RESUMO
Small objects of an alloy tool steel were built by selective laser melting at different scan speeds, and their microstructures were analyzed using electron backscatter diffraction (EBSD). To present an explicit correlation with the local thermal cycles in the objects, prior austenite grains were reconstructed using the EBSD mapping data. Extensive growth of austenitic grains after solidification could be detected by the disagreement between the networks of carbides and austenite grain boundaries. A rapid laser scan at 2000 mm/s led to less growth, but retained a larger amount of austenite than a slow one at 50 mm/s. The rapid scan also exhibited definite evolution of Goss-type textures in austenite, which could be attributed to the growth of austenitic grains under a steep temperature gradient. The local variations in the microstructures and the textures enabled us to speculate the locally different thermal cycles determined by the different process conditions, that is, scan speeds.
RESUMO
To gain the fundamental understanding of deformation mechanisms in an aluminum-containing austenitic high-Mn steel (Fe-32Mn-8.9Al-0.78 C (wt.%)), in-situ straining transmission electron microscopy (TEM) analysis is conducted. The in-situ observation during the deformation demonstrates that the plastic deformation is accommodated by the pronounced planar dislocation gliding followed by the formation of slip bands (SBs) and highly dense dislocation walls (HDDWs). Experimental evidences of the glide plane softening can be obtained from the interaction between the gliding perfect dislocations and the L'12 ordered precipitates in the austenite matrix. Furthermore, the observation of the localized cross-slip of dislocations at the slip band intersections enables to understand why slip bands are extensively developed without mutual obstructions between the slip bands. The enhanced strain hardening rate of the aluminum-containing austenitic high-Mn steels can be attributed to the pronounced planar dislocation glides followed by formation of extensive slip band which prevent premature failure by suppressing strain localization.
RESUMO
The discovery of SnSe single crystals with record high thermoelectric efficiency along the b-axis has led to the search for ways to synthesize polycrystalline SnSe with similar efficiencies. However, due to weak texturing and difficulties in doping, such high thermoelectric efficiencies have not been realized in polycrystals or thin films. Here, we show that highly textured and hole doped SnSe thin films with thermoelectric power factors at the single crystal level can be prepared by solution process. Purification step in the synthetic process produced a SnSe-based chalcogenidometallate precursor, which decomposes to form the SnSe2 phase. We show that the strong textures of the thin films in the b-c plane originate from the transition of two dimensional SnSe2 to SnSe. This composition change-driven transition offers wide control over composition and doping of the thin films. Our optimum SnSe thin films exhibit a thermoelectric power factor of 4.27 µW cm-1 K-2.
RESUMO
As more W replaced Mo in alumina-forming austenitic stainless steels, weight gain by oxidation decreased after 336 h at 1053 K. Electron microscopy revealed slower growth of scale in the presence of more numerous second phases by W addition. The retardation of oxidation was attributed to the necessary partitioning of W in front of the metal-oxide interface. The W-rich second phases interacted with growing oxides and finally transformed to fine particles of metallic W alloy within the scale.
RESUMO
A quantitative and automated phase analysis of dual-phase (DP) steel using electron backscatter diffraction (EBSD) was attempted. A ferrite-martensite DP microstructure was produced by intercritical annealing and quenching. An EBSD map of the microstructure was obtained and post-processed for phase discrimination. Band slope (BS), which was a measure of pattern quality, exhibited much stronger phase contrast than another conventional one, band contrast. Owing to high sensitivity to lattice defect and little orientation dependence, BS provided handiness in finding a threshold for phase discrimination. Its grain average gave a superior result on the discrimination and volume fraction measurement of the constituent phases in the DP steel.