Synthesis, characterization and application of gelatin-carboxymethyl cellulose blend films for preservation of cherry tomatoes and grapes.

In the present study, gelatin-carboxymethyl cellulose blend film was synthesized, characterized and applied for the first time to preserve cherry tomatoes (Solanum lycopersicum var. cerasiforme) and grapes (Vitis vinifera). Gelatin (Gel) film forming solution was incorporated with carboxymethyl cellulose (CMC) at three volume per volume (Gel:CMC) ratios, namely 75:25, 50:50 and 25:75. CMC treatment has improved the transparency, tensile strength (TS), elongation at break (EAB), water vapor permeability and oxygen permeability of gelatin films. A pronounced effect was obtained for 25Gel:75CMC film. The TS and EAB values were increased from 25.98 MPa and 2.34% (100Gel:0CMC) to 37.54 MPa and 4.41% (25Gel:75CMC), respectively. A significant improvement in antimicrobial property of gelatin films against two food pathogens, namely Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) was obtained in the presence of CMC. The effectiveness of gelatin-CMC blend films to extend the shelf life of agricultural products was evaluated in a 14-day preservation study. The gelatin-CMC films were successfully controlled the weight loss and browning index of the fruits up to 50.41% and 31.34%, respectively. Overall, gelatin-CMC film is an environmental friendly film for food preservation.

Chitosan, gelatin and methylcellulose films incorporated with tannic acid for food packaging.

In this work, chitosan, gelatin and methylcellulose films incorporated with tannic acid (TA) were synthesised, characterised and applied for the first time to preserve cherry tomatoes (Solanum lycopersicum var. cerasiforme) and grapes (Vitis vinifera). The addition of TA at 15% (w/w) increased the transparency value of biopolymer films. The highest increment of transparency value was obtained for MC-TA film, increased from 0.572 to 4.73 A/mm. Based on antimicrobial study, the addition of TA improved the antibacterial properties of biopolymers against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus). The ability of films to preserve both fruits was evaluated in a 14-day preservation study. The application of biopolymer films treated with TA has decreased the weight loss and browning index of fruits, as compared to control films. A significant reduction in the weight loss of cherry tomatoes wrapped with chitosan (from 21.3 to 19.6%), gelatin (from 22.1 to 15.5%) and methylcellulose (26.2 to 20.5%) films were obtained following TA treatment. Overall, results obtained from this study highlight the effects of TA on physiochemical properties of biopolymer films and their ability to preserve fruits.