Effect of durian peel fiber on thermal, mechanical, and biodegradation characteristics of thermoplastic cassava starch composites.

This study is focused on developing and enhancing the properties of durian peel fiber (DPF) reinforced thermoplastic cassava starch (TPCS) composites. The proposed DPF was extracted from agro-waste and incorporated into TPCS with various contents of DPF (10, 20, 30, 40, and 50 wt%) via compression molding. The mechanical and thermal characteristics of the fabricated composites were studied. The thermal properties of the biocomposite were improved with the addition of DPF, as evidenced by an increase in the material's thermal stability and indicated by a higher onset decomposition temperature. The integration of DPF into TPCS improved the biodegradation rate process of the composites. Besides, the results indicated that incorporating DPF in TPCS composites enhanced tensile and flexural properties, with a 40 wt% DPF content exhibited the highest modulus and strength. The tensile and flexural strengths of TPCS/DPF composites were raised significantly from 2.96 to 21.89 MPa and 2.5 to 35.0 MPa, respectively, compared to the control TPCS sample, as DPF increased from 0 to 40 wt%. This finding was consistent with Fourier-Transform Infrared (FT-IR) spectroscopy and scanning electron micrograph (SEM), which showed good interaction between DPF and TPCS matrix. The analysis revealed that DPF at a 40 wt% ratio was the best composition compared to the other ratio. Finally, based on improved results, DPF was identified as a potential resource of green reinforcement for the biodegradable TPCS matrix.

Unlocking the Potential of Lignocellulosic Biomass Dragon Fruit (Hylocereus polyrhizus) in Bioplastics, Biocomposites and Various Commercial Applications.

Dragon fruit, also called pitaya or pitahaya, is in the family Cactaceae. It is found in two genera: 'Selenicereus' and 'Hylocereus'. The substantial growth in demand intensifies dragon fruit processing operations, and waste materials such as peels and seeds are generated in more significant quantities. The transformation of waste materials into value-added components needs greater focus since managing food waste is an important environmental concern. Two well-known varieties of dragon fruit are pitaya (Stenocereus) and pitahaya (Hylocereus), which are different in their sour and sweet tastes. The flesh of the dragon fruit constitutes about two-thirds (~65%) of the fruit, and the peel is approximately one-third (~22%). Dragon fruit peel is believed to be rich in pectin and dietary fibre. In this regard, extracting pectin from dragon fruit peel can be an innovative technology that minimises waste disposal and adds value to the peel. Dragon fruit are currently used in several applications, such as bioplastics, natural dyes and cosmetics. Further research is recommended for diverging its development in various areas and maturing the innovation of its usage.

Natural Fiber-Reinforced Polylactic Acid, Polylactic Acid Blends and Their Composites for Advanced Applications.

Polylactic acid (PLA) is a thermoplastic polymer produced from lactic acid that has been chiefly utilized in biodegradable material and as a composite matrix material. PLA is a prominent biomaterial that is widely used to replace traditional petrochemical-based polymers in various applications owing environmental concerns. Green composites have gained greater attention as ecological consciousness has grown since they have the potential to be more appealing than conventional petroleum-based composites, which are toxic and nonbiodegradable. PLA-based composites with natural fiber have been extensively utilized in a variety of applications, from packaging to medicine, due to their biodegradable, recyclable, high mechanical strength, low toxicity, good barrier properties, friendly processing, and excellent characteristics. A summary of natural fibers, green composites, and PLA, along with their respective properties, classification, functionality, and different processing methods, are discussed to discover the natural fiber-reinforced PLA composite material development for a wide range of applications. This work also emphasizes the research and properties of PLA-based green composites, PLA blend composites, and PLA hybrid composites over the past few years. PLA's potential as a strong material in engineering applications areas is addressed. This review also covers issues, challenges, opportunities, and perspectives in developing and characterizing PLA-based green composites.

Effect of palm wax on the mechanical, thermal, and moisture absorption properties of thermoplastic cassava starch composites.

