Durable Polyacrylic/Siloxane-Silica Coating for the Protection of Cast AlSi7Mg0.3 Alloy against Corrosion in Chloride Solution.

This study presented a novel corrosion protective coating based on polyacrylic/siloxane-silica (PEHA-SS) deposited on lightweight cast aluminium alloy AlSi7Mg0.3. The synthesis of PEHA-SS comprises organic monomer 2-ethylhexyl acrylate and organically modified silane 3-(trimethoxysilyl)propyl methacrylate as well as an inorganic silane, tetraethyl orthosilicate. The steps during the synthesis process were monitored using real-time infrared spectroscopy. The coating deposited onto the AlSi7Mg0.3 surface was characterised using various techniques, including infrared spectroscopy, 3D contact profilometry, and scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy. The corrosion resistance of the coated alloy in sodium chloride solutions was evaluated using electrochemical impedance spectroscopy. The accelerated testing of the uncoated and coated sample was performed using the Machu test. This novel, nine micrometres thick PEHA-SS coating achieved durable corrosion (barrier) protection for the AlSi7Mg0.3 alloy in 0.1 M NaCl during the first four months of immersion or under accelerated corrosion conditions in a Machu chamber containing NaCl, acetic acid, and hydrogen peroxide at 37 °C.

Superhydrophobic Aluminium Surface to Enhance Corrosion Resistance and Obtain Self-Cleaning and Anti-Icing Ability.

A facile environmentally acceptable surface roughening method using chemical etching in HCl/H2O2 followed by grafting with n-octyltrimethoxysilane (AS-8) and 1H,1H,2H,2H-perfluorooctyltrimethoxysilane (FAS-8) was studied to fabricate a (super)hydrophobic aluminium surface. The ground aluminium surface after selected etching times (before and after grafting), was characterised using a contact profilometer, optical tensiometer, scanning electron microscope coupled with an energy-dispersive spectroscope and X-ray photoelectron spectroscope to evaluate surface roughness, wettability, surface morphology and composition. The durability of the grafted surface was tested using thermal and UV resistance tests. The corrosion properties were evaluated using potentiodynamic measurements and standard salts spray testing, ASTM B117-19. Finally, the self-cleaning and anti-icing abilities were assessed. The grafted aluminium surface with octyl- or perfluorooctyl silane reflected the highly hydrophobic (AS-8) and superhydrophobic behaviour (FAS-8). Moreover, the different behaviour of the octyl- or perfluorooctyl chain in the silane molecule on modified surface properties was also noticed because durability tests confirmed greater thermal, UV stability and corrosion resistance of FAS-8 compared to AS-8. The aluminium etched for 2 min and grafted with FAS-8 also demonstrated an excellent self-cleaning and anti-icing performance.

Acrylate-Based Hybrid Sol-Gel Coating for Corrosion Protection of AA7075-T6 in Aircraft Applications: The Effect of Copolymerization Time.

Pre-hydrolysed/condensed tetraethyl orthosilicate (TEOS) was added to a solution of methyl methacrylate (MMA) and 3-methacryloxypropyltrimethoxysilane (MAPTMS), and then copolymerised for various times to study the influence of the latter on the structure of hybrid sol-gel coatings as corrosion protection of aluminium alloy 7075-T6. The reactions taking place during preparation were characterised using real-time Fourier transform infrared spectroscopy, dynamic light scattering and gel permeation chromatography. The solution characteristics were evaluated, using viscosimetry, followed by measurements of thermal stability determined by thermogravimetric analysis. The optimal temperature for the condensation reaction was determined with the help of high-pressure differential scanning calorimetry. Once deposited on 7075-T6 substrates, the coatings were evaluated using a field emission scanning electron microscope coupled to an energy dispersive spectrometer to determine surface morphology, topography, composition and coating thickness. Corrosion properties were tested in dilute Harrison's solution (3.5 g/L (NH4)2SO4 and 0.5 g/L NaCl) using electrochemical impedance spectroscopy. The copolymerization of MMA and MAPTMS over 4 h was optimal for obtaining 1.4 µm thick coating with superior barrier protection against corrosion attack (Z10 mHz 1 GΩ cm2) during three months of exposure to the corrosive medium.

The effect of fluoride ions on the corrosion behaviour of Ti metal, and Ti6-Al-7Nb and Ti-6Al-4V alloys in artificial saliva.

Metallic materials used for manufacture of dental implants have to exhibit high corrosion resistance in order to prevent metal release from a dental implant. Oral cavity is aggressive towards metals as it represents a multivariate environment with wide range of conditions including broad range of temperatures, pH, presence of bacteria and effect of abrasion. An increasing use of various Ti-based materials for dental implants and orthodontic brackets poses the question of their corrosion resistance in the presence of fluoride ions which are present in toothpaste and mouth rinse. Corrosion behaviour of Ti metal, Ti-6Al-7Nb and Ti-6Al-4V alloys and constituent metals investigated in artificial saliva is significantly affected by the presence of fluoride ions (added as NaF), as proven by electrochemical methods. Immersion test was performed for 32 days. During that time the metal dissolution was measured by inductively coupled plasma mass spectrometry. At the end of the test the composition, thickness and morphology of the surface layers formed were investigated by X-ray photoelectron spectroscopy and scanning electron microscopy.