Microscopic and spectroscopic study of the corona formation and unfolding of human haemoglobin in presence of ZnO nanoparticles.

The interaction of zinc oxide nanoparticles (ZnO NPs) with human haemoglobin (Hb) is studied for the biologically safe application of ZnO NPs in the human body. The Hb corona is formed around the ZnO nanoparticles, directly observed from high-resolution transmission electron microscopy (HRTEM) images. Hb formed 'hard corona' on the surface of ZnO NPs from an exponential association mechanism over a very short duration, as well as unfolding of Hb that occurred over a long lifetime. Dynamic light scattering measurements demonstrated that the ZnO NPs were completely covered by Hb with shell thickness of c. 6 nm that formed a 'hard corona'. Zeta potential measurements represented that the ZnO NPs were fully covered by Hb molecules using an exponential association mechanism. Tryptophans (TRY), as well as heme-porphyrin moieties of Hb, are the major binding sites for ZnO NPs. The nature of the interaction between ZnO NPs and Hb was analysed from the fluorescence quenching of TRYs. Electrostatic interaction, along with the hydrophobic interaction between ZnO NPs and Hb, is responsible for the conformational change in Hb due to increase in the percentage of ß-sheets together with a decrease in α-helices.

Silver nanoparticle-human hemoglobin interface: time evolution of the corona formation and interaction phenomenon.

In this paper, we have used spectroscopic and electron microscopic analysis to monitor the time evolution of the silver nanoparticles (Ag NP)-human hemoglobin (Hb) corona formation and to characterize the interaction of the Ag NPs with Hb. The time constants for surface plasmon resonance binding and reorganization are found to be 9.51 and 118.48 min, respectively. The drop of surface charge and the increase of the hydrodynamic diameter indicated the corona of Hb on the Ag NP surface. The auto correlation function is found to broaden with the increasing time of the corona formation. Surface zeta potential revealed that positively charged Hb interact electrostatically with negatively charged Ag NP surfaces. The change in α helix and ß sheet depends on the corona formation time. The visualization of the Hb corona from HRTEM showed large number of Hb domains aggregate containing essentially Ag NPs and without Ag NPs. Emission study showed the tertiary deformation, energy transfer, nature of interaction and quenching under three different temperatures.