RESUMO
Inks for 3D printing were prepared by dispersing bacterial cellulose nanofibers (CNF) functionalized with methacrylate groups in a polymerizable deep eutectic solvent (DES) based on choline chloride and acrylic acid with water as a cosolvent. After 3D printing and UV-curing, the double-network composite gel consisting of chemically and physically crosslinked structures composed from sub-networks of modified CNF and polymerized DES, respectively, was formed. The rheological properties of inks, as well as mechanical and shape memory properties of the 3D-printed gels, were investigated in dynamic and static modes. It was shown that the optimal amount of water allows improvement of the mechanical properties of the composite gel due to the formation of closer contacts between the modified CNF. The addition of 12 wt% water results in an increase in strength and ultimate elongation to 11.9 MPa and 300%, respectively, in comparison with 5.5 MPa and 100% for an anhydrous system. At the same time, the best shape memory properties were found for an anhydrous system: shape fixation and recovery coefficients were 80.0 and 95.8%, respectively.
RESUMO
New tubular conduits have been developed for the regeneration of peripheral nerves and the repair of defects that are larger than 3 cm. The conduits consist of a combination of poly(L-lactide) nanofibers and chitosan composite fibers with chitin nanofibrils. In vitro studies were conducted to assess the biocompatibility of the conduits using human embryonic bone marrow stromal cells (FetMSCs). The studies revealed good adhesion and differentiation of the cells on the conduits just one day after cultivation. Furthermore, an in vivo study was carried out to evaluate motor-coordination disorders using the sciatic nerve functional index (SFI) assessment. The presence of chitosan monofibers and chitosan composite fibers with chitin nanofibrils in the conduit design increased the regeneration rate of the sciatic nerve, with an SFI value ranging from 76 to 83. The degree of recovery of nerve conduction was measured by the amplitude of M-response, which showed a 46% improvement. The conduit design imitates the oriented architecture of the nerve, facilitates electrical communication between the damaged nerve's ends, and promotes the direction of nerve growth, thereby increasing the regeneration rate.
RESUMO
This study focused on a potential application of electrically conductive, biocompatible, bioresorbable fibers for tubular conduits aimed at the regeneration of peripheral nerves. The conducting, mechanical, and biological properties of composite fibers based on chitosan and single-walled carbon nanotubes were investigated in this paper. It was shown that introducing 0.5 wt.% of SWCNT into the composite fibers facilitated the formation of a denser fiber structure, resulting in improved strength (σ = 260 MPa) and elastic (E = 14 GPa) characteristics. Additionally, the composite fibers were found to be biocompatible and did not cause significant inflammation or deformation during in vivo studies. A thin layer of connective tissue formed around the fiber.