A Polymer Blend Electrolyte Based on CS with Enhanced Ion Transport and Electrochemical Properties for Electrical Double Layer Capacitor Applications.

The fabrication of energy storage EDLC in this work is achieved with the implementation of a conducting chitosan-methylcellulose-NH4NO3-glycerol polymer electrolyte system. The simple solution cast method has been used to prepare the electrolyte. The impedance of the samples was fitted with equivalent circuits to design the circuit diagram. The parameters associated with ion transport are well studied at various plasticizer concentrations. The FTIR investigation has been done on the films to detect the interaction that occurs among plasticizer and polymer electrolyte. To get more insights into ion transport parameters, the FTIR was deconvoluted. The transport properties achieved from both impedance and FTIR are discussed in detail. It was discovered that the transport parameter findings are in good agreement with both impedance and FTIR studies. A sample with high transport properties was characterized for ion dominancy and stability through the TNM and LSV investigations. The dominancy of ions in the electrolyte verified as the tion of the electrolyte is established to be 0.933 whereas it is potentially stable up to 1.87 V. The rechargeability of the EDLC is steady up to 500 cycles. The internal resistance, energy density, and power density of the EDLC at the 1st cycle are 53 ohms, 6.97 Wh/kg, and 1941 W/kg, respectively.

Fabrication of Co3O4 from Cobalt/2,6-Napthalenedicarboxylic Acid Metal-Organic Framework as Electrode for Supercapacitor Application.

In this study, cobalt-based metal-organic framework (MOF) powder was prepared via the solvothermal method using 2,6-naphthalenedicarboxylic acid (NDC) as the organic linker and N,N-dimethylformamide (DMF) as the solvent. The thermal decomposition of the pristine cobalt-based MOF sample (CN-R) was identified using a thermogravimetric examination (TGA). The morphology and structure of the MOFs were modified during the pyrolysis process at three different temperatures: 300, 400, and 500 °C, which labeled as CN-300, CN-400, and CN-500, respectively. The results were evidenced via field-emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD). The crystallite size of all samples was calculated using Scherrer's equation. The smallest crystallite size of 7.77 nm was calculated for the CN-300 sample. Fourier transform infrared spectroscopy (FTIR) spectra were acquired for all the samples. The graphical study of the cyclic voltammogram (CV) gave the reduction and oxidation peaks. The charge transfer resistance and ionic conductivity were studied using electrical impedance spectroscopy (EIS). The galvanostatic charge-discharge (GCD) responses of all samples were analyzed. The relatively high specific capacitance of 229 F g-1 at 0.5 A g-1 was achieved in the sample CN-300, whereby 110% of capacitance was retained after 5000 cycles. These findings highlighted the durability of the electrode materials at high current densities over a long cycle.