Phase transformation in the "Brodie graphite oxide-acetonitrile" system - influence of the oxidizing level of the material.

Reversible phase transformation in the Brodie graphite oxide-acetonitrile system, which is intercalation or release of part of the sorbed liquid from the interplanar space accompanied by an increase or a decrease in interplanar distances, is commonly observed in twice-oxidized materials. We observed this phenomenon for once-, twice- and thrice-oxidized materials using the EPR spin probe technique, DSC, and temperature programmed XRD. It was shown that all materials under study formed similar low temperature (LT) and high temperature (HT) swollen structures with acetonitrile. The phase transformation of these structures is observed for materials with different oxidation levels in the same temperature range (∼20 K). The twice- and thrice-oxidized Brodie graphite oxides form swollen structures with the same parameters, while the once-oxidized material sorbs less acetonitrile at lower temperatures, but shows the same interplanar distances as those in twice- and thrice-oxidized materials. The spin probe technique has proven its sensitivity to the appearance of small amounts of the new forming swollen structures, which makes this method useful in studies of phase transformations.

Sorption of Polar Sorbents into GO Powders and Membranes.

The comparative study of sorption of polar substances acetonitrile and water into powders and membranes (>10 µm thick) of modified Hummers (HGO) and Brodie (BGO) graphite oxides was performed using isopiestic method (IM) and differential scanning calorimetry (DSC). Additional sorption data were obtained for pyridine and 1-octanol. Sorption measurements were accompanied by conventional XRD and XPS control. Electron paramagnetic resonance (EPR) was additionally used to characterize ordering of the membranes. The impact on sorption of synthetic procedure (Brodie or Hummers), method of making membranes, chemical nature of the sorbent, and method of sorption was systematically examined. It was demonstrated that variations in synthetic procedures within both Hummers and Brodie methods did not lead to changes in the sorption properties of the corresponding powders. Sorption of acetonitrile and pyridine was reduced by approximately half when switching from powders to membranes at ambient temperature. DSC measurements at a lower temperature gave equal sorption of acetonitrile into HGO powder and membranes. Water has demonstrated unique sorption properties. Equal sorption of water was measured for HGO membranes and powders at T = 298 K and at T = 273 K. It was demonstrated that lowering the orientational alignment of the membranes led to the increase of sorption. In practice this could allow one to tune sorption/swelling and transport properties of the GO membranes directly by adjusting their internal ordering without the use of any composite materials.