine) (PS and P2VP) with cross-linkable allyl pendent groups that are conveniently synthesized by controlled radical copolymerization. Via selective extraction of P2VP, coupled with gravimetry, small-angle X-ray scattering, and electron microscopy, we find disordered cocontinuous phases across wide composition ranges (up to ≈ 35 wt %), approaching values previously determined for RECNs. Remarkably, even for samples that appear to exhibit full percolation, a substantial fraction of P2VP (≈ 20-30 wt %) cannot be removed, which we ascribe to short strands between nearby cross-linkers that are physically embedded within PS domains. The resulting PS porous monoliths with residual surface P2VP layers enable facile surface modification to resist protein adsorption and templating of porous gold nanostructures.