Thermoplastic starch is a potentially sustainable and biodegradable material. However, it possesses some limitations in terms of mechanical performance and high moisture sensitivity. In this current work, the characteristics of thermoplastic cassava starch (TPCS) containing palm wax at various loading were evaluated. TPCS was prepared via hot pressing by varying the ratios of palm wax (2.5, 5, 10, and 15 wt%). Next, characterization via scanning electron microscopy (SEM), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), Fourier-transform infrared spectroscopy (FT-IR), mechanical, water solubility, thickness swelling and moisture absorption tests, were conducted on the samples. The findings showed that incorporating starch-based thermoplastics with palm wax has remarkably improved mechanical characteristics of the thermoplastic blends. Besides, the morphology of the samples demonstrated irregular and rougher cleavage fracture after palm wax addition. FT-IR indicated the existence of intermolecular interaction between TPCS and palm wax with the intermolecular hydrogen bonds that existed between them. The thermal stability of TPCS has improved with rising palm wax content. The incorporation of 15 wt% palm wax resulted in the lowest moisture absorption value among the samples. Overall, the developed TPCS/palm wax with improved mechanical and moisture resistance characteristics has the potential to be used as biodegradable materials.

Extraction and Characterization of Natural Cellulosic Fiber from Pandanus amaryllifolius Leaves.

Pandanus amaryllifolius is a member of Pandanaceae family and is abundant in south-east Asian countries including Malaysia, Thailand, Indonesia and India. In this study, Pandanus amaryllifolius fibres were extracted via a water retting extraction process and were investigated as potential fibre reinforcement in polymer composite. Several tests were carried out to investigate the characterization of Pandanus amaryllifolius fibre such as chemical composition analysis which revealed Pandanus amaryllifolius fibre's cellulose, hemicellulose and lignin content of 48.79%, 19.95% and 18.64% respectively. Material functional groups were analysed by using Fourier transform infrared (FTIR) spectroscopy and X-ray diffraction analysis confirming the presence of cellulose and amorphous substances in the fibre. The morphology of extracted Pandanus amaryllifolius fibre was studied using a scanning electron microscope (SEM). Further mechanical behaviour of fibre was investigated using a single fibre test with 5 kN cell load and tensile strength was found to be 45.61 ± 16.09 MPa for an average fibre diameter of 368.57 ± 50.47 µm. Meanwhile, moisture content analysis indicated a 6.00% moisture absorption rate of Pandanus amaryllifolius fibre. The thermogravimetric analysis justified the thermal stability of Pandanus amaryllifolius fibre up to 210 °C, which is within polymerization process temperature conditions. Overall, the finding shows that Pandanus amaryllifolius fibre may be used as alternative reinforcement particularly for a bio-based polymer matrix.

Thermoplastic starch/beeswax blend: Characterization on thermal mechanical and moisture absorption properties.

Cassava starch has acquired many attentions owing to its ability to be developed as thermoplastic cassava starch (TPCS) where it can be obtained in low cost, making it to be one of alternatives to substitute petroleum-based plastic. An attempt was made to investigate the thermal, mechanical and moisture absorption properties of thermoplastic cassava starch blending with beeswax (TPCS-BW) fabricated using hot moulding compression method in the range of beeswax loading from 0, 2.5, 5 to 10 wt%. Addition of beeswax has significantly reduced tensile strength, elongation and flexural strength while improving tensile modulus and flexural modulus until 5 wt% beeswax. Incorporation of 10 wt% beeswax has successfully produced the lowest value of moisture absorption and water solubility among the bio-composite which might be attributed to the beeswax's hydrophobic properties in improving water barrier of the TPCS-BW bio-composite. Furthermore, the addition of beeswax resulted in the appearance of irregular and rough fractured surface. Meanwhile, fourier transform infrared (FT-IR) spectroscopy presented that incorporation of beeswax in the mixture has considerably improve hydrogen bonding of blends indicating good interaction between starch and beeswax. Hence, beeswax with an appropriate loading value able to improve the functional properties of TPCS-BW bio-composite.

Effect of plasticizers on physical, thermal, and tensile properties of thermoplastic films based on Dioscorea hispida starch.

