RESUMO
This comparative study was conducted to assess the intramedullary bone tissue reaction of an ion-releasing resin modified glass-ionomer cement with claimed bioactivity (ACTIVA bioactive resin) restorative material versus Mineral Trioxide Aggregate High Plasticity (MTA HP) and bioceramic putty iRoot BP Plus. Fifty-six adult male Wistar rats were assigned into 4 equal groups (14 rats each). A surgical intramedullary bi-lateral tibial bone defects were performed in rats of the control group I (GI) and left without any treatment to be considered as controls (n = 28). The rats of groups II, III and IV were handled as group I except that the tibial bone defects were filled with ACTIVA, MTA HP and iRoot BP, respectively. In all groups, rats were euthanized after one month and specimens were processed to histological investigation, SEM examination and EDX elemental analysis. In addition, semi-quantitative histomorphometric scoring system was conducted for the following parameters; new bone formation, inflammatory response, angiogenesis, granulation tissue, osteoblasts and osteoclasts. The clinical follow-up outcome of this study revealed the recovery of rats after 4 days post-surgical procedure. It was observed that the animal subjects returned to their routine activities, e.g., walking, grooming and eating. The rats showed normal chewing efficiency without any weight loss or postoperative complications. Histologically, the control group sections showed scanty, very thin, new bone trabeculae of immature woven type located mostly at the peripheral part of the tibial bone defects. These defects exhibited greater amount of thick bands of typically organized granulation tissue with central and peripheral orientation. Meanwhile, bone defects of ACTIVA group showed an empty space surrounded by thick, newly formed, immature woven bone trabeculae. Moreover, bone defects of MTA HP group were partially filled with thick newly formed woven bone trabeculae with wide marrow spaces presented centrally and at the periphery with little amount of mature granulation tissue at the central part. The iRoot BP Plus group section exhibited an observable woven bone formation of normal trabecular structures with narrow marrow spaces presented centrally and at the periphery showed lesser amount of well-organized/mature granulation tissue formation. Kruskal Wallis test revealed total significant differences between the control, ACTIVA, MTAHP and iRoot BP Plus groups (p < 0.05). Meanwhile, Mann-Whitney U test showed significant difference between control and ACTIVA groups, Control and MTA HP groups, control and iRoot BP Plus groups. ACTIVA and MTA HP groups, ACTIVA and iRoot BP Plus (p Ë 0.05) with no significant difference between MTA HP and iRoot BP Plus (p > 0.05). The elemental analysis outcome showed that the lesions of the control group specimens were filled with recently created trabecular bone with limited marrow spaces. EDX tests (Ca and P analysis) indicated a lower degree of mineralization. Lower amounts of Ca and P was expressed in the mapping analysis compared with other test groups. Calcium silicate-based cements induce more bone formation when compared to an ion-releasing resin modified glass-ionomer restoration with claimed bioactivity. Moreover, the bio-inductive properties of the three tested materials are likely the same. Clinical significance: bioactive resin composite can be used as a retrograde filling.
Assuntos
Compostos de Cálcio , Silicatos , Masculino , Ratos , Animais , Ratos Wistar , Compostos de Cálcio/química , Silicatos/química , Óxidos/química , Osso e Ossos , Animais de Laboratório , Compostos de Alumínio/química , Combinação de Medicamentos , Teste de MateriaisRESUMO
Titanium alloys, such as Ti-10Ta-2Nb-2Zr (TTNZ), are promising biomaterials due to their excellent biocompatibility and low Young's modulus. The TTNZ samples herein were manufactured by selective laser melting and the novel material was evaluated as a dental implant in vitro and in vivo. The microstructure, mechanical properties, electrochemical behaviour, cytotoxicity, haemocompatibility and osteogenic differentiation were systematically investigated. Based on the tensile test results, the as-printed TTNZ samples had an elongation of 20.23% ± 1.95%, an ultimate tensile strength of 646.61 ± 24.96 MPa and a Young's modulus of 23.72 ± 1.18 GPa. According to the biocompatible value, the as-printed TTNZ sample exhibited no cell cytotoxicity and it showed even better cell adhesion ability than that of the as-printed Ti-6Al-4 V and wrought Ti-6Al-4 V samples. The haemolysis percentage of the as-printed TTNZ sample was 0.629% ± 0.363%. Moreover, the as-printed TTNZ sample facilitated protein adsorption and osteogenic differentiation of human osteoblast-like (MG-63) cells in vitro. The in vivo data also demonstrated the histocompatibility of the as-printed TTNZ. In summary, the as-printed TTNZ developed in this study demonstrated good biocompatibility, low stress shielding, excellent ductility and great osteogenic differentiation. These results indicated that as-printed TTNZ alloys can be promising for end-use human biomedical applications.