Microstructure and Corrosion Behavior of ZnAl12Mg3Si0.3 Double-Batch Hot-Dip Coatings.

This article presents the microstructure (SEM) and corrosion behavior of ZnAl12Mg3Si0.3 (ZAMS) coatings obtained by the double hot-dip method on Sebisty steel with increased strength. On the basis of chemical composition studies in micro-areas (EDS) and phase composition studies (XRD), structural components of the coating and corrosion products formed on the coating surface after exposure to the neutral salt spray (NSS) test (EN ISO 9227) were identified. The presence of the Fe(Al,Si,Zn)3 intermetallic phase was found in the Fe-Al intermetallic layer, while in the outer layer, dendrites rich in Al and Zn were identified. In these dendrites, the eutectics of Zn/MgZn2 and precipitates of the MgZn2 phase and Si were located. The NSS test showed better corrosion resistance of ZAMS coatings compared to conventional zinc hot-dip coatings. The increase in corrosion resistance is due to the formation of favorable corrosion products: simonkolleite-Zn5(OH)8Cl2·H2O and hydrozincite-Zn5(OH)6(CO3)2, and the presence of the MgZn2 phase in the coating, which is more anodic than other structural components.

Effect of Mg on the Formation of Periodic Layered Structure during Double Batch Hot Dip Process in Zn-Al Bath.

The article presents the results of studies on the influence of Mg on the formation of the periodic layered structure of the Zn-AlMg coatings. These coatings were produced by the double batch hot dip method in a Zn bath and then in a Zn-Al(Mg) bath with a content of 15, 23, 31 wt.% Al and 3, 6 wt.% Mg. The microstructure of the coatings (OM, SEM) was revealed and the phase composition (XRD) obtained in two-component Zn-Al baths and Zn-AlMg baths were determined. The periodic layered structure was found to consist of alternating FeAl3 phase layers and a bath alloy (Zn + Al + Mg). Moreover, it was observed that the addition of 3 wt.% Mg reduces the thickness of the coating in baths containing 23 and 31 wt.% Al. However, the addition of 6 wt.% Mg causes complete disappearance of periodic layered structure in a bath with 23 wt.% Al. In a bath with a content of 31 wt.% Al the addition of 6 wt.% Mg creates a compact layer consisting of the FeAl3 phase containing the precipitation of the MgZn2 phase and Fe2Al5 phase. Such a structure of the coating transition layer limits the growth of the periodic layered structure in the coating.

Development of Bath Chemical Composition for Batch Hot-Dip Galvanizing-A Review.

Obtaining zinc coatings by the batch hot-dip galvanizing process currently represents one of the most effective and economical methods of protecting steel products and structures against corrosion. The batch hot-dip galvanizing process has been used for over 150 years, but for several decades, there has been a dynamic development of this technology, the purpose of which is to improve the efficiency of zinc use and reduce its consumption and improve the quality of the coating. The appropriate selection of the chemical composition of the galvanizing bath enables us to control the reactivity of steel, improve the drainage of liquid zinc from the product surface, and reduce the amount of waste, which directly affects the quality of the coating and the technology of the galvanizing process. For this purpose, the effect of many alloying additives to the zinc bath on the structure and thickness of the coating was tested. The article reviews the influence of various elements introduced into the bath individually and in different configurations, discusses the positive and negative effects of their influence on the galvanizing process. The current development in the field of the chemical composition of galvanizing baths is also presented and the best-used solutions for the selection and management of the chemical composition of the bath are indicated.

Impact of Bi and Sn on Microstructure and Corrosion Resistance of Zinc Coatings Obtained in Zn-AlNi Bath.

The paper presents results of studies on the impact of bismuth and tin additions to the Zn-AlNi bath on microstructure and corrosion resistance of hot dip galvanizig coatings. The structure at high magnifications on the top surface and cross-section of coatings received in the Zn-AlNiBiSn bath was revealed and the microanalysis EDS (energy dispersion spectroscopy) of chemical composition was determined. The corrosion resistance of the coatings was tested relatively in a neutral salt spray test (NSS), and tests in a humid atmosphere containing SO2. Electrochemical parameters of coatings corrosion were determined. It was found that Zn-AlNiBiSn coatings show lower corrosion resistance in comparison with the coatings received in the Zn-AlNi bath without Sn and Bi alloying additions. Structural research has shown the existence of precipitations of Sn-Bi alloy in the coating. It was found that Sn-Bi precipitations have more electropositive potential in relation to zinc, which promotes the formation of additional corrosion cells.

Structural aspects of decreasing the corrosion resistance of zinc coating obtained in baths with Al, Ni, and Pb additives.

The article presented the results of tests determining the synergistic effect of Al, Ni, and Pb additions on a zinc bath on the structure and corrosion resistance of coatings obtained on low silicon steel. Analyzed coatings were produced on S235JRG2 steel with Si content of 0.02 mass%. The corrosion resistance of the coatings was compared with the corrosion resistance of the coating obtained in the "pure" zinc bath. Structure at high magnifications (SEM) was determined, as well as coating thickness and chemical composition in microspheres. The corrosion resistance of the coatings was established comparatively in standard corrosion tests in neutral salt spray and a humid atmosphere containing SO2. It was found that the addition of Pb to the zinc bath reduced the corrosion resistance of the coatings. In the coating structure obtained in the Zn-AlNiPb bath, lead precipitation was observed in both the outer layer and the intermediate layer of the coating. Grain boundaries were the preferred site for lead precipitation. The presence of Pb precipitates favored conditions for the creation of additional corrosion cells, which led to a decrease in the corrosion resistance of the coatings.

Microstructure Characterization and Corrosion Resistance of Zinc Coating Obtained on High-Strength Grade 10.9 Bolts Using a New Thermal Diffusion Process.

The article presents the results of research on the application of innovative thermal diffusion zinc coating technology with the recirculation of the reactive atmosphere to high-strength grade 10.9 bolts. The innovation of this method consists in the introduction of reactive atmosphere recirculation and the application of coating powder mix which contains zinc powder and activator. Recirculation of the reactive atmosphere ensures its uniform composition, while the presence of an activator intensifies the process of saturating steel surface with zinc, which boosts the efficiency of active agents. Coatings were created at 440 °C and a heat soaking time of 30-240 min. Coating structure (SEM) was exposed, chemical composition in microsites (EDS) was defined, and coating phase structure (XRD) was identified. The kinetics of coating growth were defined. It was found that the increment of coating thickness was controlled by square root of soaking time. Coatings obtained using innovative thermal diffusion zinc coating technology had a two-layer structure. At the substrate, a compact layer of phase Γ1 (Fe11Zn40) was created, which was covered with a layer of phase δ1 (FeZn10). The new method of thermal diffusion zinc coating will alow for the creation of coatings of very good corrosion resistance while maintaining strength properties of bolts defined as strength class 10.9.