This study examines the effects of varying the concentrations of sorbitol (S) and glycerol (G) on the physical, morphological, thermal, and mechanical properties of Dioscorea hispida, starch-based films. In this context, the films of Dioscorea hispida starch were developed using solution casting technique with glycerol (G), sorbitol (S), and a mixture of sorbitol-glycerol (SG) as plasticizers at the ratios of 0, 30, 45, and 60 wt%. The films' moisture contents were increased when increasing the plasticizer contents. The tensile strengths were decreased, but elongations at break were increased; 7.38%-11.54% for G-plasticized films, 10.17%-15.76% for S-plasticized films, and 14.41%- 16.10% for SG-plasticized films with increasing plasticizer concentrations of the film samples. Varying plasticizer concentrations exhibited a minor effect on the S-plasticized film's thermal properties. Significant decrement in the glass transition temperatures of Dioscorea hispida starch films was observed when the plasticizer contents were raised from 30% to 60%. Significantly, the present work has shown that plasticized Dioscorea hispida starch can be considered a promising biopolymer for the applications of biodegradable films.

Physical Properties of Thermoplastic Starch Derived from Natural Resources and Its Blends: A Review.

Thermoplastic starch composites have attracted significant attention due to the rise of environmental pollutions induced by the use of synthetic petroleum-based polymer materials. The degradation of traditional plastics requires an unusually long time, which may lead to high cost and secondary pollution. To solve these difficulties, more petroleum-based plastics should be substituted with sustainable bio-based plastics. Renewable and natural materials that are abundant in nature are potential candidates for a wide range of polymers, which can be used to replace their synthetic counterparts. This paper focuses on some aspects of biopolymers and their classes, providing a description of starch as a main component of biopolymers, composites, and potential applications of thermoplastics starch-based in packaging application. Currently, biopolymer composites blended with other components have exhibited several enhanced qualities. The same behavior is also observed when natural fibre is incorporated with biopolymers. However, it should be noted that the degree of compatibility between starch and other biopolymers extensively varies depending on the specific biopolymer. Although their efficacy is yet to reach the level of their fossil fuel counterparts, biopolymers have made a distinguishing mark, which will continue to inspire the creation of novel substances for many years to come.

Extraction and Characterization of Potential Biodegradable Materials Based on Dioscorea hispida Tubers.

This study was driven by the stringent environmental legislation concerning the consumption and utilization of eco-friendly materials. Within this context, this paper aimed to examine the characteristics of starch and fibres from the Dioscorea hispida tuber plant to explore their potential as renewable materials. The extraction of the Dioscorea hispida starch and Dioscorea hispida fibres was carried out and the chemical composition, physical, thermal, morphological properties, and crystallinity were studied. The chemical composition investigations revealed that the Dioscorea hispida starch (DHS) has a low moisture t (9.45%) and starch content (37.62%) compared to cassava, corn, sugar palm, and arrowroot starches. Meanwhile, the Dioscorea hispida fibres (DHF) are significantly low in hemicellulose (4.36%), cellulose (5.63%), and lignin (2.79%) compared to cassava, corn hull and sugar palm. In this investigation the chemical, physical, morphological and thermal properties of the Dioscorea hispida fibre and Dioscorea hispida starch were examined by chemical composition investigation, scanning electron microscopy (SEM), particle size distribution, thermogravimetric analysis (TGA), X-ray powder diffraction (XRD), and Fourier transform infrared (FTIR), respectively. It was found that Dioscorea hispida waste is promising alternative biomass and sustainable material with excellent potential as a renewable filler material for food packaging applications.

Characteristics of thermoplastic sugar palm Starch/Agar blend: Thermal, tensile, and physical properties.

The aim of this work is to study the behavior of biodegradable sugar palm starch (SPS) based thermoplastic containing agar in the range of 10-40wt%. The thermoplastics were melt-mixed and then hot pressed at 140°C for 10min. SEM investigation showed good miscibility between SPS and agar. FT-IR analysis confirmed that SPS and agar were compatible and inter-molecular hydrogen bonds existed between them. Incorporation of agar increased the thermoplastic starch tensile properties (Young's modulus and tensile strength). The thermal stability and moisture uptake increased with increasing agar content. The present work shows that starch-based thermoplastics with 30wt% agar content have the highest tensile strength. Higher content of agar (40wt%) resulted to more rough cleavage fracture and slight decrease in the tensile strength. In conclusion, the addition of agar improved the thermal and tensile properties of thermoplastic SPS which widened the potential application of this eco-friendly material. The most promising applications for this eco-friendly material are short-life products such as packaging, container, tray, etc.