Functionalization of magnetic nanoparticles with amphiphilic block copolymers: self-assembled thermoresponsive submicrometer particles.

For the first time the four block copolymers derived from 1-alkyl[2-(acryloyloxy)ethyl]dimethylammonium bromides with hexyl (ADA) or cetyl (ADHA) groups and 2-hydroxyethylacrylate (HEA) or N-isopropylacrylamide (NIPAM) were synthesized and employed for functionalization of monodisperse iron oxide nanoparticles (NPs). The polyADA (pADA) or polyADHA (pADHA) block consists of long hydrophobic tails (C(6) or C(16)) connected to a positively charged quaternary ammonium group, making this block amphiphilic. The second block was either fully hydrophilic (pHEA) or thermoresponsive (pNIPAM). The dependence of the NP coating on the length of the hydrophobic tail in the amphiphilic block, the composition of the hydrophilic block, and the NP sizes have been studied. Unusual self-assembling of iron oxide NPs into well-defined composite submicrometer particles was observed for pADHA-b-pNIPAM in the wide range of concentrations (at the pADHA repeating unit concentrations of 0.065 × 10(-2)-2.91 × 10(-2) mmol/mL per 1 mg/mL NPs) but only two concentrations, 1.62 × 10(-2) and 1.94 × 10(-2) mmol/mL, led to regular spherical particles. The thermoresponsive behavior of these composite particles was tested using ζ-potential and dynamic light scattering measurements, while the morphology of particles was characterized by transmission electron microscopy. Coating of NPs with pADHA-b-pHEA results in the formation of individually coated NPs. The different composite particle morphologies are explained by different properties of pHEA and pNIPAM. It is demonstrated that the composite particles based on pADHA-b-pNIPAM are responsive to a magnetic field and can be recommended as magnetic stoppers in biorelated membrane separations. The incorporation of Pd species in submicrometer particles makes them promising candidates for catalytic applications as magnetically recoverable catalysts with a high magnetic response.

Metalated diblock and triblock poly(ethylene oxide)-block-poly(4-vinylpyridine) copolymers: understanding of micelle and bulk structure.

The paper provides new insights into the structure of Pt-containing diblock and triblock copolymers based on poly(ethylene oxide) (PEO) and poly(4-vinylpyridine) (P4VP), using a combination of atomic force microscopy (AFM), X-ray diffraction (XRD), transmission electron microscopy (TEM), and anomalous small-angle X-ray scattering (ASAXS). Parallel studies using methods contributing supplemental structural information allowed us to comprehensively characterize sophisticated polymer systems during metalation and to exclude possible ambiguity of the data interpretation of each of the methods. AFM and TEM make available the determination of sizes of the micelles and of the Pt-containing micelle cores, respectively, while a combination of XRD, TEM, and ASAXS reveals Pt-nanoparticle size distributions and locations along with the structural information about the polymer matrix. In addition, for the first time, ASAXS revealed the organization of Pt-nanoparticle-filled diblock and triblock copolymers in the bulk. The nanoparticle characteristics are mainly determined by the type of block copolymer system in which they are found: larger particles (2.0-3.0 nm) are formed in triblock copolymer micelles, while smaller ones (1.5-2.5 nm) are found in diblock copolymer micelles. This can be explained by facilitated intermicellar exchange in triblock copolymer systems. For both systems, Pt nanoparticles have narrow particle size distributions as a result of a strong interaction between the nanoparticle surface and the P4VP units inside the micelle cores. The pH of the medium mainly influences the particle location rather than the particle size. A structural model of Pt-nanoparticle clustering in the diblock PEO-b-P4VP and triblock P4VP-b-PEO-b-P4VP copolymers in the bulk was constructed ab initio from the ASAXS data. This model reveals that nearly spherical micellar cores of about 10 nm in diameter (filled with Pt nanoparticles) aggregate forming slightly oblate hollow bodies with an outer diameter of about 40 nm.

Influence of metalation on the morphologies of poly(ethylene oxide)-block-poly(4-vinylpyridine) block copolymer micelles.

Micellization of a poly(ethylene oxide)-block-poly(4-vinylpyridine) (PEO45-b-P4VP28) copolymer in water during metalation (incorporation of gold compounds and gold nanoparticle formation) with three types of gold compounds, NaAuCl4, HAuCl4, and AuCl3, was studied using dynamic light scattering (DLS) and transmission electron microscopy (TEM). The transformations of the PEO45-b-P4VP28 block copolymer micelles in water were found to depend on a number of parameters including the thermal history of the as-prepared block copolymer, the type of the metal compound, and the metal loading. For the HAuCl4-filled PE045-b-P4VP28 micelles, the subsequent reduction with hydrazine hydrate results in a significant fraction of rodlike micelles, suggesting that slow nucleation (confirmed by the formation of the large gold nanoparticles) and facilitated migration of gold ions yields the ideal conditions for sphere-to-rod micellar transition.