Impact of accelerated aging cycles on the performance of extruded cement-based composites reinforced with non-bleached eucalyptus fibers.

Thermo-mechanical pulping produces well-individualized fibers compared to wood particles and less fragile fibers compared to Kraft pulping, besides presenting higher volume, higher yield, and lower production cost, which can be an exciting alternative for the fiber-cement industries. This study evaluated the impact of soak and dry-aging cycles on the performance of extruded composites reinforced with non-bleached eucalyptus fibers. The cement matrix comprised cement (70%) and limestone (30%). Composites were reinforced with 1 to 5% of eucalyptus fiber by cement mass and tested on the 28th day of cure at 99% relative humidity and after 400 accelerated aging cycles. The water absorption and apparent porosity gradually increased with the reinforcement level. Composites with 4 and 5% fibers showed the highest toughness (0.21 and 0.23 kJ/m2, respectively). The aging by 400 soak-dry cycles reduced the composites' water absorption and apparent porosity. The modulus of elasticity (MOE), rupture (MOR), and toughness increased, except for toughness for composites reinforced with 1 and 5% fibers, explained by the cementitious matrix's continuous hydration, fiber mineralization, and natural carbonation. In general, eucalyptus thermo-mechanical fibers were suitable for producing cementitious composites. Cementitious composites with 3% fibers presented a higher MOR, MOE, low water absorption, and apparent porosity after 400 accelerated aging cycles. In addition, the composites with 4% fibers also presented remarkable improvements in these properties. The aging cycles did not result in composites with less resistance, a positive fact for their application as tiles and materials for external use in civil construction.

Copaiba oil and vegetal tannin as functionalizing agents for açai nanofibril films: valorization of forest wastes from Amazonia.

The applicability of cellulose nanofibrils (CNFs) has received attention due to their attractive properties. This study proposes the functionalization of açai CNFs with copaiba oil and vegetal tannins to produce films with potential for packaging. Bio-based films were evaluated by vapor permeability, colorimetry, and mechanical strength. CNFs were produced by mechanical fibrillation, from suspensions of bleached açai fibers and commercial eucalipytus pulp. Moreover, copaiba oil and vegetal tannin were added to the CNFs to produce films/nanopapers by casting from both suspensions with concentrations of 1% (based on CNF dry mass). The bulk densities of the eucalyptus CNF films were higher (1.126-1.171 g cm-3) compared to the açai CNF ones. Films from eucalyptus and açai pulps containing copaiba oil and tannins presented higher Tonset and Tmax, respectively (312 and 370 °C). Films with açaí CNFs functionalized with copaiba oil and tannin showed the lowest permeability value (370 g day-1 m-2). Films produced with eucalyptus pulp, and eucalyptus pulp functionalized with copaiba oil highlighted by superior mechanical strength, achieving 133.8 and 121.4 MPa, respectively. The evaluation of colorimetry showed a greater tendency to yellowing for açai films, especially those functionalized with vegetal tannins. Besides the low cost, functionalized vegetal-based nanomaterials could have attractive properties, with potential for application as some kind of packaging, for transporting basic products, such as breads, flours, or products with low moisture content, enabling efficient utilization of forest wastes.